KONVERSI ZEOLIT ALAM MENJADI ZSM-5

Master Theses from JBPTITBPP / 2017-09-27 14:51:58
Oleh : Mustain (NIM 23093017), S2 - Chemical Engineering
Dibuat : 1997-04-00, dengan 8 file

Keyword : konversi zeolit, ZSM-5
Subjek : Chemical Engineering
Kepala Subjek : Chemistry
Nomor Panggil (DDC) : T 549.68 MUS

ABSTRAK:


Zeolit merupakan kristal Aluminosilikat dengan struktur berbentuk kerangka dan mempunyai pori berukuran molekul. Penggunaan Zeolit di dunia industri balk sebagai penukar kation, adsorben maupun katalis semakin meningkat. Zeolit sintetik jauh lebih disukai dibandingkan dengan Zeolit Alam, disamping karena keaktifan, dan kesetektivannya yang lebih baik juga kestabilannya. Kinerja ini tenrtama ditentukan oleh kemurnian, struktur kristal, dan komposisi kimia dari Zeolit tersebut.


Z8M-5 (Zeolite Socony Mobil -5) adalah salah sate jenis Zeolit sintetik yang banyak digakan oleh industri. Zeolit ini berstruktur kerangka tiga dimensi, memiliki aktivitas dan selektivitas yang tinggi untuk beberapa reaksi, selektif terhaciap bentuk molekul Berta tidak mudah terdeaktivasi.


Indonesia memiliki cadangan Zeolit Alam yang tidak sedikit dengan kemurnian yang cukup tinggi (55-85%) bahkan lebih tinggi dari Zeolit Alam terbaik di Jepang (55-77%). Zeolit Alam asal Malang berkemurnian tertinggi sehingga memiliki prospek yang balk untuk dikonversikan menjadi Zeolit sintetik seperti ZSM-5.


Penelitian ini merupakan wujud dari dorongan untuk mempelajari konversi Zeolit Alam menjadi ZSM-5 (dengan cara penambahan senyawa Mika untuk menaikkan perbandingan SI/Al nya). Melalui penelitian ini dipelajari penganah dari berbagai: perbandingan Si/Al (20-60), TPA/SiO2 (0,0250; 0,0500; 0,0658; 0,0816), sumber Silika aditif (Waterglas, Aerosil, Calcined Silica) dan waktu reaksi (10, 24, 48 jam) terhadap kristalinitas produk ZSM-5.


Proses dilangsungkan di dalam Autoklaf pads suhu 175 derajat C, tekanan autogenous (10 bar) dan kecepatan putaran pengaduk 400 rpm. Komposisi dan struktur produk dianalisis dengan bantuan Spektrofotometer Serapan Atom (SSA) dan Difraktometer Sinar-X (XRD).


Dari hasil penelitian tersebut diperoleh bahwa untuk mencapai kristalinitas produk ZSM-5 tertinggi (94,20%) proses dilangsungkan pads Si/Al 31,95 dan TPA/S1O2 0,0816 selama waktu retail 24 jam. Janis senyawa Silika aditif yang terbaik untuk menaikkan angka perbandingan Si/Al adalah Calcined Silica.

Deskripsi Alternatif :

ABSTRACT:


Zeolite is an Aluminosilicate crystal with framework structure and molecular size pores. It has increased usage in industry, either as cation exchanger, absorber, or catalysts. The synthetic Zeolites more liked then natural one because they have better stability along with better activity and selectivity. This performance determined mainly by pureness, crystals structure, and chemical composition of Zeolites.


ZSM-5 (Zeolite Socony Moil-5) is a type of synthetic Zeolite that used in various industry processes. This Zeolite has three dimensional frame structures, has high selectivity and activity in various reactions, very selective to molecular shape and hard to dcactivated. Indonesia has abundance natural Zeolite with high enough pureness (55-85%), and even they have higher pureness then best Zeolite of Japan (55-77%). Natural Zeolites of Malang have highest pureness and, therefore, they have a good prospect to converted become synthetic one such as ZSM-5.


This research has performed as a realization of a desire to study conversion of natural Zeolite become ZSM-5 (by addition of Silica compounds to increase its Si/Al ratio). This research performed to study effect on Crystallite of ZSM-5 Product caused by various Si/Al ratio (20-60), TPAISiO2 (0.0250; 0.0500; 0.0658; 0.0816), source of silicate additive (Waterglas, Aerosil, Calcined Silica) and reaction time (10, 24, 48 hours).


The process performed within an autoclave at 1?5 degree C and autogenous (10 bar) pressure and driver speed of 400 rpm. Composition and structure of product analyzed with spectrophotometer of Atomic Absorbed (SSA) and x-ray defractometer MD).


This research indicates that highest crystallization of ZSM-5 product (94.20%) achieved from process that used Si/Al 31.95 and TPA/SiO2 0.0816 within 24 hours of reaction time. Type of the best additive silicate compound to increase Si/Al ratio is Calcined Silicate.

Copyrights : Copyright (c) 1997 FMIPA ITB, Information Dissemination Right @ 2008 ITB Central Library, Jl. Ganesha 10 Bandung, 40132, Indonesia. Verbatim copying and distribution of this entire article is permitted by author in any medium, provided this notice is preserved.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing: Subagjo, Dr., Ir.


    Scan: Arnaz Driyastika M.


    (2008-01-04), Editor: driyastika

Download...