KARAKTERTISASI KEREKATAN DAN KETAHANAN TEKUK LAPISAN Zn PADA BAJA GALVANIS

CHARACTERIZATION OF ADHESIVENESS AND BENDING ENDURANCE OF Zn COATING IN GALVANIZED STEEL

Undergraduate Theses from JBPTITBPP / 2017-09-27 10:37:14
Oleh : PRASASTI YUDAPRAWIRA (NIM : 12506002), S1 - Metallurgy
Dibuat : 2011, dengan 7 file

Keyword : hot-dip galvanizing, kemamputekukan, non-oxidizing furnace, lapisan intermetalik.

Pelapisan baja dengan menggunakan Zn sebagai pelapisnya adalah salah satu cara untuk meningkatkan ketahanan baja terhadap korosi sehingga meningkatkan umur pakainya. Pada proses hot-dip galvanizing, teknik pelapisan ada yang menggunakan Non-Oxidizing Furnace (NOF), jadi tidak lagi memerlukan cleaning dan pre-flux sebelum proses galvanizing. Pada NOF, baja dipanaskan agar tidak terjadi thermal shock pada baja ketika dicelup ke dalam bak lelehan Zn. NOF yang saat ini digunakan oleh PT. Fumira, NOF menghembuskan % volume H2 sebesar 40%. Perusahaan mencoba menurunkan % volume H2 hingga 20%. Perubahan parameter operasi ini dikhawatirkan menimbulkan pengaruh negatif terhadap sifat-sifat mekaniknya, terutama pada kerekatan dan ketahanan tekuk lapisan Zn karena penggunaan baja galvanis PT. Fumira ini pada aplikasi deep drawing. Sampel yang diterima adalah sampel dari potongan coil yang telah dilapisi Zn dari PT. Fumira sebagai sampel as received. Sampel diprepasi untuk dilakukan pengujian tekuk. Pengujian tekuk dilakukan dengan cara menekuk spesimen hingga 180°. Jika tidak terdapat retak pada permukaan baja yang ditekuk tanpa sisipan, maka baja galvanis termasuk kualitas 0T. Namun, jika baja galvanis mengalami retakan, maka perlu dilakukan pengujian lagi dengan menyisipkan satu buah spesimen dengan ketebalan yang sama ketika baja galvanis ditekuk. Apabila tidak terjadi retak maka disebut kualitas 1T. Pengujian dilakukan hingga baja galvanis tidak mengalami retak sampai dengan n-pengujian dengan kualitas n-T. Setelah itu, bagian yang ditekuk, diamati dengan menggunakan mikroskop optik untuk dilihat ada tidaknya retak. Pengamatan lebih lanjut dilakukan dengan menggunakan SEM dan daerah retakan dianalisis komposisi kimianya dengan menggunakan EDX. Pada hasil pengujian, spesimen yang diuji tidak mengalami retak berdasarkan pengamatan visual tanpa alat bantu perbesaran. Kualitas dari semua spesimen yang diuji adalah 0T. Namun, pada pengamatan dengan menggunakan mikroskop optik, ditemukan retakan pada permukaan spesimen yang ditekuk. Retakan yang terdapat pada spesimen memiliki ukuran yang beragam, hingga ukuran 60 μm. Setelah diteliti lebih lanjut dengan menggunakan SEM dan EDX, retakan pada spesimen yang diamati ternyata memiliki kandungan FeO sebesar 99,65%. Ini menunjukkan tidak adanya lagi lapisan Zn yang menutupi baja. Berdasarkan penelitian ini, kondisi terbaik dari penelitian ini adalah spesimen yang memiliki retak yang paling kecil yaitu spesimen H20-BL. Namun, perlu dilakukan penelitian lebih lanjut mengenai keberadaan oksida dan mengetahui karakteristik dari ketebalan tiap-tiap lapisan intermetalik, karena pada pengurangan % volume H2 hingga 20%, spesimen memiliki ketebalan yang lebih tinggi dan kekerasan yang lebih tinggi.

Deskripsi Alternatif :

Coating of steel using Zn as the coat is a way to increase the resistance of steel against corrosion thus increasing the life time of the steel. In hot-dip galvanizing process, one of the coating techniques process is done by using a non-oxidizing furnace (NOF), so it is no longer required pre-cleaning and fluxing before the galvanizing process. In NOF, the steel is heated to avoid thermal shock to the steel when it dipped into bath of molten zinc. NOF that is being used by PT. Fumira injects H2 with a volume of 40%. The company try to reduce this volume until 20%. There is a concenr that the change of this parameter can cause negatif effect to the mechanical properties of steel, especially the adhesiveness and bending endurance of Zn coat in deep drawing application. Specimen that is being used in this research is a specimen from a coil that has been coated by Zn from PT. Fumira as as received specimen. It is then prepared to for bending test. The test is conducted by bending the specimen to 180°. If there are no cracks on the surface of the bent steel, then the galvanized steel is labelled as 0T quality. However, if the surface of the bent steel has a crack, it is necessary to test the spesimen again by inserting a single specimen with the same thickness between the specimen when the bending is conducted. If there is crack on the surface of the bent steel, then it is labelled 1T quality. The test is done until the galvanized steel is not cracking on the n-test with n-T quality. After that, the bent steel observed using an optical microscope to see whether there are cracks. Further observation is made by using SEM and the chemical composition were analized by using EDX.



In this bending test, the specimens tested did not experience cracking based on visual observation without any magnifying visual aids. The quality of all specimens tested were 0T. However, in the observation using an optical microscope, crack was discovered on the surface of bent specimen. Crack found in the specimens have various sizes, up to 60 μm. After further investigation by using SEM and EDX, the observed crack on the specimen has 99,65% FeO. This is showing the absence of Zn layer covering the steel. Based on this research, the best condition of the study were the specimen that have the smallest crack is the H20-BL specimen. However, further research needs to be done to find out the existence of the oxide and the characteristic of the oxide thickness of each intermetalic layer, due to reduction of % volume of H2 to 20% the specimens have a higher value of thickness and higher value of hardness.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Prof. Dr. Ir. Syoni Soepriyanto, M.Sc., Editor: Alice Diniarti

File PDF...