PENGARUH PENAMBAHAN MgO DAN BORAKS TERHADAP PEMBENTUKAN FASA MULLITE DARI PYROPHYLLITE PADA TEMPERATUR PEMBAKARAN 1100OC

Undergraduate Theses from JBPTITBPP / 2017-10-09 10:32:50
Oleh : SOFYAN REZA (NIM : 13707067); Pembimbing: Dr. Ir. Aditianto Ramelan, S1 - Material Engineering Study Programme
Dibuat : 2011, dengan 7 file

Keyword : Mullite, Pyrophyllite, Fluks, Slip Casting, MgO, Boraks

Aplikasi dari berbagai produk keramik clay-based sangat ditentukan oleh sifat fisiknya, dimana sifat fisik tersebut sangat tergantung pada komposisi kimia, mineral dan ukuran partikelnya. Salah satu fasa yang muncul dari hasil pembakaran produk keramik clay-based adalah Mullite. Proses kristalisasi mullite merupakan fenomena yang umum ditemui pada proses transformasi termal dari pyrophyllite. Pada kondisi tanpa aditif, fasa Mullite mulai muncul pada




temperatur pembakaran 960oC dan terbentuk sempurna pada temperatur pembakaran 1590oC[17]. Temperatur pembentukan Mullite dari pembakaran Pyrophyllite dapat diturunkan dengan menambahkan flux pada campuran.




Pada penelitian ini dilakukan penambahan fluks berupa MgO dan Boraks untuk mempercepat terbentuknya fasa Mullite pada pembakaran Pyrophyllite di temperatur 1100oC, menggunakan metode slip casting pada pembuatan sampelnya. X-Ray Diffraction dan SEM digunakan dalam proses karakterisasi




sampel. Penambahan 3% MgO dapat memunculkan Mullite sebanyak 38,8 w/o dan penambahan 9% Boraks dapat memunculkan Mullite sebanyak 27 w/o. Mullite yang terbentuk tidak berbentuk jarum melainkan berbentuk platelet dan rod.

Deskripsi Alternatif :

The application of clay based ceramics product is determined by its physical properties. Chemical composition and particle size of the mineral involved in the body mixture will determine the physical properties. One of the phases formed in fired clay based ceramics is Mullite. The crystallisation of Mullite is a common phenomena occured in thermal transformation from the mineral pyrophyllite.




Without additive Mullite phase will start to occure at 960oC and will completely form at 1590oC[17]. The Mullite formation temperature can be decreased by the addition of some fluxes in mixture. The Mullite characterisation was carried out by using an X-Ray diffraction method and SEM.




In this observation MgO and Borax were added as flux to accelerate the formation of Mullite at 1100oC. The specimens were prepared by a slip casting methods. It is observed that the addition of 3% MgO produced 38.8 w/o of Mullite phase, while 9% addition of Borax has produced 27 w/o. The Mullite phases were observed in the form of platelet and rod like structure.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing: Dr. Ir. Aditianto Ramelan, Editor: Alice Diniarti

File PDF...