PENGARUH RASIO SIKAFUME® – SEMEN 0,11 – 0,25 DAN RASIO AIR SEMEN 0,25 – 0,35 TERHADAP KEKUATAN TEKAN MORTAR DENGAN SEMEN 30 w/o

Undergraduate Theses from JBPTITBPP / 2017-10-09 10:32:49
Oleh : IRAWAN SURYA KUSUMA (NIM : 13705035); Pembimbing : Dr. Ir. Aditianto Ramelan, S1 - Material Engineering Study Programme
Dibuat : 2010, dengan 7 file

Keyword : Mortar, Silica Fume, rasio silica fume – semen, rasio air – semen, Mortar, Silica Fume, silica fume – cement ratio, water – cement ratio

Silica fume merupakan pozzolan yang sering digunakan untuk menaikkan kekuatan tekan beton. Penelitian ini membuat mortar berkekuatan tinggi dengan menggunakan SikaFume® yang merupakan silica fume produk PT Sika Indonesia sebagai




cement replacement dan rasio air semen yang rendah. Agar mortar memiliki flowability yang baik, maka ditambahkan superplasticizer yaitu Sikament®-NN yang juga




merupakan produk PT Sika Indonesia.




Rasio SikaFume® - semen pada penelitian ini adalah 0,11; 0,17; dan 0,25 yang digunakan pada rasio air – semen 0,25; 0,30; dan 0,35. Semen dan superplasticizer menjadi variabel tetap yaitu pada 30 w/o dan 2 w/o dengan komposisi total 1000 gram.




Metode curing yang digunakan adalah curing udara selama 2 minggu. Uji tekan menggunakan alat uji universal Tarnogrocki yang berada di laboratorium Teknik Metalurgi dan Material ITB. Hasil uji tekan yang didapat pada mortar normal pada penelitian ini sangat rendah. Kekuatan terendah didapatkan pada spesimen mortar normal w/c 0,35 yaitu 5,8 MPa dan tertinggi dicapai oleh mortar w/c 0,35 dengan s/c 0,17 yaitu sebesar 28,1 MPa. Selain pengujian tekan, dilakukan juga karakterisasi XRD dan SEM pada kedua mortar tersebut. Peneliti juga melakukan karakterisasi SEM pada pasir silika dan SikaFume®. Didapatkan SikaFume® yang digunakan telah teraglomerasi.




Dari penelitian ini didapatkan pada mortar normal, kenaikan w/c menurunkan kekuatan tekan. Sedangkan pada pemakaian SikaFume®, semakin tinggi w/c kekuatan tekan yang diperoleh semakin tinggi. Namun pada kenaikan s/c tertentu justru




menyebabkan persentase kenaikan kekuatan naik menurun. Rendahnya rasio semen – agregat (c/a) dan banyaknya pori yang terbentuk menyebabkan kekuatan tekan yang diperoleh sangat rendah dan jauh dari target 280 MPa.

Deskripsi Alternatif :

Silica fume is a pozzolanic compound that is highly known as one of the cementious material available in the production of certain types of concrete. The purpose




of this study was to find out the effectiveness SikaFume® , which is the product of PT Sika Indonesia, in producing high strength mortar with low water/cement ratio as the




substitution for cement. Superplasticizer used in this study is Sikament®-NN, a product of PT Sika Indonesia, which was added to improve the mixture’s flowability.




The ratio of SikaFume® - cement (s/c) used in this study were 0,11; 0,17; and 0,25. The ratio of water - cement (w/c) used were 0,25; 0,30; and 0,35. Cement and




superplasticizer were determined as constant variable on 30 w/o and 2 w/o. The samples were air cured for two weeks since they were casted. Compression tests were conducted




using Tarnogrocki Universal Testing in laboratory of Metallurgy and Materials Engineering ITB. The compressive strengths obtained for normal mortar in this research




is quite low. The lowest strength of speciments with w/c of 0,35 is 5,8 MPa and the highest was 28,1 MPa for w/c 0,35 with s/c 0,17. For more thorough analysis, XRD and SEM characterization were also performed for both compositions. Silica sand and SikaFume® were also characterized by SEM, therefore showed that SikaFume® in the form of agglomerates.




This study showed that on normal mortar, increasing w/c make the compressive strength lower. While the used of SikaFume® in higher w/c make the compressive strength higher. However, the increasing of s/c ratio reduce the maximum compressive strength. Lower cement – aggregate ratio (c/a) and the massive expansion of pores formed reduce the compressive strength. This result is below the targeted value of 280 MPa.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Dr. Ir. Aditianto Ramelan, Editor: Alice Diniarti

File PDF...