POLIMER ELEKTROLIT DARI LIMBAH STYROFOAM UNTUK APLIKASI BATERAI LITIUM

POLYMER ELECTROLYTE FROM STYROFOAM WASTE FOR LITHIUM BATTERY APPLICATION

Undergraduate Theses from JBPTITBPP / 2017-09-27 11:42:31
Oleh : SYNTHIA PRAMITHA BANGUN (NIM : 10506096); Pembimbing : Dr. I Made Arcana, S1 - Department of Chemistry
Dibuat : 2012, dengan 7 file

Keyword : baterai Li-ion, polimer elektrolit, polyblend, polihidroksibutirat, polistirena tersulfonasi

Teknologi telah menjadi bagian yang tidak dapat dipisahkan dari kehidupan masyarakat di era globalisasi ini. Perkembangan jaman serta kemajuan ilmu pengetahuan dan teknologi menghasilkan berbagai keluaran yang dibuat untuk mempermudah hidup manusia. Beberapa jenis perangkat elektronik portable seperti handphone, laptop, dan digital camera memanfaatkan baterai ion Litium (Li-ion) sebagai sumber energinya. Penggunaan baterai Li-ion ini memiliki dampak negatif karena cairan elektrolit di dalamnya dapat mencemari lingkungan. Oleh sebab itu, para peneliti mencari solusi untuk mengatasi masalah yang ditimbulkan oleh baterai Li-ion konvensional yang digunakan saat ini. Berbagai penelitian mengenai teknologi pemanfaatan polimer elektolit sebagai separator dalam pembuatan baterai Li-ion tengah dilakukan. Penelitian ini memanfaatkan limbah styrofoam sebagai bahan baku pembuatan membran polimer elektrolit. Polistirena diisolasi dari styrofoam kemudian disulfonasi dengan asetil sulfat. Membran polimer elektrolit dibuat dengan mencampurkan polistirena tersulfonasi (PSS), polihidroksibutirat (PHB), dan LiClO4 padat dengan komposisi bervariasi. Selanjutnya, membran dikarakterisasi melalui analisis gugus fungsi dengan FTIR, analisis morfologi permukaan dengan Scanning Electron Microscope, analisis ketahanan mekanik dengan Tensile Tester Autograph, dan analisis konduktivitas dengan Impedance Spectroscopy. Hasil penelitian menunjukkan bahwa peningkatan komposisi LiClO4 dalam membran mengakibatkan penurunan kekuatan mekanik dan peningkatan nilai konduktivitas membran. Sedangkan, penambahan PHB meningkatkan kekuatan mekanik dan kehomogenan membran.

Deskripsi Alternatif :

Technology has become an inseparable part of people's life in this era of globalization. Nowadays, science and technology are progressing rapidly and have been releasing various outputs created to facilitate human life. Several types of portable electronic devices such as mobile phones, laptops, and digital camera utilize Lithium ion (Li-ion) batteries as a source of energy. The use of Li-ion batteries has a negative impact because the electrolyte solution in battery can contaminate the environment. Therefore, researchers are looking for solutions to overcome the problems posed by conventional Li-ion batteries. Various research on utilizing polymer electrolyte as separator in the manufacture of Li-ion batteries is being developed. This study is used styrofoam waste as raw material for the making of polymer electrolyte membrane. Polystyrene was isolated from styrofoam, and then sulfonated with acetyl sulfate. Polymer electrolyte membranes were prepared by mixing sulfonated polystyrene (SPS), polyhydroxybutyrate (PHB), and solid LiClO4 with various compositions. Subsequently, the membranes were characterized through the analysis of functional groups by FTIR, surface morphology analysis by Scanning Electron Microscope (SEM), mechanical strength analysis with Tensile Tester Autograph, and conductivity analysis by Impedance Spectroscopy. The results showed that an increase of LiClO4s composition in membrane resulted in a decrease in mechanical strength of membrane and an increase in membrane's conductivity. Meanwhile, the addition of PHB increased mechanical strength and homogeneity of the membrane.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id