SINTESIS DAN KARAKTERISASI POLIANILIN TERDOPING HCL MENGGUNAKAN METODE OKSIDASI LANGSUNG DENGAN VARIASI WAKTU PENGADUKAN PADA SUHU 0 DAN 25 oC

SYNTHESIS AND CHARACTERIZATION OF HCL DOPED POLYANILINE USING DIRECT OXIDATION METHOD WITH VARIOUS STIRING DURATION AT TEMPERATURE OF 0 AND 25 oC

Undergraduate Theses from JBPTITBPP / 2017-09-27 11:42:30
Oleh : MEGA AYU PRATIWI (NIM : 10508097);Pembimbing I : Dr. Veinardi Suendo; Pembimbing II : Dr. Achmad Rochliadi, S1 - Department of Chemistry
Dibuat : 2012, dengan 7 file

Keyword : Polianilin terdoping HCl, metode oksidasi langsung, pengaruh pengadukan, bidang hamburan {(110)}.

Polianilin merupakan salah satu polimer konduktif yang banyak dipakai sebagai material utama pada sel surya, sensor gas, dan baterai. Aplikasi-aplikasi tersebut membutuhkan polianilin yang memiliki nilai konduktivitas tinggi. Beberapa penelitian menunjukkan bahwa pengadukan selama sintesis polianilin akan mempengaruhi struktur dan konduktivitas polianilin yang dihasilkan. Pada penelitian ini dilakukan sintesis polianilin terdoping HCl dengan metode oksidasi langsung menggunakan ammonium peroxodisulfat (APS) pada suhu 0 dan 25OC. Total waktu sintesis adalah 48 jam dengan variasi waktu pengadukan selama 48, 36, 24, 12, 6, 3, dan 1 jam, serta tanpa pengadukan. Polianilin yang dihasilkan berupa serbuk yang berwarna hijau kehitaman. Polianilin kemudian dikarakterisasi dengan Spektroskopi Raman, FTIR, XRD, dan SEM. Citra SEM yang didapat menunjukan bahwa semakin lama waktu pengadukan, ukuran nanofiber polianilin yang terbentuk semakin besar dengan agregat yang semakin banyak. Hasil XRD menunjukan bahwa pengadukan memberikan pergeseran ke sudut yang lebih kecil untuk puncak dengan 2θ berkisar pada 25O yang berkorespondensi dengan bidang hamburan {(110)}. Hasil Raman juga menunjukan adanya pergeseran puncak ke arah bilangan gelombang yang lebih besar akibat pengaruh pengadukan. Spektrum absorpsi inframerah menunjukan adanya gugus quinoid dan benzoid pada 1557 cm-1 dan 1477 cm-1 serta gugus C-H aromatik pada 1302 cm-1. Dari hasil EIS diketahui bahwa semakin lama waktu pengadukan, maka dihasilkan polianilin dengan nilai konduktivitas yang semakin menurun dengan nilai konduktivitas antara 0,1213-0,024 S.cm-1.

Deskripsi Alternatif :

Polyaniline is one of conducting polymer which is widely used in industry as the starting material for solar cells, battery, and gas sensor. Those applications usually need polyaniline with high conductivity. Previous research found that stirring during synthesis highly affects the structure and the conductivity of polyaniline. In this research polyaniline is doped by HCl with direct oxidation method using ammonium peroxodisulfate (APS) as the oxidator at 0 and 25OC. Here, the total time of synthesis is kept constant for 48 hours, while the strirring duration are varied for 48, 36, 24, 12, 6, 3, 1, and 0 (without strirring) hours. The total time of synthesis is approximately 48 hours. The dark green polyaniline powder is produced and characterized using Raman Spectrocopy, FTIR, XRD, SEM, and EIS. SEM results show that the size of polyaniline particles is increases with longer stirring duration. XRD results show there is an expansion of diffraction plane {(110)} from the shift of diffraction angle 2θ, from 25.5 to 25O, as the function of stirring duration. Raman spectra also show a shift for whole spectra to the higher wavenumber effected by stirring. Infrared spectra show that quinoid, benzoid, and aromatic C-H appear at 1557 cm-1,1477 cm-1, and 1302 cm-1. EIS data show that the longer stirring duration leads to the growth of polyaniline with lower conductivity in the range of 0,1-0,03 S cm-1.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing I : Dr. Veinardi Suendo; Pembimbing II : Dr. Achmad Rochliadi, Editor: Alice Diniarti

File PDF...