PENGARUH TEMPERATUR DAN DURASI SOLVOTERMAL TERHADAP SINTESIS LAPISAN TIPIS METAL ORGANIC FRAMEWORK-5 (MOF-5) PADA SUBSTRAT KACA FLUORINE TIN OXIDE (FTO)

THE EFFECT OF TEMPERATURE AND SOLVOTHERMAL DURATION ON METAL ORGANIC FRAMEWOR-5 THIN FILM SYNTHESIS ON FLUORINE TIN OXIDE (FTO) GLASS

Undergraduate Theses from JBPTITBPP / 2018-03-13 16:29:56
Oleh : SEFINA RAHMATUNISA (nim : 13313012) - RAHMAT MAULANA (nim : 13313023), S1 - Engineering Physics-FTI
Dibuat : 2018, dengan 1 file

Keyword : MOF-5, temperatur, durasi, solvotermal, FTO

Penelitian ini bertujuan untuk mengetahui pengaruh temperatur dan durasi solvotermal pada sintesis lapisan tipis Metal Organic Frameworks-5 (MOF-5) yang ditumbuhkan pada substrat kaca Fluorine Tin Oxide (FTO). Metal Organic Frameworks merupakan material polimer berpori yang terdiri atas ion-ion logam yang memiliki ikatan kovalen dengan ligan organik. MOF-5 terdiri atas Zn4O yang berikatan dengan 1,4-benzenedicarboxylic (BDC) sebagai ligan organiknya. MOF-5 sebagai material insulator dan memiliki luas permukaan serta keteraturan porositas yang tinggi dapat digunakan pada berbagai aplikasi seperti sensor gas, penyimpanan hidrogen, dan pemisahan gas. Lapisan tipis MOF-5 dapat disintesis dengan metode solvotermal, yaitu pemanasan campuran ligan organik dengan ion logam pada suatu sistem pelarut dengan pengaturan durasi sintesis, temperatur, konsentrasi campuran dan jenis pelarut. Substrat berupa kaca Fluorine Tin Oxide (FTO) dicelupkan ke dalam sistem pelarut tersebut. Pelarut yang digunakan yaitu pelarut N,N-dimethyl-formamide (DMF). Setelah dilakukan pemanasan, didapatkan kristal yang tumbuh pada substrat, dilanjutkan dengan proses pencucian, serta proses pengeringan. Kristal MOF-5 dikarakterisasi dengan Scanning Electron Microscope (SEM) untuk mengetahui morfologi kristal, metode Bruneauer, Emmet and Teller (BET) untuk mengkarakterisasi luas permukaan, dan X-Ray Diffraction (XRD) untuk mengetahui fasa kristalin yang terbentuk.


Pada penelitian ini, MOF-5 disintesis secara solvotermal di atas substrat kaca Fluorine Tin Oxide dengan material terdistribusi lebih merata pada temperatur 150°C dan durasi 8 jam.

Deskripsi Alternatif :

This research aims to know the effects of solvotermal temperature and duration on synthesis of Metal Organic Framework (MOF-5) thin film growing on Fluorine Tin Oxide (FTO) glass as substrate. Metal Organic Framework (MOF) is a porous polymer composed of metal ions having covalent bonds with organic ligands. MOF-5 consists of Zn4O binding to 1,4-benzenedicarboxylic (BDC) as the organic ligands. MOF-5 as an insulator material has large surface and high porosity that can be utilized as gas sensor, hydrogen storage and gas separation. MOF-5 thin film can be synthesized by solvotermal method, which is heating the mixture of organic ligands with metal ions in a solvent system. Time and temperature of synthesis, metals and ligands concentration and type of solvent are obtained. Substrate immersed in the solution is Fluorine Tin Oxide (FTO) glass. The solvent used is N, N-dimethyl-formamide (DMF). After heating, the crystal of MOF-5 will be grown on the substrate, continued by drying process. The formed MOF-5 thin film were characterized by Scanning Electron Microscope (SEM) to determine the crystal morphology, method of Bruneauer, Emmet and Teller (BET) to characterize the surface area, and Powder X-Ray Diffraction (PXRD) to determine the crystalline phase.


In this study, MOF-5 was solvothermal synthesized on Fluorine Tin Oxide glass with a more uniformly distributed material at a temperature of 150°C and a duration of 8 hours.


Copyrights : Copyright (c) 2001 by Perpustakaan Digital ITB. Verbatim copying and distribution of this entire article is permitted by author in any medium, provided this notice is preserved.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS1 - Engineering Physics-FTI
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing:

    Brian Yuliarto, ST.,M.Eng.,Ph.D

    Dr. Damar Rastri Adhika, ST., M.Sc., Editor: Alice Diniarti

File PDF...