PENGARUH PERBEDAAN METODA PERLAKUAN TERHADAP EFEKTIFITAS ZEOLITE SEBAGAI SUBSTITUSI PARSIAL SEMEN PADA BETON

THE INFLUENCE OF DIFFERENT TREATMENT METHODS ON EFFECTIVENESS OF ZEOLITE AS THE PARTIAL SUBSTITUTION OF CEMENT IN CONCRETE

Master Theses from JBPTITBPP / 2017-09-27 15:23:28
Oleh : SUPARYO (NIM : 250 07 027), S2 - Civil Engineering
Dibuat : 2009, dengan 7 file

Keyword : Zeolite alam; Zeolite hasil perlakuan; Aktivitas pozolanik; Kuat tekan mortar; Sifat mekanis beton; Sifat fisik beton

Zeolite merupakan mineral alam yang banyak digunakan dalam berbagai bidang seperti pertanian, peternakan, perikanan, industri dan pelestarian lingkungan. Selain itu zeolite juga mempunyai potensi untuk digunakan sebagai bahan pozzolan karena memiliki kandungan silika yang tinggi yang diharapkan dapat bereaksi dengan Ca(OH)2 untuk meperbaiki kinerja beton.


Pada penelitian ini, pengaruh zeolite sebagai subtitusi parsial semen dalam campuran beton telah dipelajari melalui perbandingan hasil pengujian dari komposisi kimia zeolite, titrasi kadar Ca(OH)2 pada larutan zeolite-Ca(OH)2, kuat tekan mortar dan beton, modulus elastisitas beton dan sifat fisik beton yang terdiri dari berat jenis, penyerapan air dan volume rongga tembus air. Mineral zeolite alam yang digunakan adalah berasal dari Lebak, Provinsi Banten, Indonesia. Zeolite alam tersebut diolah terlebih dahulu dengan mengunakan 3 metoda yaitu dipanaskan dengan suhu 250 oC, direndam dalam larutan 0,8 M NaOH, dan direndam dalam larutan 2 M NH4Cl. Jumlah semen yang disubtitusi pada benda uji mortar dan beton, masing-masing 20 % dan 10 % zeolite.


Hasil pengujian menunjukkan bahwa zeolite alam dan zeolite olahan dapat digunakan sebagai mineral admixture sesuai standar ASTM C618 dan juga diindikasikan dapat digunakan sebagai bahan tambahan dan menggantikan sebagian semen pada komposisi campuran beton.

Deskripsi Alternatif :

Zeolite is a natural mineral that is widely used in various fields such as agriculture, animal husbandry, fishery, industry and environmental conservation. Besides zeolite also has the potential to be used as Pozzolan material having a high silica content which is expected to react with Ca(OH)2 to improve the performance of concrete.


In this study, the influence of zeolite as a partial substitution of cement in concrete mixtures have been studied through comparison of test results of the chemical composition of zeolite, titration of Ca(OH)2 content in the solution of zeolite-Ca(OH) 2, the compressive strength of mortar and concrete, modulus of elasticity of concrete and physical properties consisting of concrete density, water absorption and volume of permeable pore space (voids). Natural zeolite mineral used is derived from Lebak, Banten province, Indonesia. Natural zeolite is first treated by using three of method i.e heated to a temperature of 250 oC, immersed in a solution of 0.8 M NaOH, and immersed in a solution of 2 M NH4Cl. In the mortar and concrete samples, the cement contents are substituted with 20% and 10% zeolite respectively.


Test results show that natural zeolite and zeolite treatment can be used as a mineral Admixture appropriate with ASTM C618 standard and also indicated can be used as a supplementary material or cement replacement in concrete mix.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Penulis : SUPARYO (NIM : 250 07 027), Editor: Alice Diniarti

File PDF...