Path: TopS1-Final ProjectMetallurgical Engineering-FTTM2013

ANALISIS STRUKUR MIKRO DAN SIFAT MEKANIK BAJA HOT ROLLED COIL API5LX65MO DENGAN MIKROSTRUKTUR DUAL PHASE MELALUI PROSES INTERCRITICAL ANNEALING DAN PENDINGINAN CEPAT

ANALYSIS OF MICROSTRUCTURE AND MECHANICAL PROPERTIES API5LX65MO HOT ROLLED COIL STEEL WITH DUAL PHASE MICROSTRUCTURE THROUGH INTERCRITICAL ANNEALING AND QUENCHING PROCESS

Undergraduate Theses from JBPTITBPP / 2017-09-27 10:37:15
Oleh : STEVEN (NIM : 12509007), S1 - Metallurgy
Dibuat : 2013, dengan 7 file

Keyword : baja dua fasa, intercritical annealing, quenching.

Kebutuhan akan baja berkekuatan tinggi dengan mampu bentuk yang baik pada aplikasi otomotif semakin meningkat. Untuk memenuhi kebutuhan ini, diperlukan baja yang memiliki kriteria tersebut, salah satunya adalah baja dua fasa yang memiliki kombinasi yang sangat baik antara kekuatan dan drawability sebagai akibat dari mikrostrukturnya yaitu ferit yang lunak serta martensit yang keras.



Baja dua fasa dapat diperoleh melalui perlakuan panas baja HSLA. Baja HSLA memiliki kekuatan yang tinggi melalui mekanisme penghalusan butiran dan pengerasan presipitasi. Mekanisme pengerasan martensitik kemudian dapat diberikan pada baja HSLA selain kedua mekanisme penguatan sebelumnya melalui perlakuan panas pada daerah intercritical annealing.



Pada percobaan ini, baja canai panas (hot rolled) API5LX65MO akan digunakan untuk menghasilkan baja dua fasa. Baja tersebut dipanaskan pada daerah intercritical annealing yaitu pada temperatur 740oC, 765oC, 790oC, dan 815oC dan ditahan pada waktu tahan 5, 10, 15, dan 20 menit. Setelah dipanaskan, baja segera didinginkan cepat (quenching) dalam media pendingin air. Pengujian tarik, kekerasan, dan pengujian tekuk dilakukan untuk menilai sifat mekanik baja dua fasa yang dihasilkan. Struktur mikro diamati menggunakan mikroskop optik.



Dari hasil percobaan, didapatkan temperatur pemanasan yang memberikan kekuatan paling tinggi adalah pada 815oC dengan waktu tahan 20 menit dengan tensile strength sebesar 699 N/mm2 atau naik sebesar 19,31% dari material awal. Nilai kekerasan yang didapatkan adalah 302 HVN atau naik sebesar 46% dari material awal. Elongasi turun dari 46% menjadi 26%. Fraksi volume martensit diperoleh sebesar 17,19%. Sedangkan dari hasil uji lengkung tidak ditemukan adanya keretakan pada permukaan material.

Deskripsi Alternatif :

Nowadays, the need for high strength steel with good formability in automotive applications is increasing. To meet this demand, the steel with those criterias is needed, one of them is dual phase steel with excellent combination of strength and drawability as a result of its microstructure consists of soft ferrite and hard martensite.



Dual phase steels can be obtained by heat treatment of HSLA steels. HSLA steels have high strength through the mechanism of grain refinement and precipitation hardening. Then, martensitic hardening can be given to HSLA steels in addition to the previous mechanisms through heat treatment at intrercritical annealing region.



In this research, API5LX65MO hot rolled steels were used to produce dual phase steel. Those steels were heated on intercritical annealing regional at the temperatures of 740oC, 765oC, 790oC, and 815oC and were retained at holding times of 5, 10, 15, and 20 minutes. Once heated, the steels were quickly cooled (quenched) in water coolant. Tensile test, hardness test, and bending test were done to measure the mechanical properties of the dual phase steels. Microstructures were observed using optical microscope.



From the result, it was found that the most optimal heating temperature was at 815oC with the holding time of 20 minutes. The tensile strength was observed to be at 699 N/mm2 (increased by 19.31% of the initial material). Hardness value was 302 HVN (increased by 46% of the initial material). Elongation dropped from 46% to 26%. The martensite volume fraction was 17,19%, while the result of bending tests did not reveal any cracks on the surface of the materials.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Dr. Eng. Akhmad Ardian Korda, ST., MT., Editor: Alice Diniarti

File PDF...