SINTESIS ZEOLITE FAUJASITE DAN OKSIDA BESI SEBAGAI KATALIS UNTUK MENINGKATKAN KUALITAS MINYAK BERAT

SYNTHESIS OF FAUJASITE ZEOLITE AND IRON OXIDE AS A CATALYST FOR UPGRADING HEAVY OIL

Master Theses from JBPTITBPP / 2018-08-10 15:03:43
Oleh : NUR AFIFAH ZEN (NIM: 20216046), S2 - Physics-FMIPA
Dibuat : 2018-06-28, dengan 8 file

Keyword : minyak berat, zeolite faujasite, oksida besi, aquathermolysis.

Katalis zeolite faujasite dan oksida besi untuk meningkatkan kualitas minyak berat melalui reaksi aquathermolysis telah berhasil disintesis. Zeolite faujasite disintesis menggunakan bantuan gelombang mikro dan ultrasonik dengan variasi waktu aging 0, 3, 5, 7, 14 dan 28 hari. Sintesis oksida besi dilakukan menggunakan metode co-precipitation pada temperatur 27 °C. Hasil karakterisasi menggunakan X-Ray Diffraction (XRD) menunjukan bahwa kristalisasi zeolite terjadi setelah waktu aging 5 hari dan akan mencapai kristalinitas yang seragam saat 7, 14 dan 28 hari. Ikatan kimia yang terdapat pada zeolite faujasite dikarakterisasi menggunakan Fourier Transform Infra-Red (FTIR). Hasil FTIR zeolite faujasite menunjukan jika waktu aging berpengaruh terhadap ikatan Si-O, Al-O, Al-O-Si dan Si-OH. Hasil Scanning Electron

Microscopy (SEM) menunjukkan bahwa waktu aging berpengaruh terhadap struktur kristal dan ukuran partikel zeolite. Sampel zeolite dengan waktu aging 7 hari memiliki ukuran partikel rata-rata terkecil sebesar 37,7 nm. Hasil ukuran partikel rata-rata tersebut berbanding terbalik dengan hasil karakterisasi Brunauer-Emmet-Teller (BET) yang menunjukan bahwa sampel zeolite dengan waktu aging 7 hari (FAU-7) mempunyai luas permukaan spesifik paling besar yaitu 304 m2/g. Semakin kecil ukuran partikel akan menyebabkan luas permukaan katalis semakin besar. Pengujian katalitik melalui reaksi aquathermolysis menunjukan bahwa katalis efisiensi terbesar yaitu terdapat pada sampel zeolite dengan waktu aging 7 hari (FAU-7) sebesar 81,5%. Spektrum FTIR minyak berat mengindikasikan adanya pengaruh katalis pada pemutusan rantai utama hidrokarbon C-O, C-C dan C-S serta adanya peningkatan puncak transmitansi pada ikatan saturasi C-H dan aromatik C-H. Berdasarkan hasil tersebut, katalis zeolite maupun campuran katalis zeolite faujasite dan oksida besi efektif dalam meningkatkan kualitas minyak berat.

Deskripsi Alternatif :

Faujasite-type zeolite and iron oxide as a catalyst to upgrading heavy oil in an aquathermolysis reaction has been successfully synthesized. Faujasite-type zeolite was synthesized by microwave-assisted thermal reaction with different aging time, varied from 0, 3, 5, 7, 21 and 28 days. The iron oxide synthesized by co-precipitation method at 27 °C. The X-ray Diffraction (XRD) caharcterization shows that faujasite-type zeolite crystal grew after 5 day aging time and has the same crystallinity at 7, 14 and 28 days. The chemical bonds present in zeolite faujasite are characterized using Fourier Transform Infra-Red (FTIR). FTIR zeolite faujasite results show that aging time affects Si-O, Al-O, Al-O-Si and Si-OH bonds. Scanning Electron Microscopy (SEM) results show that aging time has an effect on crystal structure and zeolite particle size. Zeolite samples with 7 day aging time had the smallest average particle size of 37,7 nm. The Brunauer-Emmet-Teller (BET) characterization results show that zeolite samples with 7 days aging time have the largest specific surface area of 304 m2/g. The smaller the particle size will cause the larger surface area of the catalyst. Catalytic analyses using aquathermolysis process shows that the viscosity of the heavy oil decreased as much of 81,5%. The FTIR spectra indicates that zeolite with 7 days aging time as a catalyst

addition affected the C-O, C-C and C-S primary hydrocarbon chains cracking and increased the C-H saturation. Based on these results, faujasite-type zeolite and iron oxide can increase the quality of heavy oil.

Copyrights : Copyright (c) 2001 by Perpustakaan Digital ITB. Verbatim copying and distribution of this entire article is permitted by author in any medium, provided this notice is preserved.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS2 - Physics-FMIPA
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing I : Dr.Eng, Fery Iskandar,

    Pembimbing II : Dr. rer. nat. Akfiny Hasdi Aimon, Editor: Ratnasari

File PDF...