Path: TopS2-ThesesMaterial Science and Technology-FTMD2011

SINTESIS MEMBRANE SUPPORT ALGINAT-KITOSAN DENGAN TEKNIK PENGERINGAN BEKU DAN PENUMBUHAN HIDROKSIAPATIT DENGAN METODE SELF ASSEMBLY UNTUK APLIKASI SCAFFOLD

Master Theses from JBPTITBPP / 2017-10-09 10:20:25
Oleh : HARIYADI KURNIANTO (NIM : 23709008); Tim Pembimbing : Dr. Ir. Hermawan Judawisastra; Dr. Ir. Bambang Sunendar , S2 - Material Science and Engineering
Dibuat : 2011, dengan 7 file

Keyword : scaffold, membrane support alginat-kitosan, hidroksiapatit, Self Assembly, freeze drying

Keterbatasan akan jumlah donor untuk transplantasi merupakan permasalahan yang serius, maka perlu dicari alternative material pengganti yang dapat mengatasi keterbatasan akan kebutuhan jumlah donor. Pada penelitian ini telah berhasil dibuat scaffold alginat-kitosan dengan metode freeze drying. Untuk meningkatkan kinerja scaffold yang dibuat, diperlukan suatu material sebagai penginisiasi pertumbuhan sel baru. Pada proses Tissue Engineering diperlukan material inisiator yang mempunyai sifat-sifat biokompatibilitas, bioaktif, biodegradasi yang baik. Maka diperlukan suatu modifikasi membrane support alginat-kitosan dengan menumbuhkan hidroksiapatit (HAp) pada permukaan membrannya. Alginat dan kitosan memiliki muatan ion yang berlawanan, dimana kitosan memilki muatan positif sementara alginat memiliki muatan negatif. Penggabungan keduanya akan membentuk dua ikatan kimia yang stabil yang dapat meningkatkan integritas strukturnya. Campuran kitosan dan alginat dapat membentuk membrane scaffold dengan proses freeze drying dalam waktu yang relatif singkat dan mudah diatur tingkat porositasnya. Membrane support alginat-kitosan digunakan sebagai media penumbuhan HAp, dimana larutan Simulated Body Fluid (SBF) jenis Kokubo digunakan sebagai sumber HAp yang disintesis dengan metode Self Assembly dengan variasi waktu perendaman yaitu 1 hari dan 4 hari. Hasil karakterisasi Scanning Electron Microscope (SEM) dari proses freeze drying




memperlihatkan morfologi dari membran yang berpori dengan diameter pori rata-rata 95μm, yang mana telah mendekati pori scaffold komersil. Hasil karakterisasi X-Ray Diffraction (XRD) menujukan bahwa telah terbentuk fasa kristalin HAp dengan referensi puncak 2θ pada kisaran antara 32o - 33o, dimana derajat kristalinitas dari HAp meningkat seiring dengan lamanya perendaman.

Deskripsi Alternatif :

Limitation to the number of donors for transplantation is a serious problem, which need for an alternative replacement material that can overcome this limitation. In this study, alginate-chitosan scafffold has been succesfully synthesized by freeze drying method. To improve the performance of scaffold, it is needed a material as initiator for new cell growth. In Tissue Engineering, the materials for initiator of new cell growth are required to have good properties of biocompatible, bioactive and biodegradable. To meet the requirment of those properties, it needs to modificate alginate-chitosan membrane by growing hydroxyapatite (HAp) on the membrane surface. Alginate and chitosan have opposite ion charge, where the chitosan has a positive charge and the alginate has a negative charge. The mixing of chitosan and alginate will form two stable chemical bonds that increase their structural integrity. Mixture of chitosan and alginate can form a scaffold membrane by freeze drying process in relatively short time and easy to set the level of porosity. Alginate-chitosan membrane support was use as growing media for HAp with Simulated Body Fluid (SBF) solution was used as a source of HAp. The growth oh




HAp was synthesized by self assembly method with immersing time was varied by 1 day and 4 days. Scanning Electron Microscope (SEM) characterization of freeze drying process of membrane support showed porous morphology with average diameter of 95μm, which closed to comercial product. X-ray Diffraction (XRD) characterization showed the formation of HAp phase with index reference at 2θ of around 32o - 33o, where degree of crystalinity of HAp was increase along with the immersion time.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Tim Pembimbing : Dr. Ir. Hermawan Judawisastra; Dr. Ir. Bambang Sunendar , Editor: Alice Diniarti

File PDF...