SINTESIS LAPISAN TIPIS NANOSTRUKTUR ZINC OXIDE SEBAGAI SENSOR GAS VOLATILE ORGANIC COMPOUNDs (VOCs): METANOL

SYNTHESIS OF ZINC OXIDE NANOSTRUCTURED THIN FILM AS VOLATILE ORGANIC COMPOUNDS (VOC) GAS SENSOR: METHANOL

Undergraduate Theses from JBPTITBPP / 2017-09-27 11:05:13
Oleh : YUYUT RIMA JEMIRA (13309113); Pembimbing: Brian Yuliarto, Ph.D; Dr. Ir. Nugraha, S1 - Department of Engineering Physics
Dibuat : 2016, dengan 7 file

Keyword : ZnO, sensor gas, semikonduktor, methanol, VOC

Volatile Organic Compounds (VOCs) memiliki banyak manfaat sekaligus membahayakan untuk kesehatan manusia dan keselamatan kerja. Dalam kondisi atmosferis, VOCs memiliki kemampuan untuk memicu kebakaran. Salah satu


senyawa yang termasuk VOCs adalah metanol. Paparan langsung terhadap gas metanol bisa menyebabkan mual, pusing, sakit kepala, kehilangan koordinasi dan


berkurangnya fungsi penglihatan. Semikonduktor dengan elemen deteksi lapisan tipis ZnO nano-rod mampu mendeteksi gas metanol. Sensor ini disintesis menggunakan prekursor Zinc Nitrate Tetrahydrate dengan metode Dip-Coating dan Chemical Bath Deposition.


Pengujian sensor gas ZnO terhadap gas metanol menunjukkan bahwa sensitivitas dan konduktivitas sensor naik seiring dengan kenaikan temperatur operasi,


sedangkan waktu respon dan waktu pulih sensor mengalami


penurunan.Temperatur optimal sensor dengan proses 1x CBD adalah pada 250oC, dengan sensitivitas 90,89%, waktu respon 4,6 menit, dan waktu pulih 8,5 menit. Temperatur optimal sensor dengan proses 2x CBD adalah pada 300oC, dengan sensitivitas 93,58%, waktu respon 1,9 menit, dan waktu pulih 3,9 menit.

Deskripsi Alternatif :

Volatile Organic Compounds (VOCs) have many benefits but also can be harmful to human health and safety. In atmospheric conditions, VOCs have the ability to trigger a fire. One of the compounds that's categorized as VOCs is methanol. Direct exposure to methanol gas can cause nausea, dizziness, headaches, loss of coordination and loss of visual function. Semiconductor thin film ZnO with nanorod structure has the ability to detect methanol gasas sensing element. This thin film can be synthesized using Zinc Nitrate Tetrahydrate as precursor and both methods of Dip-Coating and Chemical Bath Deposition. Sensors responses to methanol gas exposure show that the sensitivity and conductivity sensorsincrease, whileresponse time and recovery time decrease asthe operating temperatures increase. Optimal temperature sensor with once CBD process is at 250oC, with sensitivity of 90.89%, response time of 4.6 minutes


and 8.5 minutes recovery time. Optimal temperature sensor with twice CBD process is at 300oC, with a sensitivity of 93.58%, response time of 1.9 minutes


and 3.9 minutes recovery time.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing:


    Brian Yuliarto, Ph.D;


    Dr. Ir. Nugraha, Editor: Alice Diniarti

File PDF...