SINTESIS DAN KARAKTERISASI SERBUK NANOMAGNETIK FE3O4 DENGAN VARIASI KONSENTRASI SODIUM ALGINATE SEBAGAI CHELATING AGENT

Undergraduate Theses from JBPTITBPP / 2017-10-09 10:32:50
Oleh : RIKY CIAYADI (NIM : 13707062); Pembimbing : Dr. Ir. Bambang Sunendar, S1 - Material Engineering Study Programme
Dibuat : 2011, dengan 7 file

Keyword : ko-presipitasi, superparamagnetik, natrium alginat, Fe3O4.

Fe3O4 merupakan suatu padatan yang disintesis dari suatu senyawa berbasis besi dengan menggunakan metode ko-presipitasi dari campuran larutan Ferrous sulphate heptahydrate (FeSO4.7H2O) dan Ferric chloride hexahydrate (FeCl3.6H2O) dengan ratio perbandingan mol 1 : 2 yang dipanaskan pada suhu 70oC selama 30 menit pada kondisi lingkungan tertutup. Parameter yang digunakan dalam proses




sistesis Fe3O4 ini adalah konsentrasi dari sulphate heptahydrate (FeSO4.7H2O) dan Ferric chloride hexahydrate (FeCl3.6H2O ) dan sodium alginate. Untuk mengetahui fasa, morfologi mikrostruktur permukaan, bentuk partikel nano, gugus-gugus kimia dan sifat magnetik digunakan X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Fourier Transform Infrared Spectrometer (FTIR) dan vibrating sample magnetometer (VSM). Hasil uji pada serbuk Fe3O4 didapatkan fasa tunggal Fe3O4 dan Puncak karakteristik Fe3O4 dengan indeks sesuai referensi JCPDS File No. 19−629, yaitu (2 2 0), (3 1 1), (4 0 0), (4 2 2), (5 1 1) and (4 4 0) pada 2θ = 30,2o, 35,5o, 43,1o, 53,4o, 57o, dan 62,6o. Kemudian pada karakterisasi SEM morfologi dari partikel Fe3O4 terlihat bulat-bulat dan terdispersi pada diameter rata-rata partikel tanpa alginat adalah 46 nm dan dengan alginat adalah 40 nm. Pada karakterisasi FTIR




terlihat adanya gugus O-H dengan panjang gelombang 3386,39cm-1 dari alginat dan adanya gugus Fe-O dengan panjang gelombang 563,112cm-1, bearti memperlihatkan




adanya interaksi antar alginat-FeO dari prekursor sebagai awal terjadinya rantai metal Fe-O-Fe. Dari karakterisasi VSM kita dapatkan kurva histerisnya yang menandakan




sifat magnetiknya dari sifat magnetik partikel Fe3O4 adalah superparamagnetik dengan momen magnetnya sebesar 67,29 emu/gram dan sifat magnetik pada penambahan alginat maka momen magnet yang didapat lebih kecil yaitu dengan rentang (60,7 sampai 42,48 emu/gram), sampai pada penambahan natirum alginat 0,2% maka momen magnetnya 57,31 emu/gram.

Deskripsi Alternatif :

Fe3O4 is a solid which is synthesized from an iron-based compound using the co-precipitation method of a mixture of ferrous sulphate heptahydrate solution (FeSO4.7H2O) and Ferric chloride hexahydrate (FeCl3.6H2O) with a ratio of mole ratio 1: 2 is heated at 70°C for 30 minute in a closed system. Parameter used in the synthesis of Fe3O4 is the concentration of Ferrous sulphate heptahydrate(FeSO4.7H2O) and Ferric chloride hexahydrate (FeCl3.6H2O) and sodium alginate. To determine the phase, microstructure of the surface, the shape of nano particles, functional group and magnetic properties to use X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Fourier Transform Infrared Spectrometer (FTIR) and a vibrating sample magnetometer (VSM). The test results obtained on single-phase Fe3O4 and the characteristic peak with the index corresponding JCPDS File No. reference. 19-629, ie (2 2 0), (3 1 1), (4 0 0), (4 2 2), (5 1 1) and (4 4 0) at 2θ = 30,2o, 35,5o, 43,1o, 53,4o, 57o and 62,6o. Then in the characterization by SEM the morphology of the particles Fe3O4 visible round and dispersed at an average diameter




of particles without alginate is 46 nm and with alginate is 40 nm. In the FTIR characterization of the OH group with a visible wavelength 3386,39 cm-1 from alginate and Fe-O clusters with wavelengths 563,112 cm-1, this showed the interaction among alginate-FeOH itself from precursor as Fe-O-Fe polimerization. VSM characterization we get a hysteria curve which indicates the magnetic properties of




Fe3O4 is superparamagnetic with the magnetic moment 67,29 emu/gram and magnetic properties on the addition of alginate has smaller magnetic moment of the range (60,7




to 42,48 emu/gram), until the addition of 0,2% sodium alginate so the magnetic moment is 57,31 emu/gram.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Dr. Ir. Bambang Sunendar, Editor: Alice Diniarti

File PDF...