PENGARUH LAPISAN PENYANGGA PrBa2Cu3O7-δ PADA FILM TIPIS SUPERKONDUKTOR YBa2Cu3O7-δ

Master Theses from #PUBLISHER# / 2006-06-02 10:29:20
Oleh : Horasdia Saragih (NIM : 20296506), S2 - Physics
Dibuat : 1998-10-00, dengan 1 file

Keyword :

Lapisan penyangga, Substrat, Magnetron sputtering

Buffer layer, Substrate, Magnetron sputtering


Subjek :
Applied physics - electrical engineering

Kepala Subjek :
Engineering

Nomor Panggil (DDC) :
T 621.381 5 SAR

Sumber pengambilan dokumen : Tesis Magister fisika, Bidang Khusus fisika Material Elektronik. (20051762)

Abstrak :

Telah berhasil difabrikasi film tipis YBa2Cu3O7-δ dengan lapisan penyangga PrBa2Cu3O7-δ pada substrat MgO(100). Metode yang digunakan adalah On-axis Unbalanced dc Magnetron Sputtering. Film tipis yang dideposisi dikarakterisasi dengan X-Ray Diffraction (XRD), pengukuran p-T dan Scanning Electron Microscopy (SEM). Dari hasil analisa XRD, diperoleh fraksi volume PrBa2Cu3O7-δ/MgO sebesar 79,84%, fraksi volume YBa2Cu3O7-δ/MgO sebesar 69,01%, fraksi volume YBa2Cu3O7-δ/PrBa2Cu3O7-δ/MgO (film-I) sebesar 57,23% dan fraksi volume YBa2Cu3O7-δ/PrBa2Cu3O7-δ/MgO (film-II) sebesar 65,54%. Hasil pengukuran p-T, didapatkan temperatur kritis YBa2Cu3O7-δ/MgO sebesar 84,15K, temperatur kritis YBa2Cu3O7-δ/PrBa2Cu3O7-δ/MgO (film-I) sebesar 85,00K dan temperatur kritis YBa2Cu3O7-δ/PrBa2Cu3O7-δ/MgO (film-II) sebesar 85,70K. Penggunaan lapisan penyangga PrBa2Cu3O7-δ menurunkan fraksi volume superkonduktor film tipis YBa2Cu3O7-δ/ yang ditumbuhkan pada substrat MgO(100), namun jika ketebalan lapisan penyangga PrBa2Cu3O7-δbertambah, cenderung meningkatkan fraksi volume film tipis YBa2Cu3O7-δ. Kehadiran lapisan penyangga dapat meningkatkan temperatur kritis film tipis superkonduktor YBa2Cu3O7-δ, di samping itu, temperatur kritis film tipis superkonduktor YBa2Cu3O7-δ juga semakin meningkat dengan bertambahnya ketebalan lapisan penyangga PrBa2Cu3O7-δ

Deskripsi Alternatif :

Abstract :

The thin film YBa2Cu3O7-δ with buffer layer PrBa2Cu3O7-δ on substrate MgO (100) have successful fabricated by using On-axis unbalanced dc magnetron sputtering method. The deposit thin film was characterized by X-ray diffraction, p-T measuring and Scanning electron microscopy. The X-ray diffraction analysis result the volume fraction of PrBa2Cu3O7-δ/MgO(100), YBa2Cu3O7-δ/MgO(100), YBa2Cu3O7-δ/ PrBa2Cu3O7-δ/MgO(100) (film-I), and YBa2Cu3O7-δ/PrBa2Cu3O7-δ/ MgO(100) (film-II) was 79,84%, 69,01%, 57,23% and 65,54% respectively. The using buffer layer PrBa2Cu3O7-δ will decrease the volume fraction of the thin film superconductor YBa2Cu3O7-δ, however the volume fraction will increase by increasing of the thickness of the buffer layer PrBa2Cu3O7-δ. Present of the buffer layer affect the increasing of the critical temperature of the thin film superconductor YBa2Cu3O7-δ as well as increasing of the thickness of the buffer layer PrBa2Cu3O7-δ

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing :
    M. Barmawi, Prof., Ph.D.

    Scan :
    Hidayat (2006-05-31)

    , Editor: hidayat@#publisher#

File PDF...