PENGARUH KONSENTRASI ASAM FOSFAT PADA KARAKTERISTIK MEMBRAN NATA DE COCO TERFOSFATASI

Undergraduate Theses from JBPTITBPP / 2017-05-19 10:38:48
Oleh : SHABRINA FARHA NISA (NIM : 10508033), S1 - Department of Chemistry
Dibuat : 2014, dengan 7 file

Keyword : minyak bumi, Sel bahan bakar (fuel cell), Membran Nata De Coco

Ketersediaan SDA (Sumber Daya Alam), khususnya minyak bumi yang dijadikan sebagai sumber energi dalam kehidupan sehari-hari semakin menipis. Sel bahan bakar (fuel cell) merupakan salah satu sumber energi pengganti yang cukup berpotensi menggantikan minyak

bumi. Dewasa ini, membran yang dipakai sebagai zat elektrolit dalam fuel cell adalah membran Nafion. Namun, karena membran nafion harganya cukup mahal, perlu diteliti kembali material alternatifnya. Dalam penelitian ini, telah dilakukan modifikasi terhadap membran nata de coco menjadi membran nata de coco terfosfatasi supaya dapat digunakan sebagai membran polimer elektrolit pada DMFC (Direct Methanol Fuel Cell). Proses fosfatasi film nata de coco dengan massa 0,2882 g dilakukan dalam campuran pereaksi N,N-dimetilformamida (DMF), urea, dan asam fosfat yang bervariasi konsentrasinya dengan gelombang mikro (microwave) pada daya 560 Watt. Penelitian ini menghasilkan tiga jenis membran nata de coco terfosfatasi, yaitu membran nata de coco yang difosfatasi dengan 2 g H3PO4 (F1), 4 g H3PO4 (F2), dan 6 g H3PO4 (F3). Membran yang dihasilkan dikarakterisasi

dengan analisis gugus fungsi dengan FTIR-ATR, uji KPI (Kapasitas Penukar Ion), konduktivitas proton, derajat penggembungan, permeabilitas metanol, dan analisis morfologi membran dengan SEM (Scanning Electron Microscope). Hasil penelitian menunjukkan bahwa membran F3 merupakan membran yang paling baik dijadikan sebagai membran elektrolit pada DMFC dengan nilai KPI sebesar 9,19 mEq/g dan nilai konduktivitas proton pada 80°C (100 mV) sebesar 0,0442 S/cm.

Deskripsi Alternatif :

The availability of natural resources, especially petroleum which is used as a source of energy in everyday life, is running low. Fuel cell is one of the substitute energy sources considered potential to replace petroleum. Today, Nafion® is used as an electrolyte membrane in fuel cells. However, due to its high price, alternative materials need to be investigated. In this study, modification of nata de coco membranes to phosphorylated ones has been carried out in order to be applied as polymer electrolyte membrane in DMFC (Direct Methanol Fuel Cell). The phosphorylation of nata de coco membranes having a mass of 0,2882 g each was done in a mixture of N,N dimethylformamide (DMF), urea and varied concentration of phosphoric acid in a microwave with 560 watts of power. This work produced three variations of phosphorylated nata de coco membranes, i.e. phosphorylated membranes nata de coco with 2 g of H3PO4 (F1), 4 g of H3PO4 (F2), and 6 g of H3PO4 (F3). The resulting membranes were characterized by functional group analysis by FTIR-ATR, Ion Exchange Capacity (IEC), proton conductivity, degree of swelling, methanol

permeability, and membrane morphology analysis by SEM (Scanning Electron Microscope). The experimental results showed that the F3 membrane is the optimum electrolyte

membrane having an IEC value of 9,19 mEq/g and proton conductivity of 0,0442 S/cm at 80°C.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS1 - Department of Chemistry
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id