PELAPISAN NANOPARTIKEL CuO-SnO2 PADA ALUMUNIUM MENGGUNAKAN METODE LAPIS CELUP TERMODIFIKASI SEBAGAI LAPISAN TAHAN AUS

CuO-SnO2 NANOPARTICLE COATING ON ALUMUNIUM USING MODIFIED DIP COATING METHOD AS WEAR RESISTANT COATING

Undergraduate Theses from JBPTITBPP / 2017-09-27 11:05:15
Oleh : NUR MUHAMMAD AZIS (NIM : 13309022), S1 - Department of Engineering Physics
Dibuat : 2015, dengan 7 file

Keyword : CuO, SnO2, thin film, keausan, dip coating modifikasi.

Keausan pada komponen mesin menjadi masalah yang diperhatikan oleh banyak kalangan mengingat dampaknya yang buruk secara ekonomi apabila tidak ditangani dengan baik, yaitu peningkatan konsumsi bahan bakar dan penambahan biaya operasional mesin untuk penggantian komponen mesin. Penggunaan oli menjadi solusi yang umumnya digunakan karena oli dapat memisahkan permukaan antar dua komponen mesin secara sempurna sehingga keausan dapat dihindarkan. Akan tetapi oli tidak dapat digunakan pada beberapa keadaan tertentu, seperti temperatur ekstrim, lingkungan korosif, dan radiasi nuklir. Salah satu solusi yang dapat ditawarkan adalah penggunaan wear resistant coating.






Pada penelitian ini, material coating dibuat dari nanopartikel CuO dan SnO2 sebagai material penyusun wear resistant coating karena kedua material ini memiliki performa wear resistant yang baik serta memiliki stabilitas suhu yang baik. Kedua material ini akan digunakan dalam bentuk thin film yang dilapiskan pada suatu substrat logam dengan menggunakan metode dip coating yang dimodifikasi dengan menggunakan surfaktan. Kedua nanopartikel ini disintesis menggunakan metode sol gel dengan cara melarutkan garam logam ke dalam air lalu menambahkan basa hingga mencapai pH dimana terdapat kesetimbangan antara endapan dan larutan. Adapun surfaktan yang digunakan adalah larutan kitosan 1%. Kedua larutan nanopartikel ini kemudian dicampur dalam variasi rasio mol CuO dan SnO2 yang berbeda-beda, yaitu 3:1, 1:1, dan 1:3.






Berdasarkan hasil foto SEM dapat diketahui bahwa rasio mol memiliki efek terhadap hasil pelapisan thin film pada kedua material. Semakin banyak kandungan CuO pada larutan coating, pelapisan yang dihasilkan semakin baik.

Deskripsi Alternatif :

Wear on the engine components has become a problem noted by many people due to its economical impact if not handled properly, such as the increase in fuel consumption and operational costs for the replacement of engine components. Usage of oil becomes a solution that is commonly used because oil can perfectly separate between two surfaces of engine components in contact so that the wear can be avoided. However, oil can not be used under certain conditions, such as extreme temperatures, corrosive environment, and nuclear radiation. One of the solutions that can be offered for this problem is the use of wear resistant coatings.






In this study, the coating material is made of CuO and SnO2 nanoparticles because the materials have good wear resistant performance and good temperature stability. Both of these materials will be used in the form of thin film coated on a metal substrate by dip coating method modified using a surfactant. Both of these nanoparticles were synthesized using sol-gel method by dissolving the metal salt in the water and then adding a base to achieve a pH where there is an equilibrium between deposition and solution. The surfactant used is 1% chitosan solution. Both nanoparticle solution is then mixed in a mole ratio of CuO variations and different SnO2, which is 3: 1, 1: 1, and 1: 3.






Based on the SEM images, it can be seen that the mole ratio has an effect on the results of the second thin film coating material. The more the content of CuO in the coating solution, the coating characteristics become better.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Prof. Dr. Ir. Bambang Sunendar, M.Eng. ; Dr. Ir. Ahmad Nuruddin, M.Sc. Ph.D., Editor: Alice Diniarti

File PDF...