PENGARUH REGANGAN TERHADAP NILAI KETANGGUHAN PATAH DAN PERILAKU PERAMBATAN RETAK BAJA HIGH STRENGTH Low Alloy UNTUK APLIKASI PEMBUATAN PIPA GAS API 5L X-60

Undergraduate Theses from JBPTITBPP / 2017-10-09 10:31:13
Oleh : Herman R Siagian (NIM : 12103045), S1 - Department of Geophysics and Meteorology
Dibuat : 2007-06-00, dengan 7 file

Keyword : Low Alloy ;

Abstrak :






Salah satu aplikasi pengembangan baja high strength low alloy (HSLA) adalah material untuk pembuatan pipa. Baja HSLA hasil produksi PT. Krakatau Steel ini akan digunakan dalam pembuatan pipa gas API 5L X-60. Pipa ini rencananya digunakan untuk mengalirkan gas yang mengandung asam. Besar ukuran diameter pipa dapat dipengaruhi oleh regangan yang diberikan pada baja sebagai material pembuatan pipa. Dalam penelitian ini dilakukan analisis pengaruh regangan terhadap ketangguhan perambatan retak baja HSLA sebagai material pipa melalui nilai KIC. Dari pengujian mekanika patahan, akan dihasilkan grafik beban (kN) versus perpindahan (mm) yang akan digunakan untuk mencari nilai ketangguhan patah (fracture toughness) yang diwakili oleh parameter CTOD (crack tip opening displacement). Pengujian dilakukan dengan menggunakan standar ASTM E1290. Nilai ketangguhan patah hasil pengujian untuk spesimen regangan 0%, 5%, 10%, dan 15% berturut-turut adalah 83.8, 67.9, 46.2, dan 42.5 Mpa m1/2. Pengamatan terhadap permukaan patahan dilakukan dengan menggunakan foto mikro (SEM). Hasil foto mikro menunjukan jenis patahan untuk spesimen regangan 0%, 10%, dan 15% masing-masing adalah patah ulet, patah ulet dan intergranular, dan patah intergranular. Untuk mengetahui pengaruh regangan terhadap pengerasan regangan yang terjadi, dalam penelitian ini dilakukan pengujian kekerasan Vickers yang kemudian dikonversikan terhadap kekuatan ultimat baja HSLA. Hasil analisis pengaruh regangan menunjukan bahwa nilai ketangguhan patah spesimen baja menurun secara linear dengan meningkatnya nilai regangan, sedangkan kekerasan dan kekuatan ultimat baja HSLA meningkat dengan meningkatnya regangan yang diberikan. Disamping itu, diameter pipa maksimum yang dapat dibuat akan semakin kecil dengan meningkatnya nilai regangan yang diberikan.

Deskripsi Alternatif :

Abstract :






One of the high strength low alloy steel (HSLA) development application is material for produce pipe. This HSLA steel that produced by PT. Krakatau Steel will be used in the production of API 5L X-60 Gas Pipe. This Pipe will be used to flow out gases that contains of sour. The diameter of the pipe that will made is affected by strain that force to the steel plate as the material in the production of pipe. In this research the analysis is carried out to study the affect of that strain on the crack propagation toughness of HSLA steel as material of pipe by its KIC. From the test of fracture mechanism, the load (kN) vs displacement (mm) graph obtained will be used to calculate the fracture toughness value that represent by CTOD parameter. This test is determined by using ASTM E1290 standard. The fracture toughness values as the result on this 0%, 5%, 10%, and 15% strain specimens resvectively in a series are 83.8, 67.9, 46.2, and 42.5 Mpa m1/2. Observation on the fracture surfaces is carried out using SEM. The results of the SEM show the type of fracture for 0%, 10%, and 15% strain spesimens resvectively are ductile fracture, ductile and intergranular fracture, and intergranular fracture. To study the effect of strain on strain hardening that occur, in this research the Vickers hardness test is carried out and then converted to ultimate strength of HSLA steel. The results of the strain effect show that the fracture toughness value of steel specimens decrease linearly with increasing in strain, while the hardness and ultimate strength of HSLA steel increasingly with increasing in strain. Besides that, the maximum diameter of pipe that can be made will be smaller with increasing in strain.

Copyrights : Copyright (c) 2007 by Fakultas Ilmu Kebumian Dan Teknologi .Information Dissemination Right @2007






ITB Central Library, Jl. Ganesha 10 Bandung,40132, Indonesia.






Verbatim copying and distribution of this entire article is permitted by author to ITB Central






Library in any medium, provided this notice is preserved.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing Tugas Akhir I:Syoni Soepriyanto.Ir.,M.Sc.,Dr. ;






    Pembimbing Tugas Akhir II:






    Ahmad Taufik Joeneos M.Eng.,Dr.







    Scanner: Alice Diniarti; 2007-11-25, Editor: PKL-SMK

File PDF...