PENENTUAN PROSES PERLAKUAN PANAS BAJA GS-25CrMo4 UNTUK MATERIAL KOMPONEN BUCKET TOOTH ADAPTOR

DETERMINATION OF THE HEAT TREATMENT PROCESS OF GS-25CrMo4 STEEL FOR BUCKET TOOTH ADAPTOR COMPONENT MATERIAL

Undergraduate Theses from JBPTITBPP / 2018-02-14 14:40:03
Oleh : Irza Aulia Zaim - Nim: 13712006 , S1 - Materials Engineering-FTMD
Dibuat : 2018-02-14, dengan 1 file

Keyword : Perlakuan panas, bucket tooth adaptor, GS-25CrMo4, quenching,

align="justify">Baja GS-25CrMo4 merupakan material dari PT. Pindad (Persero) yang digunakan untuk komponen bucket tooth adaptor pada excavator atas permintaan PT. Pamapersada Nusantara. Bucket tooth adaptor merupakan komponen yang terekspos pada kondisi lapangan yang bersifat abrasif, sehingga dibutuhkan sifat mekanik yang baik terutama kekerasan dan ketahanan impak yang tinggi. Oleh karena itu, PT. Pindad (Persero) menginginkan komponen bucket tooth adaptor yang memiliki kekerasan 26 - 32 HRC dan ketahanan impak diatas 32 Joule. Untuk mencapai tujuan tersebut, dilakukan perlakuan panas yaitu quench and temper. Percobaan ini dilakukan dengan memanaskan baja pada temperatur austenisasi, lalu dicelup (quenching) ke dalam air sebagai medium pendingin. Kemudian tempering dilakukan pada temperatur 200oC, 300oC, 400oC, 500oC, 600oC untuk mencari temperatur optimal. Hasil uji keras menunjukkan adanya penurunan kekerasan seiring semakin tingginya temperatur tempering. Hasil metalografi menunjukan perubahan struktur mikro sebelum dan sesudah diberi perlakuan panas. Hasil uji impak pada spesimen yang mengalami tempering di 300oC mengalami penurunan dibandingkan dengan produk as quench dan mengalami kenaikan di temperatur tempering 600oC . Kesimpulannya, temperatur tempering yang sesuai dengan hasil yang diinginkan PT. Pindad (Persero) adalah di antara 500-600 oC

align="justify">

Deskripsi Alternatif :

align="justify">GS-25CrMo4 steel is a material used for bucket tooth adaptor components in excavators by PT. Pindad (Persero) as required by PT. Pamapersada Nusantara. Bucket tooth adaptor is exposed to the abrasive condition that it requires an excellent mechanical properties. Therefore, PT. Pindad (Persero) stipulates that the components hardness is 26 - 32 HRC and Charpy V Notch impact resistance above 32 Joule. To meet those requirements, the quench and temper hear treatments were done. The experiment was carried out by heating the steel at austenitization temperature and then quenching into the water as a cooling medium. The tempering is done at temperatures of 200oC, 300oC, 400oC, 500oC, 600oC to find the optimal temperature. Hardness testing results indicated a decline as the tempering temperature is rising. Metallographic results show changes in microstructure before and after heat treatments. The impact test on specimens shows that tempering at 300oC has a lower impact resistance than the As-Quenched and specimens tempered at 300oC shows the highest among all. In conclusion, 500-600oC is the optimum tempering temperature to meet specification from PT. Pindad (Persero).

align="justify">

Copyrights : Copyright (c) 2001 by Perpustakaan Digital ITB. Verbatim copying and distribution of this entire article is permitted by author in any medium, provided this notice is preserved.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Prof. Dr. Ir. Rochim Suratman , Editor: Irwan Sofiyan

File PDF...