BIOAKTIVITAS SARGASSUM SP. DAN GRACILARIA SP. SEBAGAI INHIBITOR BIOKOROSI PADA BAJA KARBON

BIOACTIVITY SARGASSUM SP. AND GRACILARIA SP. AS BIOCORROSION INHIBITOR AT CARBON STEEL

Undergraduate Theses from JBPTITBPP / 2014-03-11 13:07:41
Oleh : ISRIYANTI AFFIFAH (NIM : 10508102); Pembimbing 1 : Dr. Fida Madayanti W. ; Pembimbing 2 : Dr. Bunbun Bundjali, S1 - Department of Chemistry
Dibuat : 2012, dengan 7 file

Keyword : anti korosi, bioaktivitas, makroalga, T. ferooxidans

Korosi atau perkaratan logam merupakan proses oksidasi suatu logam dengan udara atau elektrolit. Udara atau elektrolit tersebut akan mengalami reduksi, sehingga proses korosi merupakan proses elektrokimia. Pada penelitian sebelumnya diketahui bahwa korosi yang disebabkan mikroorganisme pengoksidasi besi (Thibacillus ferooxidans) memiliki peranan yang cukup signifikan terhadap kerugian ekonomi bagi industri. Lapisan biofilm yang dihasilkan mikroorganisme pada permukaan logam dapat mengubah karakteristik elektrokimia permukaan logam tersebut dan dapat menginduksi terjadinya korosi. Untuk mengatasi masalah tersebut, pada penelitian ini dilakukan ekstraksi Sargassum sp. dan Gracilaria sp. yang diduga efektif menginhibisi pertumbuhan mikroba pengoksidasi besi (Thibacillus ferooxidans) yang biasanya terdapat di bangunan bawah laut. Hasil ekstraksi Sargassum sp. dan Gracilaria sp. menggunakan pelarut metanol-kloroform (1:1) memberikan yield terhadap berat basah sebesar 44,5% dan 36,5%. Ekstrak tersebut diuji bioaktivitasnya terhadap pertumbuhan T. ferooxidans secara kualitatif (kasat mata) dan kuantitatif (metode weight-loss). Melalui kurva pertumbuhan diketahui bahwa T. ferooxidans mampu tumbuh sampai hari ke-7 dan mengalami fasa stasioner pada hari ke-8. Analisis metode weight-loss dilakukan menggunakan coupon dengan luas permukaan 3,6 cm2. Hasil analisis menunjukkan bahwa pada hari ke-7 ekstrak Sargassum dan Gracilaria memiliki aktivitas antibakteri terhadap pertumbuhan T. ferooxidans pada konsentrasi 400 μL dan 300 μL dalam 10 ml media. Hal ini ditandai dengan berkurangnya pengurangan berat pada coupon dalam media yang mengindikasikan berkurangnya korosi. Nilai LD50 ekstrak makroalga terhadap pertumbuhan T. ferooxidans diperoleh sebesar 477 μL untuk Sargassum sp dan 318 μL untuk ekstrak Gracilaria sp dalam 10 ml media padat. Melalui uji variasi hari diketahui bahwa kedua ekstrak makroalga mampu menginhibisi pertumbuhan T. ferooxidans sampai hari ketiga.

Deskripsi Alternatif :

Corrosion is a process of metal oxidation by air or electrolyte which the air or electrolyte will be reduced, so that the process of corrosion is an electrochemical process. In the previous study, it was known that corrosion caused by microorganisms oxidizing iron (Thiobacillus ferooxidans) has a significant role towards the economic losses for industry. Biofilm on metal surface caused by microorganism can alter the electrochemical characteristics of the metal surface and can induce the occurrence of corrosion. To overcome these problems, extraction of Sargassum sp. and Gracilaria sp. that is suspected as an antimicrobial agent is used in this study. Yield of exctraction macroalgal using methanol-chloroform (1:1) as solvent was 44.5% for Sargassum sp and 36.5% for Gracilaria sp. Those extract was tested toward inhibit on the growth of Thiobacillus ferooxidans qualitatively (visible) and quantitatively (weight-loss method). The growth curve showed that T. ferooxidans was able to grow until day 7th and had a stationary phase on day 8 th. Analysis of corrotion inhibiting effect using weight-loss method was performed using a coupon with a surface area of 3.6 cm2. The analysis showed that at day 7 th the methanol extract of Sargassum and Gracilaria have antibacterial activity against the growth of T. ferooxidans at a concentration of 400 μL and 300 μL in 10 mL of media. It is characterized by less severe reduction in the coupon in the media indicating reduced corrosion. The LD50 value of macroalgal extract obtained 477 μL (Sargassum sp) and 318 μL (Gracilaria sp) in 25 ml media. Furthermore the corrosion rate determination is being made with a variety of day. The data show that both extracts of macroalgal could inhibit the growth of T. ferooxidans until the third day.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing 1 : Dr. Fida Madayanti W. ; Pembimbing 2 : Dr. Bunbun Bundjali, Editor: Alice Diniarti

Download...