ANALISIS PENGARUH PERSEN VOLUME H2 PADA PROSES PELAPISAN BAJA GALVANIS SEBAGAI MEDIA DALAM NON OXIDIZING FURNACE

ANALYSIS OF THE INFLUENCE OF % VOLUME H2 IN GALVANIZED STEEL COATING PROCESS AS A MEDIUM IN A NON-OXIDIZING FURNACE

Undergraduate Theses from JBPTITBPP / 2017-09-27 10:37:14
Oleh : JULHARBI (NIM : 125 06 011), S1 - Metallurgy
Dibuat : 2011, dengan 7 file

Keyword : Baja galvanis, Non Oxidizing Furnace (NOF)

Baja galvanis merupakan jenis baja yang telah dilapisi dengan seng untuk menanggulangi terjadinya korosi pada baja. Metode yang paling banyak dipakai dalam proses pelapisan baja dengan seng adalah continous hot dip galvanizing. Sebelum strip baja dimasukkan ke dalam bak yang berisi lelehan seng, harus terlebih dahulu memasuki furnace untuk dilakukan proses annealing dan pembersihan permukaan strip baja. Salah satu jenis furnace yang digunakan adalah Non Oxidizing Furnace (NOF). Di dalam NOF ditiupkan gas H2 yang berfungsi untuk membersihkan permukaan strip baja dari oksida. Persen volume H2 yang dipakai didalam NOF saat ini adalah 40%. Persen volume H2 sebesar 40% dianggap terlalu besar sehingga menyebabkan biaya produksi yang mahal. Oleh sebab itu, penggunaan gas hidrogen dalam NOF harus dikurangi sampai suatu batas toleransi tanpa menimbulkan cacat atau efek berupa kegagalan pada baja galvanis yang dihasilkan.



Sampel diperoleh dari PT FUMIRA dengan ukuran 10 x 10 x 0.02 cm. Pengujian ketebalan, kekerasan dan kekasaran permukaan lapisan Zn dilakukan untuk mengetahui pengaruh % volume H2 terhadap proses pelapisan baja galvanis. Selain itu juga dilakukan pengamatan dengan menggunakan SEM dan EDS untuk mengetahui komposisi oksida yang terdapat di lapisan Fe-Zn. Sampel yang diuji mempunyai persen volume H2 mulai dari 38% sampai 20%.



Hasil pengujian yang didapat menunjukkan semakin turun % volume H2, ketebalan lapisan Zn semakin naik sehingga menyebabkan kekerasan lapisan Zn juga naik. Hasil pengamatan dengan menggunakan EDS menunjukkan pada 20% volume H2 masih terdapat oksida sebesar 7.34 % di lapisan Fe-Zn. Selain itu, % volume H2 juga mempengaruhi kekasaran permukaan lapisan seng. Semakin tinggi % volume H2, permukaan lapisan Zn cenderung lebih kasar karna lebih banyak spangle dipermukaan lapisan. Penurunan % volume H2 sampai 20% masih di rekomendasikan karena ketebalan lapisan Zn dan kekerasannya tidak berubah secara signifikan.

Deskripsi Alternatif :

Galvanized steel is a type of steel that has been coated with zinc to prevent corrosion in steel. The most widely used method in the process of coating steel is a continuous hot dip galvanizing. Before the steel strip is inserted to a bath containing molten zinc, the steel strip must first enter the furnace to do the process of annealing and surface cleaning of steel strip. One type of furnace used is a non-oxidizing furnace (NOF). In the NOF exhaled H2, which serves to clean the oxide on surface of the steel strip. %volume of H2 used in the NOF is currently 40%. This value of % volume of H2 is considered too big and it makes the production cost expensive . Therefore, the use of H2 in NOF should be reduced to a limit of tolerance without causing defects on galvanized steel product. The sample has been obtained from the factory of galvanized steel PT FUMIRA and it has 10 x 10 x 0.02 cm in size. Measurement of the thickness, hardness and surface roughness of Zn coating performed to determine the effect of %volume of H2 on galvanized steel coating process. It was also observed by using SEM and EDS to determine the composition of the oxides contained in the Fe-Zn coating. The samples tested had benn used volume of H2 ranging from 38% to 20%. From the test results, it is found that Zn coating thickness will increase with the reduction of % volume H2 and further it also increase the hardness of the Zn coating. From the observation by using EDS, in 20 % volume H2 there are still 7.34 % amount of oxides in the Fe-Zn coating. In addition, % volume of H2 is also affecting the surface roughness of zinc coating. The higher % volume H2, the surface layer of Zn become rougher because there are more spangles in the surface layers. The decreasing of % volume of H2 until 20% is still recommended because the thickness and hardness of the zinc coating doesn’t change significantly.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Prof. Dr. Ir. Syoni Soepriyanto, M.Sc.
    , Editor: Alice Diniarti

File PDF...