STUDI PENGARUH PERLAKUAN PERMUKAAN AWAL DAN PERLAKUAN TERMAL TERHADAP HASIL PELAPISAN DOUBLE HARD CHROMIUM BAJA JIS SCM440H

Study of the Effect of Initial Surface Treatment and Thermal Treatment of Double Hard Chromium Coatings Results of Steel JIS SCM440H

Undergraduate Theses from JBPTITBPP / 2018-03-13 16:27:43
Oleh : RIAN DIKDIK ANDIKA (NIM : 13713057), S1 - Materials Engineering-FTMD
Dibuat : 2018, dengan 1 file

Keyword : hard chrome, perlakuan awal, perlakuan termal, difusi, kekerasan

Pelapisan hard chrome diterapkan pada komponen teknik yang memerlukan kekerasan tinggi khususnya untuk ketahanan aus dan kekuatan ikatan lapisan yang baik. Untuk mendapatkan kualitas lapisan baik dengan kekerasan tinggi dan kekuatan ikatan lapisan yang tinggi maka perlu dilakukan optimasi proses pelapisan. Proses pelapisan pada penelitian ini dilakukan dengan double plating untuk mendapatkan lapisan yang tebal. Proses diawali dengan memberikan perlakuan awal pada hasil lapisan pertama dengan variasi; tanpa perlakuan, sand blasting dan shot peening. Selain itu juga dilakukan perlakuan termal annealing (600oC selama 1 jam) pada sampel untuk mendorong proses difusi krom lebih jauh kedalam substrat untuk meningkatkan chemical bonding.



Variasi perlakuan awal dilakukan untuk mengetahui karakteristik morfologi permukaan deposit krom. Pada perlakuan permukaan shot peening didapatkan morfologi butir paling seragam. Selain itu nilai kekerasan permukaan lapisan dari tertinggi ke terendah berturut-turut sampel tanpa perlakuan permukaan, perlakuan sand blasting, perlakuan shot peening. Sedangkan perlakuan termal memberikan perubahan kombinasi unsur Cr+Fe pada sampel sand blasting yang menunjukkan adanya difusi kedalam substrat sehingga mengindikasikan adanya peningkatan chemcical bonding. Namun menimbulkan retak mikro dan menimbulkan efek penurunan kekerasan yang signifikan dibandingkan kekerasan sampel tanpa perlakuan termal.

Deskripsi Alternatif :

Hard chrome coating is applied to engineering components that require high hardness especially for wear resistance. To obtain good coating quality with high hardness and high coat bond strength it is necessary to optimize the coating process. The coating process in this study was done by double plating beginning with pre-treatment on the first layer result with variation; without treatment, sand blasting and shot peening. In addition, annealing thermal treatment (600oC for 1 hour) was applied to the sample to encourage further diffusion of chromium into the substrate to improve chemical bonding.



Variation of pre-treatment was done to know the morphological characteristics of chromium deposit surface. In the surface treatment shot peening obtained the most uniform grain morphology. In addition, the coating surface hardness value from the highest to the lowest consecutive samples without surface treatment, sand blasting treatment, shot peening treatment. While the thermal treatment provides a change in the combination of Cr + Fe elements in sand blasting samples which indicate the diffusion into the substrate, thus indicating an increase in chemical bonding. However, it has microstructural cracks result and a significant effect of decreasing hardness compared to sample hardness without thermal treatment.

Copyrights : Copyright (c) 2001 by Perpustakaan Digital ITB. Verbatim copying and distribution of this entire article is permitted by author in any medium, provided this notice is preserved.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS1 - Materials Engineering-FTMD
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing :

    Dr. Eng. R. Dadan Ramdan

    Firmansyah Sasmita, S.T., M.T., Editor: cecep hikmat

File PDF...