STUDI PENGARUH PENGGUNAAN PERLIT SEBAGAI POZOLAN ALAM TERHADAP KUAT TEKAN SPESIMEN MORTAR

STUDY THE EFFECT OF PERLITE AS A NATURAL POZZOLAN ON COMPRESSION STRENGTH OF MORTAR SPECIMEN

Master Theses from JBPTITBPP / 2017-10-09 10:20:25
Oleh : Marisa Hirary - NIM: 23715302 , Central Library Institute Technology Bandung
Dibuat : 2017-09-28, dengan 1 file

Keyword : Semen portland, PCC, pozolan, perlit, kuat tekan

Perlit (perlite) merupakan batuan vulkanik glassy yang kaya akan SiO2 amorf. Pemanfaatan perlit untuk campuran semen portland adalah salah satu upaya peningkatan nilai tambah sumber daya mineral bukan logam. Penelitian ini bertujuan untuk meningkatkan kualitas semen portland dengan memanfaatkan bahan alam berupa batuan perlit sebagai pozolan. Karakterisasi XRD dan XRF dilakukan untuk mengetahui komposisi kimia bahan perlit. Pengaruh penambahan perlit diketahui dari hasil pengujian kuat tekan spesimen mortar semen portand – perlit. Pengurangan jumlah semen portland untuk campuran mortar hingga 50%, diganti dengan perlit. Pengujian kuat tekan dilakukan terhadap pada umur 7 hari, 28 hari, dan 60 hari. Hasil XRD dan XRF menunjukkan bahwa perlit adalah senyawa amorf dengan komposisi kimia sebagian besar terdiri SiO2. Kuat tekan spesimen bertambah dengan meningkatnya umur spesimen. Penambahan 30% perlit menaikkan kuat tekan dari 25,4 MPa menjadi 28,9 MPa pada umur spesimen 28 hari. Peningkatan kuat tekan terjadi seiring bertambahnya jumlah fasa Calcium Silicate Hydrate (CSH) berdasarkan analisis XRD. Penambahan perlit lebih dari 30% tidak lagi optimal untuk meningkatkan kuat tekan spesimen karena jumlah portlandite/ Calcium Hydroxide (CH) semakin sedikit.

Deskripsi Alternatif :

Perlite are glassy volcanic rocks that rich in amorphous SiO2. The use of perlite in portland cement will increase the value of nonmetallic mineral resources. The properties of perlite are influenced by the location and it’s formation. This study aims to improve the quality of portland cement by using natural resource such as perlite rocks as natural pozzolan. XRD and XRF characterizations was conduct to determine the chemical composition of perlite. The effect of the addition of pearlite was observed from compressive strength of cement portand – perlite mortar specimens. Reduction of portland cement in the mortar specimens up to 50%, replaced by perlite. The compressive test was done at the age of specimens 7 days, 28 days, and 60 days. The XRD and XRF result indicate that perlite is an amorphous compound which chemical composition mostly consist of SiO2. The compressive strength of the specimens rise by increasing the age of the specimen. Addition of 30% perlite increase the compressive strength from 25.4 MPa to 28.9 MPa at the age 28 days. Calcium Silicate Hydrate (CSH) phase in the specimens rise as the increasing of compressive strength based on XRD analysis. The addition more than 30% perlit is no longer optimal to increase the compressive strength of the specimen as the number of portlandite / Calcium Hydroxide (CH) decrease.

Copyrights : Copyright (c) 2001 by Perpustakaan Digital ITB. Verbatim copying and distribution of this entire article is permitted by author in any medium, provided this notice is preserved.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiC
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Dr. Ir. Aditianto Ramelan , Editor: Irwan Sofiyan

File PDF...