STUDI PENGARUH WAKTU DAN PENGGUNAAN BIOFILM Psudomonas putida strain SKCH 7 PADA KOROSI MIKROBIOLOGI AKIBAT KONSORSIUM Alicyclobacillus ferrooxidans DAN Aspergillus sp. DAN Comamonas testosteroni PADA API 5L X52

Undergraduate Theses from JBPTITBPP / 2017-10-09 10:32:49
Oleh : PATUAN D P BATUBARA (NIM : 13707029); Tim Pembimbing : Dr.Ir.Bambang Widyanto; Siti Khodijah Chaerun, Ph.D, S1 - Material Engineering Study Programme
Dibuat : 2011, dengan 7 file

Keyword : Microbiological Influenced Corrosion, Alicyclobacillus ferrooxidans, Aspergillus sp., Comamonas testosteroni, Pseudomonas putida strain SKCSH 7.

Penelitian ini ditujukan untuk beberapa hal menyangkut Microbiological Influenced Corrosion (MIC). Masalah yang dibahas pada penelitian kali ini salah satunya adalah kerusakan korosi yang diakibatkan oleh konsorsium Alicyclobacillus ferrooxidans dan Aspergillus sp. dan bakteri Comamonas testeroni. Pada penelitian ini dibahas pula pengaruh waktu pengeksposan dan penggunaan biofilm yang dibentuk oleh bakteri Pseudomonas putida strain SKCSH 7 terhadap pengurangan berat spesimen dan kerusakan yang terjadi. Selain itu, dilakukan konfirmasi genus jamur yang berkonsorsium dengan Alicyclobacillus ferrooxidans serta perannya dalam korosi yang terjadi.




Pada penelitian kali ini digunakan 8 spesimen yang memiliki parameter jenis bakteri, waktu dan penggunaan biofilm. Kemudian dalam menganalisis dilakukan melalui karakterisasi produk korosi menggunakan Scanning Electron Microscopy




(SEM) dan Energy Dispersive X-Ray Spectroscopy (EDX) dan metode Analisis Anorganik Kualitatif serta X-Ray Diffraction (XRD), penghitungan pengurangan berat serta analisis morfologi kerusakan pada permukaan spesimen menggunakan Scanning Electron Microscopy (SEM). Dari hasil pengujian yang telah dianalisis didapatkan bahwa mekanisme kerusakan korosi yang diakibatkan oleh Alicyclobacillus ferrooxidans dan Aspergillus sp. dan bakteri Comamonas testosteroni adalah pitting diperlihatkan oleh morfologi penampang permukaan dan melintang spesimen. Selain itu, waktu pengeksposan yang lama dengan tidak menggunakan biofilm bakteri Pseudomonas putida strain SKCSH 7 mengakibatkan pengurangan berat yang besar dibandingkan yang lainnya.




Hal ini diperlihatkan spesimen pada medium Alicyclobacillus ferrooxidans yang tidak menggunakan biofilm dengan lama pengeksposan 3 minggu mengalami pengurangan terbesar yaitu 2.767 mg/cm2. Sedangkan pengurangan terkecil diperlihatkan pada spesimen yang diekspos pada medium Comamonas testosteroni yang menggunakan biofilm dengan lama pengeksposan 1 minggu mengalami pengurangan terkecil yaitu




0.467 mg/cm2.

Deskripsi Alternatif :

This study aimed to several things including the Microbiological Influenced Corrosion (MIC). The problems discussed in this research one of which is corrosion




damage caused by a consortium of Alicyclobacillus ferrooxidans and Aspergillus sp. and bacteria Comamonas testeroni. In this study also discussed the influence of




exposure time and the use of biofilms formed by Pseudomonas putida strain SKCSH 7 to weight loss of specimens and the damage. In addition, be confirmed fungal genus in which consortium with Alicyclobacillus ferrooxidans and its role in the corrosion.




In this research used 8 specimens that have parameter types of bacteria, the time and use of biofilm. Later in the analysis is done through the characterization of corrosion products using Scanning Electron Microscopy (SEM) and Energy dispersive X-Ray Spectroscopy (EDX) and method of Inorganic Qualitative Analysis and X-Ray Diffraction (XRD), calculation of weight loss and analysis of morphological damage to the specimen surface using Scanning Electron Microscopy (SEM). From this test has been analyzed it was found that the mechanism of corrosion damage caused by Alicyclobacillus ferrooxidans and Aspergillus sp. and bacteria Comamonas testosteroni is shown by pitting the surface morphology and crosssectional specimens. In addition, a long exposure time by not using a biofilm of




Pseudomonas putida strain SKCSH 7 resulted in a greater weight loss than others.




This is shown in the medium Alicyclobacillus ferrooxidans specimens that do not use a long exposure biofilms with 3 weeks of experiencing the greatest reduction of 2.767 mg/cm2. While the smallest reduction is shown in specimens exposed to the medium Comamonas testosteroni using biofilms with long exposure 1 week experienced the smallest reduction of 0.467 mg/cm2.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Tim Pembimbing : Dr.Ir.Bambang Widyanto; Siti Khodijah Chaerun, Ph.D, Editor: Alice Diniarti

File PDF...