ANALISIS UJI IMPACT PADA BATANG KOMPOSIT BERSERAT BAMBU

Undergraduate Theses from JBPTITBPP / 2017-10-09 10:33:27
Oleh : MUHAMAD YUNUS (NIM : 13605025); Pembimbing : Dr. Ir. Bambang Kismono Hadi, Ir. Muhammad Kusni, M.T., S1 - Department of Aerospace Engineering
Dibuat : 2009, dengan 7 file

Keyword : Komposit serat bambu, Uji impact

Penggunaan serat alami seperti serat bambu sebagai penguat pada material komposit meningkat luar biasa. Hal ini disebabkan sifat-sifatnya yang potensial seperti berat spesifik yang rendah sehingga menghasilkan kekuatan spesifik dan kekakuan yang lebih tinggi dari serat gelas. Hal ini tentu saja menjadi keuntungan terutama apabila serat tersebut dipakai untuk menjadi material yang memang didesain memiliki kekakuan lentur. Serat alami seperti bambu ini merupakan sumber daya alam yang dapat diperbarui, hanya membutuhkan sedikit energy dalam produksinya. Material dari serat bambu dapat diproduksi dengan biaya yang rendah, sehingga membuat material ini menjadi produk yang menarik untuk negara-negara dengan pendapatan rendah. Proses produksi yang relative aman, tidak membutuhkan peralatan yang rumit, dan tidak menimbulkan iritasi kulit dalam proses produksinya membuat material dari serat bambu ini menarik untuk dikembangkan. Tugas akhir ini merupakan studi mengenai pengujian impact komposit lamina. Pengujian impact ini dilakukan untuk mengetahui modus kegagalan yang terjadi pada spesimen komposit serta bambu dan bagaimana karakteristiknya. Hasil yang diperoleh setelah pengujian adalah energi maksimum yang mampu diserap sampai spesimen tersebut benar-benar hancur adalah 427.5 Joule baik untuk pelat maupun lidi. Sedangkan energi treshould yang bisa diserap sesaat sebelum spesimen hancur untuk pelat 62-65 Joule dan untuk lidi 162.5 Joule. Modus kegagalan yang terjadi pada spesimen komposit serat bambu lebih dominan adalah perambatan retak dengan arah ± 45 o.

Deskripsi Alternatif :

The use of natural fibers such as bamboo fibers as reinforcement in composite materials increased remarkable. This is due to characteristics such as potential low specific weight to produce specific strength and higher stiffness of glass fiber. This is of course an advantage, especially when fibers are used for a material that is designed to have bending rigidity. Natural fibers such as bamboo is a natural resource that can be updated, just need a little energy in its production. Material from bamboo fiber can be produced with low cost, thus making these materials into products of interest to countries with low income. The production process is relatively safe, does not require complex equipment, and does not cause skin irritation in the production process makes the material of bamboo fiber is attractive for development. This final task is the study of the impact testing of composite lamina. Impact test was performed to determine the failure mode that occurs in the composite specimens as well as bamboo and how its characteristics. The results obtained after the test is the maximum energy that could be absorbed until the specimen is completely destroyed is good to 427.5 Joule plates or sticks. While treshould energy can be absorbed just before the specimens were destroyed to the plate for 62-65 Joule and 162.5 Joule for lidi. Failure mode that occurs in the composite specimens of bamboo fiber is more dominan direction of crack propagation with ± 45 o.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Tim Pembimbing : Dr. Ir. Bambang Kismono Hadi, Ir. Muhammad Kusni, M.T., Editor: Alice Diniarti

File PDF...