ANALISIS SIFAT TRANSPOR PROTON PADA MEMBRAN BLEND PSF-SPSF-TEOS MELALUI PENGUKURAN POTENSIAL MEMBRAN

ANALYSIS OF PROTON TRANSPORT PROPERTIES OF PSF-SPSF-TEOS BLEND MEMBRANE THROUGH POTENTIAL MEMBRANE MEASUREMENTS

Undergraduate Theses from JBPTITBPP / 2017-09-27 11:42:31
Oleh : NUNGKY APRILIA (NIM : 10508040); Pembimbing : Dr. Veinardi Suendo, S1 - Department of Chemistry
Dibuat : 2012, dengan 7 file

Keyword : PSF-SPSF-TEOS blend, PEMFC, tranpor proton, potensial membran

Salah satu sumber energi alternatif yang sedang berkembang pesat yaitu Polymer Electrolyte Membrane Fuel Cell (PEMFC). PEMFC merupakan sel bahan bakar yang menggunakan membran polimer bermuatan yang dapat mentranspor proton dari anoda ke katoda. Untuk menghasilkan energi, PEMFC memerlukan gas oksigen dari udara dan gas hidrogen sebagai bahan bakar untuk melangsungkan reaksi redoks dan menghasilkan air. Dalam penelitian ini, dilakukan pembuatan membran penghantar proton dari campuran antara polisulfon (PSF), polisulfon tersulfonasi (SPSF) dan tetraetoksisilan (TEOS). Membran ini diharapkan dapat menggantikan membran penghantar proton komersil, yaitu Nafion, yang harganya relatif mahal dan limbahnya cenderung tidak ramah lingkungan. Dalam penelitian ini, SPSF dibuat bervariasi dari 10 hingga 50 persen berat, dengan berat total yang konstan. Adanya gugus sulfonat dan silanol dalam membran polimer diharapkan dapat meningkatkan kemampuannya dalam mentranspor proton. Sulfonasi polisulfon dilakukan menggunakan senyawa asam klorosulfonat dalam kloroform sedangkan polimerisasi TEOS menggunakan asam metansulfonat sebagai katalis. Hasil pengukuran potensial membran menunjukkan, seiring meningkatnya persen SPSF, nilai muatan efektifnya juga meningkat, yang berarti semakin baik kemampuannya dalam mentranspor proton. Data ini juga didukung oleh hasil pengukuran konduktivitas proton yang juga cenderung mengalami peningkatan. Dilakukan juga karakterisasi pendukung seperti pengamatan struktur dan morfologi membran menggunakan Scanning Electron Microscope (SEM), spektrofotometri infrared (IR), dan spektroskopi Raman, serta pengamatan terhadap sifat fisika-kimia membran melalui pengukuran water uptake, sudut kontak, dan kapasitas penukar ion.

Deskripsi Alternatif :

One of the alternative energy sources being widely developed is Polymer Electrolyte Membrane Fuel Cell (PEMFC). PEMFC is a fuel cell that uses charged polymer membrane that transports proton from anode to cathode. To produce energy, PEMFC needs oxygen from air and hydrogen as fuel to perform redox reaction and produce water. In this research, proton conducting membrane was synthesized by blending polysulfone (PSF), sulfonated polysulfone (SPSF) and tetraethoxysilane (TEOS). This membrane is expected to replace the commercial proton conducting membrane, Nafion, which is expensive and its waste is not enviromentally friendly. Here, SPSF was varied from 10 to 50 weight percent, while the total weight is kept constant. The presence of sulfonate and silanol groups in the polymer membrane is expected to increase its ability in transporting proton. Polysulfone is sulfonated with chlorosulfonic acid in chloroform where TEOS is polymerized using methanesulfonic acid as catalyst. The results of membrane potential indicate that the increase of SPSF content also increases the effective charged which means that the ability to transport proton is increased. This result is supported by proton conductivity test that also tend to increase. Supporting characterizations were also conducted such as membrane structure and morphology using Scanning Electron Microscope (SEM), Infrared (IR) spectrophotometry, and Raman spectroscopy, where the physical-chemical properties of the membrane was observed using water uptake, contact angle and ion-exchange capacity measurements.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Dr. Veinardi Suendo, Editor: Alice Diniarti

File PDF...