Path: Top > S1-Final Project > Material Engineering-FTMD > 2008

PREPARASI DAN KARAKTERISASI HYBRID FILM DAN GEL POWDER SiO2-TiO2-PDMS DENGAN METODE SOL GEL

Undergraduate Theses from JBPTITBPP / 2017-10-09 10:32:50
Oleh : TUMPAL HAMONANGAN SIMATUPANG (NIM 13703005), S1 - Material Engineering Study Programme
Dibuat : 2008, dengan 9 file

Keyword : Hybrid film SiO2-TiO2-PDMS, Hybrid Organic Inorganic Materials, Struktur berpori, Teknik sol-gel

Hybrid Organic Inorganic Materials (HOIM) secara luas telah dipelajari. Hal ini dikarenakan kemudahannya untuk disintesis dengan menggunakan metode sol-gel. HOIM merupakan campuran antara material organik dan material inorganik pada tingkat molekular yang sifat-sifatnya tergantung dari kedua material organik dan inorganiknya. Hybrid film dan gel powder SiO2-TiO2-PDMS termasuk ke dalam jenis Organically Modified Silicates (Ormosils) yang merupakan jenis baru dalam HOIM. Pada penelitian tugas akhir ini, hybrid film SiO2-TiO2-PDMS dibuat dengan metode sol-gel dip coating, sedangkan gel powder SiO2-TiO2-PDMS dibuat dengan metode sol-gel. Prekursor yang digunakan adalah tetraethoxy silane (TEOS) dan titanium isopropoxide Ti(OiPr). Perbandingan molar antara SiO2 dengan TiO2 yang digunakan adalah 0,07 : 0,03 dan persen berat (% wt) PDMS terhadap TEOS yang digunakan adalah 5% wt dan 10% wt. Variasi persen berat (% wt) PDMS terhadap TEOS bertujuan untuk mengetahui sifat-sifat yang diperoleh pada hybrid film SiO2-TiO2-PDMS sedangkan variasi temperatur pada proses perlakuan panas bertujuan untuk mengetahui fasa-fasa yang terbentuk. Hasil SEM menunjukkan hybrid film SiO2-TiO2-PDMS dengan struktur berpori terjadi pada 10% wt PDMS terhadap TEOS. Hasil XRD pada hybrid film SiO2-TiO2-PDMS menunjukkan fasa amorf , sedangkan hasil XRD pada gel powder SiO2-TiO2-PDMS menunjukkan fasa kristalin TiO2, yaitu anatase dan rutile.

Deskripsi Alternatif :

Hybrid Organic Inorganic Materials have been widely studied. This has been due to their relatively easy synthesis utilizing the sol-gel method. Hybrid Organic Inorganic Materials are a mixture of organic and inorganic materials at a molecular level, their properties being dependent on both organic and inorganic materials. Hybrid film and gel powder SiO2-TiO2-PDMS are included in Organically Modified Silicates (Ormosils) that are new kind of Hybrid Organic Inorganic Materials. In this final project, SiO2-TiO2-PDMS hybrid film was prepared by sol-gel dip coating method, whereas SiO2-TiO2-PDMS gel powder was prepared by sol-gel method. Tetraethoxy silane (TEOS) and titanium isopropoxide Ti(OiPr) were used as a precursors. Molar ratio of SiO2 : TiO2 was 0,07 : 0,03 and % wt of PDMS to TEOS were 5% wt and 10% wt. The variation of % wt of PDMS to TEOS were intended to know the properties of SiO2-TiO2-PDMS hybrid film, whereas the variation of temperature in heat treatment were intended to know the phases were formed. The results of SEM showed the SiO2-TiO2-PDMS hybrid film has a pore structure at 10% wt PDMS to TEOS. The results of XRD in SiO2-TiO2-PDMS hybrid film showed amorphous phase, whereas in SiO2-TiO2-PDMS gel powder showed crystalline phase, such as anatase and rutile.

Copyrights : Copyright Â(c) 2001 by ITB Central Library. Verbatim copying and distribution of this entire article is permitted by author in any medium, provided this notice is preserved.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id