APLIKASI NANOBIOSILIKA MIKROALGA LAUT THALASSIOSIRA SP. SEBAGAI MATRIKS KOLOM GEL FILTRASI

APPLICATION OF THE NANOBIOSILICA FROM MARINE MICROALGAE THALASSIOSIRA SP. AS A MATRIX FOR GEL FILTRATION COLOUMN

Undergraduate Theses from JBPTITBPP / 2017-09-27 11:42:38
Oleh : VIVI FITRIYANTI ( NIM : 10510037) ; Pembimbing Zeily Nurachman D.Sc, S1 - Department of Chemistry
Dibuat : 2014, dengan 7 file

Keyword : Gel filtrasi, Nanobiosilika, mikroskop elektron pemindai-spektroskopi pemancar energy, Thalassiosira sp.

Pada penelitian terdahulu, biomassa mikroalga laut Thalassiosira sp. telah dimanfaatkan




sebagai bahan baku untuk produksi biodiesel dan menghasilkan limbah residu berupa




dinding sel yang mengandung biosilika berpori nano. Nanobiosilika ini dapat dimanfaatkan




sebagai matriks untuk kolom gel filtrasi. Pada penelitian ini, nanobiosilika dari Thalassiosira




sp. dipelajari sebagai matriks untuk kolom pemisahan. Untuk memperoleh nanobiosilika,




lipid harus diekstrak dari sel kemudian dicuci dengan asam dan dikalsinasi pada 600oC




dengan laju pemanasan 3oC/menit selama 6 jam. Topologi permukaan dan kandungan kimia




nanobosilika yang diperoleh dikarakterisasi dengan menggunakan mikroskop elektron




pemindai-spektroskopi pemancar energy (SEM-EDS). Nanobiosilika dari Thalassiosira sp.




diaplikasikan sebagai matriks untuk kolom gel filtrasi untuk memisahkan campuran protein




BSA dan lisozim. Hasil penelitian menunjukkan 1 g nanobiosilika dapat dihasilkan dari 100




g sel basah Thalassiosira sp. Topologi nanobiosilika Thalassiosira sp. putih adalah




berbentuk bulat dengan pori berukuran 80–400 nm yang terdistribusi secara acak pada




permukaan. Kandungan SiO2 pada dinding sel basah dan nanobiosilika tanpa pengasaman




berturut-turut adalah 10,85% dan 93,79% (w/w). Pemisahan campuran BSA dan lisozim




dengan kromatografi kolom berbasis matriks nanobiosilika menghasilkan dua kumpulan




fraksi potein pada no. 15-17 dan 20-21. Melalui analisis SDS-PAGE, satu pita protein




dengan massa molekul 66 kDa dari fraksi 1517 diidentifikasi sebagai BSA, Namun, tidak




ada pita protein dari fraksi 2021 diamati akibat jumlah protein terlalu sedikit. Hal ini




menunjukkan bahwa nanobiosilika Thalassiosira sp. dapat diaplikasikan untuk pemisahan




protein.

Deskripsi Alternatif :

Based on our previous research, biomass of marine microalgae Thallasiosira sp. has been




used as feedstock for biodiesel production and produces waste of debris of cell walls




containing macroporous silica (50 nmm). These nanobiosilica may be used as a matrix




for gel filtration coloumn. In this present research, nanobiosilica of Thalassiosira sp. was




studied as a matrix for separation coloumn. To obtain nanobiosilica of Thalassiosira sp., first




lipid had to be extracted from the cell followed by acid treatment and calcination at 600oC




with heat rate of 3oC/min for 6 hour. Surface topology and chemical composition of the




nanobiosilica was characterized by scanning electron microscopy-energy dispersive




spectroscopy (SEM-EDS). Nanobiosilica of Thalassiosira sp. was applied for matrices of gel




filtration coloumn to separate mixtures of BSA and lisozyme. The results showed that one




nanobiosilica was obtained from 100 g wet biomass. The topology of white nanobiosilica of




Thalassiosira sp. has cylinder in shape with porous size of 80400 nm distributed randomly




in the surface. The composition of SiO2 of Thalassiosira sp. cells before and after acid




treatment was 10.8 and 93.79%, respectively. Separation of BSA and lisozim mixtures by




chromatography coloumn based on a nanobiosilica matrix produced two protein fraction at




nos. 1517 and 2021. By SDS-PAGE analysis, a protein band of 66 kDa of fraction no.




1517 was identified as BSA, but no protein band of fraction no. 2021 was observed due to




a little amount of protein. Thus, a nanobiosilica of Thalassiosira sp. matrix might be applied




for protein separation

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing Zeily Nurachman D.Sc, Editor: Alice Diniarti

File PDF...