PENGARUH KONSENTRASI CHITOSAN DAN PERLAKUAN HYDROTHERMAL TERHADAP PEMBENTUKAN MORFOLOGI GAMMA-ALUMINA SEBAGAI APLIKASI CATALYTIC CONVERTER AUTOMOBILE

Undergraduate Theses from JBPTITBPP / 2017-10-09 10:32:50
Oleh : VALENDRA GIANDITA (NIM : 13706019); Pembimbing : Dr.Ir. Bambang Sunendar, S1 - Material Engineering Study Programme
Dibuat : 2011, dengan 7 file

Keyword : Catalytic Converter, Gamma Alumina, Ceramic Foam, Chitosan, Hydrothermal

Dengan semakin banyaknya produksi kendaraan bermotor, semakin banyak pula polusi gas buang yang akan dihasilkan seperti COx, NOx, Methane, dan gas buang berbahaya lainnya. Karena hal ini, kebutuhan terhadap catalytic converter




semakin bertambah besar. Pada catalytic converter yang sudah banyak dibuat, membran aktifnya terbuat dari platinum yang tergolong memiliki biaya produksi cukup tinggi. Untuk mengurangi biaya produksi, sudah dilakukan penelitian




dengan menggunakan gamma alumina sebagai membran aktifnya. Gamma alumina memiliki biaya produksi yang relatif rendah karena memiliki temperatur pembentukan sekitar 500-700oC. Penelitian dilakukan dengan menggunakan serbuk alumina untuk membuat ceramic foam sebagai body. Lalu body dilapisi




dengan membran gamma alumina dengan melakukan proses impregnasi larutan AlOH. Dilakukan juga variasi penambahan konsentrasi chitosan pada larutan yang diimpregnasi. Kemudian diberikan perlakuan hydrothermal dengan variasi waktu yang berbeda-beda. Setelah itu dikalsinasi pada temperatur 6000C selama 2 jam. Proses karakterisasi menggunakan XRD, FTIR, SEM, dan BET. Dari pengujian




XRD disimpulkan bahwa kristal gamma alumina berhasil terbentuk. Hal ini dapat dilihat dari adanya 3 puncak pada sudut difraksi 37,340, 45,840, dan 67,360 . Lalu pada pengujian FTIR dapat terlihat adanya ikatan Al-O pada puncak 1627 dan gugus O-H pada puncak 3448,1. Terdapat juga gugus N-H pada puncak 1419,35 dan 3448,1 yang menunjukkan adanya sisa chitosan dari proses impregnasi. Kemudian, dari hasil SEM, terlihat morfologi kristal gamma alumina yang




menyerupai lembaran-lembaran (pelat) akibat adanya kalsium dan sisa chitosan yang sebelumnya diimpregnasi kedalam ceramic foam. Hasil pengujian BET menunjukkan bahwa gamma alumina memiliki luas permukaan spesifik yang relative besar yaitu 132,5338 sq m/g.

Deskripsi Alternatif :

Development of automobile industry will increase the production of automobile pollution such as COx, NOx, methane, and other hazardous gas pollution. So that,




the needs of catalytic converter are getting bigger. In well-made catalytic converter, the active membrane is made by platinum which have high production cost. To reduce the production cost, there is a research that use gamma alumina as an active membrane previously. Gamma alumina has low production cost relatively because it has low forming temperature (500-700oC). This research carried out by using alumina powder to make ceramic foam as the body. Then, the body is coated with gamma alumina membrane by impregnation process of AlOH solution. In this process, the impregnation solution is also added by some variation of chitosan concentration. After that, the green body is provided by




hydrothermal treatment with variation of processing time. Then, it calcined at 6000C temperature with 2 hours holding time. The characterization that use in this research are XRD, FTIR, SEM, and BET. In XRD testing concluded that




gamma alumina crystal are successfully formed. It can be see from the presence of three peaks ars diffraction angle 37,340, 45,840, and 67,360. Then, in the FTIR testing can be seen the Al-O bond at 1627 peak and O-H bond at 3448,1 peak. There are also N-H bond at 1419,35 and 3448,1 peak that indicate the presence of residual chitosan impregnation process. In the SEM results, are formed crystal morphology of gamma alumina sheets (plates) as a results of calcium and residual chitosan that previously impregnated into ceramic foam. BET test result showed




that gamma alumina has large specific surface area, about 132,5338 sq m/g.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Dr.Ir. Bambang Sunendar, Editor: PKL-SMK

File PDF...