SINTESA DAN KARAKTERISASI BaFe(12-x)Ti0.5xMg0.5xO19 VARIASI (x=0,5;1;1,5;2) DENGAN DOPING Ti-Mg MENGGUNAKAN METODE METALURGI SERBUK UNTUK MATERIAL PENYERAP GELOMBANG ELEKTROMAGNETIK (RAMs)

Undergraduate Theses from JBPTITBPP / 2018-05-24 14:05:39
Oleh : SRI MULYATI LATIFAH (NIM: 23716004), S2 - Materials Engineering-FTMD
Dibuat : 2018-04-16, dengan 1 file

Keyword : Barium heksaferit, doping Ti-Mg, metalurgi serbuk, latice parameter, nilai koersivitas, saturasi magnet, remanen magnet, reflection loss.

Material penyerap gelombang elektromagnetik yang menggunakan tipe –M ferit BaFe(12-x)Ti0.5xMg0.5xO19 didoping Ti-Mg variasi (x=0,5;1;1,5;2) disintesa dengan metode metalurgi serbuk melalui proses pulverizing 2,4,8 jam. Penelitian ini bertujuan untuk membuat material penyerap gelombang mikro dan mengetahui pengaruh penambahan doping senyawa Ti-Mg terhadap peningkatan sifat magnet barium heksaferit juga mengetahui hasil proses pulverizing terhadap nilai penyerapan gelombang elektomagnetik. Dari hasil pengujian XRD adanya perubahan latice parameter a,b,c pada sistem kristal heksagonal dengan meningkatnya volume kristal dan merubah nilai porositas sampel lebih rendah sebesar 6%. Hasil XRD dapat dikonfirmasi dengan hasil pengujian SEM yaitu dengan terbentuknya struktur kristal heksagonal pada sampel berbentuk pelet dengan pembesaran 5000x. Sedangkan sampel yang berbentuk serbuk terlihat adanya perubahan ukuran yang diambil secara kasar dengan rata-rata nilai terkecil dideteksi dengan SEM adalah 217,63 nm setelah proses pulverizing selama 8 jam , dan tampak sampel serbuk teraglomerasi akibat adanya gaya vander walls dan Rasio perbandingan antara tegangan permukan dengan volume lebih tinggi. Dari hasil penelitian pada BaFe(12-x)Ti0.5xMg0.5xO19 dengan penambahan doping dapat meningkatkan sifat magnet dan nilai penyerapan gelombang elektomagnetiknya. Penambahan doping Ti-Mg dengan x=2 sifat magnet meningkat dengan nilai koersivitasnya rendah yaitu 0,177 kOe, saturasi magnet tinggi, Ms 54,013 emu/gram dan remanan magnetnya, Mr 21,744 emu/gram. Untuk nilai penyerapan gelombang elektromagnetik yang tertinggi dihasilkn pada x=1,5 ketebalan 2 mm sebesar -19,500 dB pada frekuensi 10,300 GHz.

Deskripsi Alternatif :

The electromagnetic wave absorbent materials using the M-type ferrite BaFe(12-x) Ti0.5xMg0.5xO19 doped with Ti-Mg and variation of x=0.5;1;1,5;2 is synthesized by powder metallurgy method through pulverizing process 2,4 and 8 hours. The aim of this research work is to make electromagnetic wave absorbing materials (RAMs = Radar Absorbent Materials) and to understand the effect of doping addition of Ti-Mg compound on increasing magnetic properties of barium hexaferrite also to unerstand the result of pulverizing process to the absorption value of electromagnetic wave. From the result XRD test doping additions can change the latice parameter a, b, c on the hexagonal crystalline system, if the crystal volume increases then the X-Ray density is low. The XRD results can be confirmed by SEM test results with the formation hexagonal crystal structure on a pelletized sample with 5000x magnification. While the powdered sample showed a rough size change taken with the smallest average value detected with SEM was 217.63 nm after pulverizing process for 8 hours, and looked agglomerated powder. From the results of research on BaFe(12-x)Ti0.5xMg0.5xO19 with the addition of doping can improve the magnetic properties and absorption values of electromagnetic waves. The more addition of doping Ti-Mg for x=2 its magnetic properties is increasing with coercivity value of 0.177 kOe, saturation magnetization, Ms 54.013 emu/gram and remanent magnetization, Mr 21.744 emu/gram. For the highest electromagnetic wave absorption value or reflection loss is achieved at x=1.5 with thickness of 2 mm equal to -19.500 dB at frequency 10.300 GHz.


Copyrights : Copyright (c) 2001 by Perpustakaan Digital ITB. Verbatim copying and distribution of this entire article is permitted by author in any medium, provided this notice is preserved.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS2 - Materials Engineering-FTMD
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing :

    Dr. Ir. Slameto Wiryolukito.

    Dr. Dedi, ST., MT., Editor: Alice Diniarti

File PDF...