PEMBUATAN SERAT KOMPOSIT PVP/CA YANG MENGANDUNG EKSTRAK DAUN SIRSAK (Annona muricata) DENGAN PEMINTAL ELEKTRIK UNTUK APLIKASI PENUTUP LUKA

ELECTROSPUN PVP/CA/EXTRACT OF SOURSOP’S LEAVES ( Annona muricata) COMPOSITE FIBERS FOR WOUND DRESSING APPLICATION

Master Theses from JBPTITBPP / 2017-09-27 14:41:05
Oleh : NENNI MONA ARUAN (NIM: 20214047), S2 - Physics
Dibuat : 2016, dengan 7 file

Keyword : Ekstrak daun sirsak, pemintal elektrik, PVP/CA.

Annona muricata L., sirsak dalam bahasa Indonesia, adalah tanaman famili Annonaceae yang telah terbukti mengandung zat kimia dan senyawa bioaktif yang dapat digunakan sebagai obat tradisional. Ekstrak daun sirsak (EDS) juga telah dikonfirmasi untuk memiliki aktivitas antibakteri terhadap bakteri gram negatif dan gram positif. Dalam penelitian ini, serat komposit diproduksi dari ekstrak daun sirsak dan cellulose acetate (CA) dicampur dengan polyvinylpirolidone (PVP) dan kemudian dipintal dengan metode pemintal elektrik (electrospinning). Serat hasil pemintalan elektrik telah banyak diaplikasikan dalam berbagai bidang. Salah satu terapan dalam bidang biomedis sebagai penutup luka. Penutup luka dengan morfologi serat dan mengandung antibakteri sangat penting terkait perlindungan sepenuhnya dari bakteri dan kemampuan mensintesis protein yang lebih baik pada proses penyembuhan luka. Serat komposit PVP/CA/EDS disintesis dari PVP/CA dengan perbandingan berat 6/4 dan penambahan EDS dengan variasi perbandingan 20:1, 20:2 dan 20:3 (b/b). Hasil penelitian yang didapat adalah: (a) berhasil memproduksi serat komposit PVP/CA/EDS menggunakan metode pemintalan elektrik dengan rata-rata ukuran diameter 289-527 nm, (b) nanoserat memiliki derajat pengembangan, pH permukaan dan Modulus Young serat yang memenuhi syarat sebagai penutup luka, (c) secara in-vitro dapat menghambat pertumbuhan bakteri S. aureus dan S. epidermidis. Parameter proses untuk larutan PVP/CA/EDS dipintal dengan tegangan 8 kV, laju alir 0,2 mL/jam dan jarak antara jarum dan kolektor 12 cm. Pemintalan dengan parameter tersebut menghasilkan serat tanpa manik-manik dan distribusi ukuran diameter serat yang homogen.

Deskripsi Alternatif :

Annona muricata L., known as soursop, is a plant in family of Annonaceae which have been proven to contain chemical and bioactive compounds that can be used as traditional medicine. Extract of Annona muricata leaves (EAML) has also been confirmed to have antibacterial activity against gram-negative and gram-positive bacteria. In this study, composite fibers were produced from cellulose acetate (CA) and polyvinylpirolidone (PVP) as a polymeric matrix and incorporated by EAML through electrospinning process. Electrospinning is one of the techniques used in producing fibers up to nano size and is applicable to produce wound dressing mats. Wound dressing with fiber morphology with some antibacterial agent inside was very important concerning protection from bacteria and the ability to synthesize protein in the wound healing process. Composite fibers of PVP/CA/EAML synthesised from PVP/CA polymer blended in 6/4 ratio and added EAML with ratio of 20:1, 20:2 and 20:3 (w/w). This study showed that we: (a) successfully produced electrospun of PVP/CA/EAML composite fibers with average fiber diameter of 289-527 nm, (b) electrospun of PVP/CA/EAML have a swelling degree, pH and Young’s modulus as eligible as wound dressing, (c) showed an in-vitro antibacterial activity toward S. aureus and S. epidermidis. The process parameters for executing the electrospinning process were voltage of 8 kV, flow rate of 0.2 mL/h and distance between collector to injection of 12 cm.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Prof. Dr.Eng. Khairurrijal, Editor: Ratnasari

File PDF...