PEMBUATAN POLYDIMETHYLSILOXANE NANOEMULSION

Undergraduate Theses from JBPTITBPP / 2017-09-27 11:39:34
Oleh : PUTRI RAMADHANI (NIM 13003079); Pembimbing : Dr. Ir. Irwan Noezar, M.Sc. dan Dr. Ir. Subagjo, S1 - Department of Chemical Engineering
Dibuat : 2007, dengan 7 file

Keyword : Polydimethylsiloxane, Polimerisasi emulsi, Emulsi nano

Polydimethylsiloxane (PDMS) adalah polimer organik berbasis silikon yang paling banyak digunakan di dunia. Bentuk fisik dari PDMS yang umum diproduksi, selain berupa cairan, adalah emulsi. Penggunaan emulsi PDMS sangat beragam, mulai dari agen defoaming sampai bahan baku industri tekstil. Dalam penggunaannya, ukuran droplet emulsi PDMS sangat menunjang performa produk PDMS. Ukuran droplet emulsi PDMS yang semakin kecil dapat meningkatkan performa produk PDMS. Keberhasilan beberapa penelitian mendapatkan emulsi polimer PDMS berukuran mikro, mendorong penelitian selanjutnya untuk mendapatkan emulsi polimer PDMS berukuran nano.








Penelitian ini bertujuan untuk mengetahui pengaruh penambahan kosurfaktan trietanolamin (TEA) dalam pembentukkan emulsi polimer PDMS berukuran nano. Indikasi emulsi polimer berukuran nano dapat dilihat dari transparansinya. Kontribusi dari penelitian ini adalah mendapatkan emulsi polimer PDMS berukuran nano. Penelitian dilakukan dengan polimerisasi emulsi D4 (octamethylcyclotetrasiloxane) dengan KOH (kalium hidroksida) sebagai inisiator. Surfaktan yang digunakan adalah polioxyethylene nonylphenol ether (NP=40), polyoxyethylene (EO=15) lauryl ether (AEO-15), polyoxyetylene (EO=25) stearyl ether (PPJ-O). Fasa kontinu yang digunakan adalah air dengan penambahan TAE (trietanolamin) dan AE (aminoetanol). Variasi yang dilakukan adalah variasi konsentrasi kosurfaktan TEA.




Penambahan kosurfaktan TEA dapat meningkatkan nilai konversi monomer D4 dan meningkatkan transparansi emulsi polimer PDMS. Pada [TEA] = 78,4 gr/L dan [TEA] = 195,12 gr/L, nilai konversi yang didapat sebesar 73,09% dan 84,24%. Selain itu, penambahan kosurfaktan [TEA] = 78,4 gr/L memberikan nilai transparansi emulsi polimer PDMS sebesar 13,21% dan 20,89%, sedangkan penambahan kosurfaktan [TEA] = 195,12 gr/L memberikan nilai transparansi emulsi polimer PDMS sebesar 70,79% dan 88,61%. Pada [AE] = 195,12 gr/L, nilai konversi dan transparansi yang didapat adalah 31,40% dan 9,87%.

Deskripsi Alternatif :

Polydimethylsiloxane (PDMS) is the world's most common silicon based organic polymer. Physical structure of PDMS that generally produced, beside fluid, is emulsion. Its applications range from anti-foam agents to textile enhancing. For all of its applications, droplets size are directly associated to the performance of PDMS product. The decrease of average size of PDMS emulsions will increase the performance of PDMS product. The succeed of getting PDMS micro emulsion in some research leads to another research to get PDMS nano emulsions.




An aim of this research is to get the effect of cosurfactant aminoethanol (TEA) to production of PDMS nano emulsion. Contribution of this research is to get PDMS nano emulsion. This research is done by emulsion polymerization of D4 (octamethylcyclotetrasiloxane) or D5 (decamethylcyclopentasiloxane) with KOH (potassium hydroxide) as an initiator. The used surfactant are polioxyethylene nonylphenol ether (NP=40), polyoxyethylene (EO=15) lauryl ether (AEO-15), polyoxyetylene (EO=25) stearyl ether (PPJ-O).The continues phase is water with addition of triethanolamine (TEA) and aminoethanol (AE). A variation of the research is concentrations of TEA.




Addition of cosurfactant TEA can increase the conversions of monomer D4 and also increase the transparency of PDMS polymer emulsion. At [TEA] = 78,4 gr/L and [TEA] = 195,12 gr/L, the conversion value can reach to 73,09% and 84,24%. Afterall, addition of [TEA] = 78,4 gr/L gives transparency values to 13,21% and 20,89%, meanwhile addition of [TEA] = 195,12 gr/L gives transparency values to 70,79% and 88,61%. At [AE] = 195,12 gr/L gives conversion and transparency values to 31,40% and 9,87%.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Dr. Ir. Irwan Noezar, M.Sc. dan Dr. Ir. Subagjo, Editor: Rizki Apriyanti

File PDF...