EVALUASI KINERJA STRUKTURAL CAMPURAN BERASPAL STONE MASTIC ASPHALT DENGAN ASPAL MODIFIKASI POLIMER BERORIENTASI PLASTOMER (ETHYLENE VINYL ACETATE)

STRUCTURAL PERFORMANCE EVALUATION OF STONE MASTIC ASPHALT MIXTURE WITH POLYMER MODIFIED ASPHALT - PLASTOMER ORIENTED (ETHYLENE VINYL ACETATE)

Undergraduate Theses from JBPTITBPP / 2017-09-27 10:25:48
Oleh : MARIO GAMASEPTO (NIM : 15007030); Pembimbing : Dr. Harmein Rahman S.T.,M.T., S1 - Department of Civil Engineering
Dibuat : 2011, dengan 7 file

Keyword : Stone Mastic Asphalt, Ethylene Vinyl Acetate, Kadar Aspal Optimum, Indeks Kekuatan Sisa

Suatu struktur perkerasan diharapkan memiliki kinerja struktural dan fungsional yang baik, serta memiliki usia layan yang lebih lama. Penelitian ini bertujuan untuk membandingkan kinerja struktural dari suatu campuran aspal Stone Mastic Asphalt (SMA) yang menggunakan aspal pen 60/70 dan aspal modifikasi polimer Ethylene Vinyl Acetate (EVA) 3%. Pemanfaatan EVA sebagai modifier aspal pada campuran SMA diharapkan dapat meningkatkan kinerja struktural campuran.


Pengujian laboratorium yang dilakukan adalah dengan menggunakan metoda Marshall untuk menentukan kadar aspal optimum (KAO) dari masing-masing campuran aspal. Pengujian dilanjutkan dengan metoda Marshall Immersion (perendaman) untuk mengetahui durabilitas dari campuran aspal.


Hasil KAO yang diperoleh adalah 6.6% untuk aspal pen 60/70 dengan gradasi agregat D=5mm; 5.6% untuk aspal pen 60/70 dengan gradasi agregat D=2mm; 7% untuk aspal modifikasi EVA 3% dengan gradasi agregat D=5mm; dan 6.1% untuk aspal modifikasi EVA 3% dengan gradasi agregat D=22mm.


Hasil Marshall Immersion menunjukkan bahwa dengan penambahan EVA 3% pada aspal dan dengan gradasi agregat D=5mm akan menghasilkan Indeks Kekuatan Sisa (IKS) campuran sebesar 97.63%, jauh lebih baik daripada campuran dengan aspal pen 60/70 biasa yang menghasilkan IKS sebesar 91.48%.

Deskripsi Alternatif :

A pavement structure is expected to have a good structural and functional performance, and also a long service life. This research aimed to compare the structural performance of a Stone Mastic Asphalt (SMA) mixture using Pen 60/70 asphalt with the one using Polymer Modified Asphalt – Ethylene Vinyl Acetate (EVA). The utilization of EVA as an asphalt modifier on SMA mixture is expected to improve structural performance of the mixture.


Laboratory testing is done by using the Marshall Test method to determine the optimum asphalt content (OAC) of each mixture. Testing continued with the Marshall Immersion method to determine the durability of the mixtures.


OAC results obtained is 6.6% for the 60/70 pen asphalt with aggregate gradation D = 5mm; 5.6% for the 60/70 pen asphalt with aggregate gradation D = 22mm; 7% for the EVA 3% modified asphalt with aggregate gradation D = 5mm; and 6.1% for the EVA 3% modified asphalt with aggregate gradation D = 22mm.


Marshall Immersion results show that with the addition of EVA 3% on the asphalt with the gradation D = 5mm will result in 97.63% of Index of Remaining Strength (IRS), much better than the Pen 60/70 asphalt mixture with 91.48% of IRS.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Dr. Harmein Rahman S.T.,M.T., Editor: PKL-SMK

File PDF...