SINTESIS TITANIUM DIOKSIDA (TiO2) DARI KONSENTRAT ILMENIT DENGAN FUSI KAUSTIK UNTUK BAHAN KERAMIK MAJU

Undergraduate Theses from JBPTITBPP / 2017-09-27 10:37:14
Oleh : RENI NOVIYANTI (NIM : 12506012), S1 - Metallurgy
Dibuat : 2011, dengan 6 file

Keyword : Ilmenit, TiO2, Fusi kaustik

Ilmenit dengan rumus kimia FeTiO3 merupakan salah satu potensi tambang yang ada di Indonesia. Ilmenit adalah salah satu unsur terpenting dalam ekstraksi unsur Titanium. Secara komposisi ilmenit terdiri atas 36,80% Fe, 31,57% Ti, dan 31, 63 % O[1].Di Indonesia, mineral ilmenit banyak terdapat dalam hasil produk samping penambangan timah di Pulau Bangka dengan kandungan ilmenit 86%. Ilmenit dapat diproses langsung untuk membuat Titanium Dioksida (TiO2) untuk keperluan penggunaan yang lebih beraneka ragam. Penggunaan TiO2 sintetis baik dalam bentuk tetragonal rutile ataupun anatase sangat banyak dipakai dalam industri antara lain sebagai pigment pemutih dan bahan utama keramik untuk elektronik (BaTiO3). Selain itu, TiO2 sintetis berguna sebagai bahan baku untuk pembuatan TiO2polimeric precursor yang sangat penting untuk bahan keramik maju, antara lain pelapisan optik (film-optic), bahan electro-optik dan bahan komposit polimer keramik (Ceramer). Pada percobaan ini, metode pengolahan Ilmenit menjadi TiO2 yang digunakan adalah fusi kaustik yang mencakup 4 tahap utama yaitu tahap fusi kaustik, water washing, pelindian asam, serta kristalisasi. Parameter fusi kaustik yang digunakan pada percobaan ini adalah rasio molar TiO2 : NaOH = 1 : 6, temperatur fusi kaustik 450°C, waktu fusi selama 2 jam. Selanjutnya, dari 3 kondisi percobaan dibedakan berdasarkan variasi dari konsentrasi H2SO4 yang dipakai saat pelindian asam. Sampel yang dihasilkan akan dianalisis kualitatif dan kuantitatif (SEM/EDX, XRD). Berdasarkan percobaan yang telah dilakukan, nilai perolehan dari tiap sampel yang didapat dipengaruhi oleh tingkat keasaman kondisi pelindian. Komposisi TiO2 maksimal yang didapat adalah 84,38%. Berdasarkan analisis sampel pada ilmenit awal terdapat FeTiO3, TiO2, dan SnO2. Pada sampel akhir proses yang terbentuk adalah TiO2, N, Na2O, SO3, dan FeO.Percobaan terbaik yang didapat adalah pada saat pelindian dengan konsentrasi H2SO4 9 M dengan perolehan sebanyak 21,88% dari konsentrat awal.

Deskripsi Alternatif :

Ilmenit with the chemical formula FeTiO3 is one of the potential mineral mines in Indonesia. Ilmenit is one of the most important elements in the extraction of Titanium. Composition of ilmenit consists of 36.8% Fe, 31.6% Ti, and 31, 6% O [1]. In Indonesia, mineral ilmenit found in the results by products of tin mining in Bangka Island with the content of ilmenit is 86%. Ilmenit can be processed directly to make a Titanium Dioxide (TiO2) for the use of a greater variety. The use of titanium in the form of synthetic TiO2 rutil or anatase tetragonal very widely used in industries such as whitening pigmentsand primary ingredient for electronic ceramics (BaTiO3). Furthermore, synthetic TiO2 useful as a raw material for the manufacture of TiO2 polimeric precursors which is very important for advanced ceramic materials, such as optical coatings (film-optic), electro-optic materials and polymer composite materials ceramic (Ceramer). In this experiment, from ilmenit to TiO2 processing methods used is caustic fusion that includes four main stages are caustic fusion, water washing, acid leaching, and crystallization. Caustic fusion parameters used in this experiment is the molar ratio TiO2: NaOH = 1: 6, temperatur caustic fusion 450°C, fusion time for 2 hours. Furthermore, the three experimental conditions distinguished by the variation of the concentration of H2SO4 used as acid leaching. The resulting sample will be analyzed qualitatively and quantitatively (SEM / EDX, XRD). Based on experiments that was carried out, recovery of each sample was obtained is influenced by the acidity of leaching conditions. The maximum TiO2 composition obtained is 84.38%.Based on the analysis of ilmenite samplethere are some minerals such as FeTiO3, TiO2, and SnO2.The composition of calcinations process contain TiO2, N, Na2O, SO3, and FeO. The best experiment is obtained which leaching concentration of H2SO4 9 M with the recovery 21.88%.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing :Prof. Dr. Ir.Syoni Soepriyanto, M.Sc., Editor: PKL-SMK

File PDF...