RECOVERY PERAK (I) DARI LIMBAH CUCI/CETAK FOTO DENGAN MENGGUNAKAN TEKNIK MEMBRAN CAIR EMULSI

Master Theses from / 2006-09-25 08:57:32
Oleh : Imam Santoso, S2 - Chemistry
Dibuat : 2000-10-00, dengan 1 file

Keyword :

limbah cuci/cetak foto,menggunakan teknik membran cair emulsi.




Nomor Panggil (DDC) : T. 541.348 2 SAN
Sumber pengambilan dokumen : 20051765

Abstrak :



Telah dipelajari pada penelitian ini ekstraksi perak (I) dari limbah cuci/cetak foto hitam putih dengan teknik membran cair emulsi. Fasa membran yang berupa emulsi terdiri dari kerosen sebagai pelarut, sorbitan monooleat (Span 80) sebagai surfaktan, dimetildiokta.desilammonium bromida sebagai pengemban dan HNO3 sebagai fasa internal. Dari hasil percobaan didapat kondisi optimum sebagai berikut : Perbandingan volume fasa internal dengan volume fasa membran adalah 1 : 1.Konsentrasi surfaktan yang digunakan 2% (v/v). Konsentrasi dimetildioktadesilammonium bromida 0,01M. Lama pengadukan pembuatan emulsi 20 menit. Kecepatan pengadukan pembuatan emulsi 1100 rpm. Lama pendiaman emulsi 3 menit. Perbandingan volume emulsi dengan volume fasa ekstemal 1 : 5. Kecepatan kontak emulsi 500 rpm. Waktu kontak emulsi 40 menit. Konsentrasi peraktiosulfat dalam fasa ekstemal 100 ppm. pH larutan fasa ekstemat. 3, sedang pH larutan fasa internal adalah 1. Penerapan kondisi optimum pada ekstraksi perak (I) dari limbah cucilcetak foto hitam putih dicapai angka rata-rata 77,33 % di mana 56,06 % rata-rata perak (I) terdapat pada fasa internal dan 22,66 % rata-rata terdapat pada fasa ekstemal. Pada penelitian ini juga dipelajari pengaruh matriks seperti ion Br , ion 52032-, dan ion 5032_ terhadap persen ekstraksi perak (I). Ion Br" (100 ppm), ion 5032_ (100 ppm dan 200 ppm) menunuikan persen ekstraksi perak (I). Ion Br (200 ppm) dan ion 52O32- (200 ppm) menaikkan persen ekstraksi perak (I), sedang ion 52032-(100 ppm) tidak berpengaruh terhadap parses ekstraksi perak.



Deskripsi Alternatif :

Abstract :



Extraction of silver (I) has been studied from black/white printing photographic waste by emulsion liquid membrane technique. Composition emulsion at the membrane phase was cerosene as solvent, sorbitan monooleat (span 80) as surfactant, dimethyldioctadesylammonium bromide as carrier and as internal phase was HNO3. Optimum condition was obtained : Ratio of internal phase volume and membrane phase volume was 1 : 1. Concentration of surfactant was 2 % (v/v). Time of making emulsion was 20 second. Rate of shining emulsion was 1100 rpm. Rest time emulsion was 3 second. Ratio of emulsion volume and external phase volume was 1 : 5. Emulsion contact rate was 500 rpm. Emulsion contact time was 40 second. Concentration of silvertiosulfate as external phase was 100 ppm; pH of external phase was 3 and pH of internal phase was I. Optimum condition was applied in silver (I) extraction from black/white printing photographic waste. It was obtained 77.33 % average which 56.06 % silver (I) average of internal phase and 22.66 % in the external phase. Effect of ma-tries such Br , 52032- and 5032- ions has been studied to percent extraction of silver (I). Br (100 ppm) ion and 5032- (100 ppm, 200 ppm) ion decreased silver (I) percent extraction. While Br (200 ppm) ion and 52032- (200 ppm) ion icreased silver (I) percent extraction. And ion 52032- (100 ppm) didn't effect silver (I) percent extraction.




Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID Publisher
OrganisasiS
Nama KontakYoka Adam Nugrahaa, S.Sos.
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon022 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing :
    Buchari,Dr.

    Scan :
    Mudjiono
    (25-09-2006)

    , Editor: mudjiono@

File PDF...