SINTESIS NANOWIRE MAGNETIK BERBASIS FERRITE DENGAN PENAMBAHAN CALSIA DAN ALUMINA SEBAGAI ADDITION MATERIALS UNTUK MATERIAL SUPERPARAMAGNETIK

17 views

Penulis	:	FANDI YOGISWARA (NIM : 13705036)
Kontributor / Dosen Pembimbing	:	Dosen Pembimbing : Dr.Ir.Bambang Sunendar
Jenis Koleksi	:	Tugas Akhir
Tahun Terbit	:
Penerbit	:	Teknik Material
Fakultas	:	Fakultas Teknik Mesin dan Dirgantara
Subjek	:
Kata Kunci	:	Ca(Al,Fe)12O19, Magnetoplumbite, SuperParamagnetic,Co-Precipitation.
Sumber	:
Staf Input/Edit	:	Alice D Ena Sukmana
File	:	7 file
Tanggal Input	:	09 Okt 2017

2011 TA PP FANDI YOGISWARA 1-COVER.pdf

PUBLIC Open In Flip Book Ena Sukmana

2011 TA PP FANDI YOGISWARA 1-BAB 1.pdf

PUBLIC Open In Flip Book Ena Sukmana

2011 TA PP FANDI YOGISWARA 1-BAB 2.pdf

PUBLIC Open In Flip Book Ena Sukmana

2011 TA PP FANDI YOGISWARA 1-BAB 3.pdf

PUBLIC Open In Flip Book Ena Sukmana

2011 TA PP FANDI YOGISWARA 1-BAB 4.pdf

PUBLIC Open In Flip Book Ena Sukmana

2011 TA PP FANDI YOGISWARA 1-BAB 5.pdf

PUBLIC Open In Flip Book Ena Sukmana

2011 TA PP FANDI YOGISWARA 1-PUSTAKA.pdf

PUBLIC Open In Flip Book Ena Sukmana

CaAl4Fe8O19 merupakan suatularutan padatdari dua buah senyawa, yaitu CaAl12O19 dan CaFe12O19 dengan perbandingan 1 : 2. Unsur Ca biasanya digunakan untuk keperluanbioceramicnamun kali ini akan digunakan untuk keperluan material magnetik. Serbuk ini dibuatdenganmetode ko-presipitasilarutan dengan perbandingan oksida CaO, Al2O3, dan Fe2O3 adalah 1:2:4 yang dilanjutkan dengan proses kalsinasi. Variabel yang dilihat adalah temperatur kalsinasi yaitu pada 750oC,850oC, dan 950oCyang dilakukan pada kondisi vakum. Untuk mengetahui fasa , morfologi mikrostruktur ,dan sifat magnetik digunakan XRD, SEM, dan vibrating sample magnetometer (VSM). Secara keseluruhan dapat diketahui bahwa larutan padatini memiliki struktur hexagonal magnetoplumbite . Sifat magnet hasil pengujian mendekati superparamagnetik pada temperatur kamar.