PEMBUATAN SUPERALLOY DENGAN TINJAUAN PENGARUH PENAMBAHAN MOLIBDENUM TERHADAP KESTABILAN STRUKTUR MIKRO PADA TEMPERATUR 1000 oC

SUPERALLOY MAKING WITH REVIEW OF MOLYBDENUM ADDITION EFFECT ON MICROSTRUCTURE STABILITY AT TEMPERATURE OF 1000 0C

Undergraduate Theses from JBPTITBPP / 2017-09-27 10:37:15
Oleh : MUHAMMAD IQBAL GUMAY (NIM : 12506030), S1 - Metallurgy
Dibuat : 2010, dengan 9 file

Keyword : Superalloy, molbdenum

Penggunaan material pada temperatur tinggi membutuhkan perhatian khusus terhadap perubahan sifat mekanik dan ketahanan oksidasinya. Pada temperatur tinggi, material cenderung untuk kehilangan kemampuannya mempertahankan berbagai sifat dan keunggulannya sebagai akibat dari perubahan struktur mikro pada material. Untuk kepentingan aplikasi pada temperatur tinggi digunakanlah


paduan-paduan khusus yang dapat mempertahankan berbagai sifat dan keunggulannya diantaranya adalah superalloy khususnya yang berbasis nikel.


Penelitian ini dilakukan untuk mempelajari pengaruh penambahan molibdenum terhadap kestabilan struktur mikro dan ketahanan terhadap pelarutan pada paduan 75Ni-10Cr-15Al akibat oksidasi temperatur tinggi. Paduan divariasikan kandungan molibdenumnya menjadi 3 komposisi paduan, paduan1 (73,66Ni- 14,89Al-8,42Cr-3,02Mo); paduan 2 (72,65Ni-15,35Al-7,97Cr-4,04Mo); dan paduan 3 (73,51Ni-15,54Al-8,95Cr-2,01Mo), kemudian dilakukan proses ageing pada tekanan 1 atm pada temperatur 1000 0C dengan variasi waktu ageing 10, 100, 1.000, 10.000 menit dalam lingkungan oksidatif. Pengamatan dan pengukuran dilakukan terhadap ketebalan denuded zone yang terbentuk, kekerasan dan perubahan fraksi volum presipitat gamma prime dengan menggunakan mikroskop optik, Microhardness dan analisa Optimas 6.1. Beberapa hasil telah diperoleh dari pengamatan yakni peningkatan waktu ageing sebanding dengan meningkatnya ketebalan denuded zone dan menurunkan kekerasan paduan setelah terjadi over ageing, penambahan molibdenum menurunkan ketahanan paduan terhadap pelarutan presipitat dan kekerasan paduan.

Deskripsi Alternatif :

Use of materials at high temperatures requires special attention to changes in mechanical properties and oxidation resistance. At high temperatures, the material


tends to lose its ability to maintain the various properties and advantages as a result of changes in the microstructure of the material. For the purposes of the


application on high temperature, special alloy that can sustain a variety of properties and advantages are used such as nickel-based superalloys in particular.


This research was conducted to study the influence of molybdenum on the microstructure stability and resistance to dissolution of in the alloy 75Ni-10Cr-


15Al due to high temperature oxidation. Alloy is varied in molybdenum content into 3 alloy compositions, alloy 1 (73,66Ni-14,89Al-8,42Cr-3,02Mo), alloy 2 (72,65Ni- 15,35Al-7,97Cr-4,04Mo), alloy 3 (73,51Ni-15,54Al-8,95Cr-2,01Mo) and then made aging process at a pressure of 1 atm at a temperature of 1000 0C with aging time variation of 10, 100, 1000, 10.000 minutes in the oxidative environment. Observations and measurements made to the thickness of the denuded zone that formed, hardness and change in volume fraction of gamma prime precipitates by using optical microscop, Leco Microhardness and Optimas 6.1 analysis.


Some of the results is obtained from the observations such as the increase in aging time is proportional to the increase in thickness of denuded zone and reduce of


hardness after over ageing, the addition of molybdenum alloys lowered resistance to the dissolution of precipitate and hardness on alloy.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Dr. Ir. Eddy Agus Basuki, M.Sc; Ir. Djoko Hadiprayitno, MSME., Editor: PKL-SMK

File PDF...