PEMBUATAN MEMBRAN SELULOSA ASETAT DARI PULP KENAF (HISBISCUS CANNABINUS)

Master Theses from JBPTITBPP / 2017-09-27 15:39:43
Oleh : SENNY WIDYANINGSIH (NIM 20501018), S2 - Chemistry
Dibuat : 2003, dengan 7 file

Keyword : Kenaf pulp, Hibiscus cannabinus, cellulose, membrane
Subjek : Organic chemistry: Cellulose
Kepala Subjek : Chemistry
Nomor Panggil (DDC) : T 547.782 WID
Sumber pengambilan dokumen : 20041066

Pulp kenaf (Hibiscus cannabinus) merupakan salah satu sumber selulosa dan bahan non kayu yang dapat dimanfaatkan untuk menghasilkan selulosa asetat (SA). Analisa spektroskopi inframerah menunjukkan puncak khas gugus asetil pada daerah 1237,4 cm-1 SA kenaf yang dihasilkan mempunyai kadar asetil 40,40% sedangkan SA komersial 40,11%. Membran selulosa asetat dibuat dengan cara inversi fasa dalam tiga variasi komposisi 14%, 16%, dan 18% berat (SA), sedangkan karakterisasi membran dilakukan pada tiga variasi tekanan operasional yaitu 1 sampai 3 kgf/cm2. Permeabilitas air terbesar adalah membran dengan komposisi berat SA 14% tekanan 3 kgf/cm2 dengan fluks 253,75+0,00 L/m2jam untuk membran SA kenaf dan fluks 137,57+3,53 L/m2jam untuk membran SA komersial. MWCO terkecil adalah membran dengan komposisi 18% tekanan 1 kgf/cm2 dengan nilai 4,8. 105 untuk membran SA kenaf dan 1,1.105 untuk membran SA komersial. Hasil analisa SEM menunjukkan bahwa membran SA komersial mempunyai struktur yang lebih rapat daripada membran SA kenaf Sedangkan berdasarkan uji tarik modulus Young terbesar adalah membran komposisi 18% dengan nilai 6.85E+07 untuk SA kenaf dan 5.60E+07 untuk SA komersial. Membran SA kenaf dan membran SA komersial mempunyai efisiensi yang sama untuk penjernihan air keruh yang mengandung ion) dengan rejeksi 100%. Fluks terbesar adalah membran dengan komposisi berat SA 14% tekanan 3 kgf/cm dengan fluks 429,04+1,77 L/m2jam untuk membran SA kenaf dan 201,78+3,06 L/m2jam untuk membran SA komersial.

Deskripsi Alternatif :

Kenaf (Hibiscus cannabinus) pulp is one of non wood cellulose sources which can be used for producing cellulose acetate (CA). Infrared spectroscopy showed the characteristics of acetyl group at 1237,4 cm-1. The acetyl content of kenaf CA is 40.40% and commercial CA is 40.11%. CA membrane have been prepared by using phase inversion method in three varied compositions, i.e. 14, 16, and 18 wt.% of CA. The membrane characteristics were determined at three varied applied pressures, i.e. 1, 2, and 3 kgf/cm2. The highest water permeability was obtained by membranes of 14 wt.% CA, shown by fluxes of 253.75+0.00 L/m2h for kenaf CA and 137.57+3.53 L/m2h for commercial CA at 3 kgf/cm2. The lowest MWCO was obtained by membrane of 18 wt.% CA, shown by fluxes of 4.8.105 L/m h for kenaf CA and 1.1.105 L/m h for commercial CA at 1 kgf/cm. SEM analysis showed that commercial CA membrane was denser than kenaf CA membrane. The highest tensile strength was obtained by membranes of 18 wt.% CA, shown by Young modulus 6.85E+07 for kenaf CA membrane and 5.60E+07 for commercial CA membrane. Kenaf CA membrane and commercial CA membrane have the same efficiency in water purification with 100% rejection towards) ions. The highest permeability was obtained by membranes of 14 wt.% CA, shown by a flux of 429.04+1.77 L/m2h for kenaf CA and 201.78+3.06 L/m h for commercial CA at 3.

Copyrights : Copyright Â(c) 2001 by ITB Central Library. Verbatim copying and distribution of this entire article is permitted by author in any medium, provided this notice is preserved.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing: DR. Ing. Cynthia L. Radiman, Editor: Vika A. Kovariansi

File PDF...