PERANCANGAN DAN PEMBUATAN ALAT FILTER PRESS MEKANIK UNTUK MENDAPATKAN BODY PLASTIS KERAMIK

Undergraduate Theses from JBPTITBPP / 2017-10-09 10:32:51
Oleh : TANIA RAHAYU (NIM 13702043), S1 - Material Engineering Study Programme
Dibuat : 2008, dengan 7 file

Keyword : Filter press skala laboratorium, body plastis, keseragaman air

Pembuatan body plastis keramik yang seragam dengan kadar air yang diinginkan untuk keperluan praktikum ataupun penelitian keramik tidak mudah diperoleh. Hal ini menunjukkan bahwa alat filter press yang kadar airnya dapat ditentukan secara tepat sangat diperlukan. Sampai saat ini penelitian mengenai proses pembentukan plastis yang dikaitkan dengan kadar air, komposisi, dan susut bakar linear menemui kesulitan. Hal tersebut terkait dengan penentuan kadar air secara tepat dan seragam.

Perancangan dan pembuatan alat filter press mekanik dengan skala laboratorium telah dilakukan. Saat ini body keramik dengan kandungan air tertentu dan seragam belum dapat dihasilkan dari filtrasi dengan filter press yang telah dibuat, karena terjadi kebocoran slurry pada seal yang ada diantara plunger dan silinder. Penelitian awal mengenai pengaruh kadar air dan komposisi lempung terhadap nilai susut bakar linear body keramik hasil ekstrusi proses pencampurannya telah dilakukan secara manual. Sehingga ketidakseragaman data susut yang diperoleh diasumsikan sebagai akibat dari ketidakseragaman sifat body plastis yang diperoleh.

Hasil penelitian ini menunjukkan adanya kecenderungan bahwa susut bakar untuk sampel hasil ekstrusi untuk komposisi I (lempung 50%, air 25%) dan IV (lempung 50%, air 21%) lebih besar daripada susut bakar komposisi II (lempung 25%, air 17,5%) dan III (lempung 25%, air 15.5%), yaitu antara 4,7-5,5 % dan 2,1-2,6 %. Walaupun demikian perbedaan susut bakar sampel yang dibuat secara manual tersebut tidak signifikan dan tidak seragam. Ketidakseragaman nilai susut bakar tersebut menunjukkan perlunya pengendalian kualitas body plastis, sehingga penyempurnaan filter press yang dibuat masih perlu dilanjutkan lagi.

Deskripsi Alternatif :

Preparation of a plastic ceramic body with a variety of homogeneous water content for ceramic practical or research is not easy to obtain. This shows the need for a filter press system that could produce a plastic cake with a homogeneous and determine water content. The observation of the forming processes on a ceramic plastic body with determine and homogeneous water content and clay content to the linear firing shrinkage characteristic has faced some in-homogeneity problem in the fired properties.

The design and manufacture of a laboratory filter press has been carried out and some initial testing has been undertaken. It is found that some slurry leakage occurred from the seal between the plunger and the outer cylinder. Preliminary research on the effect of water content and the amount of ball clay to the fired linear shrinkage of a plastic ceramic body through extrusion has been done with manual mixing. Due to the in-homogeneity observed on shrinkage data an assumption was made that this has a correlation with the plastic body property.

It has been observed that the firing shrinkage of the extruded samples for composition I (50% clay, 25% water content) and IV (50% ball clay, 21% water content) is higher than firing shrinkage for composition II (25% ball clay, 17,5% water content) and III (25% ball clay, 15,5% water content), which is between 4,7-5,5% and 2,1-2,6%. Even though for manually prepared plastic body extruded samples, the difference were not significant and homogeneous. The inhomogeneity shows the need for a close monitoring of the plastic body characteristic, hence the filter press system should be improved further.

Copyrights : Copyright Â(c) 2001 by ITB Central Library. Verbatim copying and distribution of this entire article is permitted by author in any medium, provided this notice is preserved.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS1 - Material Engineering Study Programme
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing: Dr. Ir. Aditianto Ramelan, Editor: Vika A. Kovariansi

File PDF...