Oleh : YESSI AGUSTIN (NIM 23005016), Central Library Institute Technology Bandung
Dibuat : 2007, dengan 7 file

Keyword : Montmorillonite, SEM, XRD, BET

Untuk meningkatkan aktivitas katalitiknya, telah dilakukan modifikasi terhadap lempung alam dengan jenis montmorillonite. Modifikasi dilakukan melalui dua metode yang berbeda yaitu pengasaman dengan menggunakan asam sulfat pekat dan pilarisasi dengan ion Keggin. Sampel-sampel yang terdiri dari montmorillonite, H-montmorillonite, dan PILC-montmorillonite kemudian dianalisis dengan menggunakan X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), analisis luas permukaan yang lebih dikenal dengan nama analisis BET, dan analisis keasaman dengan menggunakan metode titrimetri. Difraktogram sinar X dari ketiga sample tidak menunjukan adanya perbedaan yang signifikan. Akan tetapi, berdasarkan hasil foto SEM, dapat terlihat dengan jelas bahwa agregat-agregat montmorillonite mengecil akibat kedua jalur modifikasi tersebut. Lebih jauh, agregasi yang lebih homogen yang ditunjukan oleh foto SEM untuk sample H-montmorillonite mengimplikasikan bahwa delaminasi oleh asam terjadi secara merata. Luas permukaan montmorillonite ditentukan dengan analisis BET Analisis tersebut menunjukan peningkatan luas permukaan montmorillonite setelah pengasaman maupun setelah pilarisasi. Hasil ini sesuai dengan hasil yang ditunjukan oleh analisis SEM. Akan tetapi rendahnya luas permukaan montmorillonite yang diperoleh setelah pilarisasi pada penelitian ini bila dibandingkan dengan literatur-literatur yang sudah ada, mengindikasikan bahwa hanya sebagian dari montmorillonite tersebut yang berhasil dipilarisasi. Hal ini pula yang menjelaskan tidak ditemukannya pergeseran puncak pada 2θ kurang dari 100 pada difraktogram PILC-montmorillonite. Analisis keasaman mengindikasikan bahwa pengasaman dapat meningkatkan keasaman montmorillonite lebih dari dua kali lipat, sementara itu PILC-montmorillonite tidak menunjukan perbedaan yang signifikan. Peningkatan keasaman dan atau luas permukaan pada montmorillonite termodifikasi menyebabkan peningkatan aktivitas katalitiknya. Peningkatan tertinggi dicapai oleh H-montmorillonite dengan kenaikan konversi hingga 12% dari montmorillonite yang tidak dimodifikasi. Akan tetapi bila dibandingkan dengan katalis asam sulfat, konversi yang dicapai oleh montmorillonite hasil modifikasi masih relatif rendah. Hal ini kemungkinan disebabkan oleh halangan ruang pada mikropori montmorilonite dan hanya asam bronsted yang berkontribusi dalam mengkatalisis reaksi esterifikasi.

Deskripsi Alternatif :

In order to increase the catalytic activities, a natural montmorillonite clay has been modified. The modification was carried out in two different methods, i.e. acidification in concentrated sulphuric acid solution and pillarization with Keggin ion. The existing samples (montmorillonite, H-montmorillonite and PILC-montmorillonite) were then analyzed by using X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), surface area analysis known as BET analysis, and acidity analysis based on titrimetry method. The X-Ray diffractograms indicated no significant difference found between those three different samples. However, from the SEM images, it was clearly observed that the aggregates of montmorillonite decreased by both types of modification. Furthermore, a relative homogeneous aggregation showed by H-montmorllonite SEM image implied the acid delaminating occurred homogeneously. Surface area determination was carried out by using BET analysis. This analysis results in increasing of the surface area of montmorillonite after the acid treatment as well as the pillarization. This result was relevant to that showed by the SEM image. However, the surface area achieved by the pillarization which was too low compared to other literatures indicated that only a part of the existing montmorilonite was successfully pillared. It also explained the absent of peak shift at 2θ less than 100 in the PILC-montmorillonite diffractogram. The acidity analysis indicated that acid treatment can increase the montmorillonite acidity more than twice, while no significant difference obtained from PILC-montmorillonite. The increase of acidity and or surface area in modified montmorillonites caused the increase of their catalytic activity. The highest increment was achieved by H-montmorillonite for about 12 % compared to unmodified montmorilonite. However, the conversion achieved by modified montmorillonites was relatively lower than sulphuric acid catalyst. This fact is due to the steric effect in microphores of montmorillonite and only Bronsted acids have contribution in esterification catalysis.

Copyrights : Copyright Â(c) 2001 by ITB Central Library. Verbatim copying and distribution of this entire article is permitted by author in any medium, provided this notice is preserved.

Beri Komentar ?#(0) | Bookmark

Properti	Nilai Properti
ID Publisher	JBPTITBPP
Organisasi	Central Library Institute Technology Bandung
Nama Kontak	Drs. Mahmudin, SIP.
Alamat	Jl. Ganesha 10
Kota	Bandung
Daerah	Jawa Barat
Negara	Indonesia
Telepon	62-22-2509118, 2500089
Fax	62-22-2500089
E-mail Administrator	digilib@lib.itb.ac.id
E-mail CKO	digilib@lib.itb.ac.id