FORMULASI MIKROPARTIKEL BERPORI DAN ENKAPSULASI PROTEIN DALAM POLI (D,L-LAKTIDA)

Undergraduate Theses from JBPTITBPP / 2009-04-17 15:01:11
Oleh : LILI FITRIANI (NIM 10704065), S1 - Department of Pharmacy
Dibuat : 2008, dengan 8 file

Keyword : mikropartikel berpori, enkapsulasi protein, Poli (D,L-Laktida)

Poli (D,L-Laktida) telah digunakan untuk pembuatan mikropartikel sebagai matriks dan kontrol pelepasan protein, seperti faktor pertumbuhan, dalam teknik rekayasa jaringan. Pada penelitian ini mikropartikel dibuat dalam bentuk mikropartikel berpori dan mikropartikel tidak berpori dan digunakan papain sebagai model protein. Mikropartikel berpori yang berisi hidrogel ditujukan untuk menahan pelepasan awal protein dan mencegah difusi ke jaringan yang tidak diinginkan. Mikropartikel tidak berpori dibuat sebagai sistem penghantaran protein. Formulasi mikropartikel berpori dilakukan dengan emulsifikasi ganda penguapan pelarut air/minyak/air (A1/M/A2) menggunakan gas porogen hasil reaksi natrium bikarbonat dan asam sitrat. Parameter yang diteliti yaitu jumlah natrium bikarbonat, rasio volum larutan asam sitrat dan waktu pengadukan emulsi primer. Evaluasi mikropartikel berpori meliputi morfologi, distribusi ukuran, dan porositas. Enkapsulasi protein dalam mikropartikel tidak berpori dilakukan dengan emulsifikasi ganda penguapan pelarut A1/M/A2 dan padat/minyak/air (P/M/A). Diteliti pengaruh jenis emulsifikasi dan jumlah PEG 20000 terhadap efisiensi enkapsulasi papain dalam mikropartikel. Formula optimum mikropartikel berpori dihasilkan dengan rasio volum larutan asam : metilen klorida : poli vinil alkohol (PVA) = 1:3:3 dan rasio natrium bikarbonat : PDLLA = 2:3. Hidrogel tidak dapat menyatu dalam pembuatan mikropartikel berpori sehingga ditambahkan di luar mikropartikel. Efisiensi enkapsulasi papain dengan emulsifikasi A1/M/A2 yaitu 6,38%+-0,025; sedangkan metode P/M/A dengan rasio papain-PEG 20000 1:1 ; 1:4 ; dan 1:5 berturut-turut adalah 6,24%+-0,91 ; 30,15%+-1,66 dan 60,67%+-4,93. Dapat disimpulkan bahwa mikropartikel berpori dapat dibuat dengan menggunakan gas sebagai porogen dan efisiensi enkapsulasi tertinggi diperoleh dengan emulsifikasi P/M/A.

Deskripsi Alternatif :

Poly (D,L-lactide acid) has been used as scaffold and controlled release device for protein such as growth factor in tissue engineering. In this study, PDLLA microparticles were made in two types, porous and non-porous microparticles and papain was used as model protein. Porous microparticles were proposed to reduce burst release of protein and to prevent diffusion of released protein into non-target tissue, whilst non-porous microparticles were used as delivery system of the protein. Formulation of porous microparticles was made by water-oil-water (W1/O/W2) emulsification-solvent evaporation using gas foamed as porogen. Variations of the amount of sodium bicarbonate, volume of citric acid solution and time for homogenization were optimized to produce optimum formulation. Evaluation for this microparticles included morphology of particles, particle size distribution and porosity. Protein was encapsulated in microparticles using W1/O/W2 and solid-oil-water (S/O/W) emulsification-solvent evaporation. Types of encapsulation methods and ratios of papain-PEG 20000 were observed in this study to provide the highest encapsulation efficiency. Porous microparticle produced by ratio volume of acid : dichloromethane : poly(vynil alcohol) (PVA) = 1:3:3 and the ratio of sodium bicarbonate : PDLLA = 2:3 was the optimum formulation. Hydrogel could not be encapsulated within microparticles, therefore will be added into prepared microparticles. The entrapment efficiency made by W1/O/W2 method was 6,38%+-0,025, whilst S/O/W using ratios of papain-PEG 20000 1:1 ; 1:4 ; and 1:5 were 6,24%+-0,91 ; 30,15%+-1,66 and 60,67%+-4,93, respectively. To conclude, porous microparticle can be produced using gas foamed as porogen and S/O/W is the best method to encapsulate protein with highest entrapment efficiency.

Copyrights : Copyright Â(c) 2001 by ITB Central Library. Verbatim copying and distribution of this entire article is permitted by author in any medium, provided this notice is preserved.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing: Dr. Tri Suciati, M.Si., dan Dr. Heni Rachmawati, Editor: Vika A. Kovariansi

File PDF...