Studi pembentukan superkonduktor Ba1-xKxBiO3 melalui proses elektrokimia.

Master Theses from JBPTITBPP / 2001-05-28 12:32:00
Oleh : Rahmat Hidayat, S2 - Engineering Materials
Dibuat : 2001-01-00, dengan 1 file

Keyword : Ba1-XKXBiO3;potentiostatic and galvanostatic eletrochemical methods; galvanostatic process; superconductivity properties.
Nomor Panggil (DDC) : T 620.112 973 H

Telah dibuat film Ba1-XKXBiO3 melalui proses elektrokimia potensiostat dan galvanostat yang dilengkapi dengan proses aniling. Karakterisasi yang dilakukan meliputi pengukuran kurva resistivitas-suhu untuk menentukan suhu kritis bahan, sedangkan karakterisasi struktur dilakukan dengan pengukuran difraksi sinar-X, dan pengamatan pola SEM. Pengukuran kurva transisi resistif (T)menunjukkan bahwa film yang dihasilkan dengan proses galvanostat baik yang dilengkapi maupun tanpa prosses anil tidak m enunjukkan difat superkonduktivitas. Di pihak lain, suhu kritis Tc yang ditentukan dari kurva (T) pada sampel yang diperoleh dari proses potensiostat memiliki nilai bervariasi antara 10-11 K dan Tcon yang berkisar antara 13 dan 18 K, bergantung pada tegangan elektroda yang digunakan dalam proses sintesis. Tc tertinggi sebesar 11 K dan kualitas struktur mikro terbaik dicapai pada sampel hasil sintesis dengan tegangan 0,65 V. Namun hasil analisis data karakterisasi secara keseluruhan menunjukkan adanya kemungkinan meningkatkan kualitas hasil sintesis dengan tegangan lebih tinggi melalui proses anil yang lebih tepat.

Deskripsi Alternatif :

Films of Ba1-XKXBiO3 have been synthesized by means of potentiostatic and galvanostatic eletrochemical methods incorporating a post annealing process. The critical temperature was determined from measurement of resistive transition vurve, while structural characterization was carried out by X-ray diffraction and SEM measurements. The resistive transition curves show that the films prepared by galvanostatic process do not indicate superconductivity properties. On the other hand, the critical temperature measurement from the samples prepared by potensiostatic process show that th Tc varies between 13 and 18K depending on the electrode voltage used in the process. The highest Tc of 11 K and the best micro structure were attained in the sample prepared with electrode voltage of 0,65 V. Further analysis of the characterization data reveals however, that the sample prepared with higher electrode voltage may attain higher quality by employing more appropriate annealing process.


Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Editor:

Download...