PROTOTYPE FABRIKASI FILM PVDF DENGAN METODA CALENDRING DAN KARAKTERISTIK STRUKTURNYA

Undergraduate Theses from JBPTITBPP / 2017-09-27 11:45:12
Oleh : TETA PRATIWI (NIM 10204035), S1 - Department of Physics
Dibuat : 2009, dengan 8 file

Keyword : PVDF, sensor piezoelektrik, pooling

Poly(vinylidene fluoride) mempunyai bagian kristal dan bagian amorf sehingga dikenal sebagai polimer semikristalin. Poly(vinylidene fluoride) memiliki sifat piezoelektrik karena memiliki orientasi molekul yang memenuhi syarat bahan piezoelektrik. Secara umum terdapat tiga fasa pada bahan tersebut,yaitu fasa c,fasa P,dan fasa y. Orientasi molekul yang besar untuk syarat piezoelektrik dipenuhi oleh fasa P.

Pada percobaan ini dilakukan pembuatan film tipis dari polimer poly(vinylidene fluoride) untuk membuktikan seberapa besar pengaruh dari pooling (pemberian medan listrik tinggi) agar menghasilkan fasa P, yang menyebabkan timbulnya sifat piezoelektrik yang besar. Dengan cara memipihkan poly (vinylidene fluoride) yang berbentuk pelet untuk diubah menjadi film tipis dengan cara digiling menggunakan dua silinder yang didalamnya terdapat filament pemanas.

Sampel yang belum dipooling dan yang telah dipooling dianalisa menggunakan fourier transform infra red(FTIR). Maka diperoleh kesimpulan bahwa peningkatan pemberian medan listrik pada saat dipooling dapat meningkatkan orientasi molekul poly(vinylidene fluoride) ditandai dengan banyaknya puncak maksimum maupun minimum yang sangat berguna dalam perbandingan. Dalam karakterisasi film PVDF digunakan inframerah dengan bilangan gelombang 4000-750 cm-1. Peningkatan orientasi molekul dapat meningkatkan perubahan fasa a ke fasa P dan peningkatan efek piezoelektrik film poly(vinylidene fluoride).

Deskripsi Alternatif :

Poly(vinylidene fluoride) has a crystal part and an amorf part, and is known as semi-crystalin polymers. Poly(vinylidene fluoride) has piezoelectric property because it has molecule orientation that fulfill the standard of piezo-electric material. In general there are three phase of those material, that is a-phase, b-phase, and g-phase. Great orientation of molecule that is a piezo-electric stipulation fulfilled by b-phase.

At this experiment, a thin film is made from poly(vinylidene fluoride) polymers, to prove how big an influence from a polling (given a high electric field) to yield beta-phase, which causes big piezo-electric property incidence. Poly(vinylidene fluoride) which is in the form of pellet is thinned to be turned into thin film by milled it using two cylinders that include a heater filament.

Polling and un-polling samples are analysed by fourier transform infra red(FTIR). Hence, conclusion is obtained: increasing the electric field when applied at pooling time can increase poly(vinylidene fluoride) molecule orientation, marked with many maximum and also minimum top, that is useful for comparison between samples. In PVDF film characterization, infrared with wave number 4000-750 cm-1 is applied. The increasing of molecule orientation can increase the transformation between alpha-phase to beta-phase, and also an improvement of poly(vinylidene fluoride) film piezo-electric effect.

Copyrights : Copyright Â(c) 2001 by ITB Central Library. Verbatim copying and distribution of this entire article is permitted by author in any medium, provided this notice is preserved.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing: Dr. Ing Soeparno Satira, Editor: Vika A. Kovariansi

File PDF...