KINERJA MODULUS RESILIEN DAN DEFORMASI PLASTIS CAMPURAN LASTON LAPIS PENGIKAT (AC-BC) MENGGUNAKAN MATERIAL HASIL DAUR ULANG (RAP) DAN ASPAL MODIFIKASI ELVALOY

MODULUS RESILIENT AND DEFORMATION PERFORMANCE OF ASPHALTIC CONCRETE – BINDER COURSE (AC-BC) USE OF RECYCLED MATERIAL AND ASPHALT MODIFIED ELFALOY

Master Theses from JBPTITBPP / 2017-09-27 15:29:58
Oleh : RAHMI ZURNI (NIM : 269 10 302), S2 - Transportation
Dibuat : 2013, dengan 8 file

Keyword : Lapis Pengikat (AC-BC), RAP, Aspal Modifikasi Elvaloy, Modulus Resilien, Deformasi Permanen.

Dengan semakin terbatasnya material alam, sehingga harga material tersebut semakin mahal, maka teknologi daur ulang merupakan teknologi alternatif dalam pembangunan dan rehabilitasi perkerasan jalan. Penelitian ini bertujuan untuk menggunakan kembali material perkerasan daur ulang (Reclaimed Asphalt Pavement) dalam campuran lapis pengikat (AC-BC) dengan menggunakan aspal Pen 60/70 dan aspal polimer Elvaloy.


Persentase dari Reclaimed Asphalt Pavement (RAP) dibatasi sebesar 7,5% dan 10%, dengan alasan persentase RAP tersebut jika dicampurkan baik dengan aspal Pen 60/70 ataupun aspal modifikasi, campuran tersebut masih masuk kedalam nilai penetrasi 50. Sedangkan aspal modifikasi yang dipakai adalah 50% aspal Shell Pen 60/70 dan 50% aspal berpolimer Elvaloy (terhadap berat). Pengujian laboratorium yang dilakukan adalah percobaan Marshall, Marshall Immersion, Modulus Resilien UMATTA dan Wheel Tracking test.


Hasil yang diperoleh dari percobaan UMATTA adalah Modulus Resilien tertinggi pada temperatur 25oC dan 35oC diperoleh campuran A1 (aspal modifikasi Elvaloy dan 7,5% RAP), hal ini didukung dengan hasil Marshall yang memperlihatkan optimum RAP dalam penelitian ini adalah 7,5%. Rasio Modulus Resilien antara percobaan dan perhitungan menggunakan metoda Shell dan Nottingham relatif kecil yaitu 1,23 dan 0,94, yang menandakan kedua metode tersebut dapat memberikan pendekatan yang baik untuk memprediksi Modulus Resilien campuran (Smix).


Secara umum, campuran A1 (7,5% RAP dan aspal modifikasi Elvaloy) memberikan hasil terbaik dibandingkan dengan campuran lainnya (campuran A2, B1 dan B2), karena A1 memiliki nilai Modulus Tertinggi (3593 MPa) dan tertinggi pada nilai Stabilitas Dinamis yang dihasilkan dari uji Wheel Tracking (5250 T/mm).

Deskripsi Alternatif :

Due to the limitation of natural agregate for asphalt pavement, the technology using recycled materials is one alternative to solve the problem. The objective of this research is to use the Recycled Asphalt Pavement (RAP) materials in AC-BC (Asphalt Concrete Binder Course) mixes, blending with asphalt Pen 60/70 and modified binder Elvaloy. The percentage of RAP materials is limited at 7,5% and 10%, considering the penetration value of blending result of those materials with aspal pen 60/70 and modified binder “limited” was about 50. For the same reason, the blend between modified binder “Elvaloy” and asphalt pen 60/70 was determined at 50% to 50% (by weight). The Laboratory testings conducted in this research were an Marshall test, Marshall Immersion, Resilient Modulus UMATTA and Wheel Tracking test. The result of UMATTA test give the highest Resilien Modulus for A1 mix, at two temperatur (25oC and 35oC). Those results were confirmed by the value of Marshall Stability. The result Modulus ratio between UMATTA test and the formula proposed by Shell and Nottingham, gave the small value, i.e. 1,23 and 0,94 respectively. This ratio indicates that the two methods could predict the Resilient Modulus of Asphalt Mix with a good accuracy. In general, the A1 mix (7,5% RAP and modified binder Elvaloy) gave the best result comparing with the other mixes (A2, B1 and B2 mixes), because the A1 mix has the highest Resilient Modulus (3593 MPa) and highest Dynamic Stability resulting from Wheel Tracking test (5250 T/mm)

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing :


    Prof. Dr. Ir. Bambang Sugeng S, DEA;


    Dr. Ir. Harmein Rahman, MT, Editor: PKL-SMK

File PDF...