KINERJA CAMPURAN HANGAT (WARM MIX) UNTUK CAMPURAN LAPIS ANTARA (AC-BC) MENGGUNAKAN ASPAL PEN 60/70 DAN ZAT ADITIF LEADCAP® DAN SASOBIT®

PERFORMANCE OF WARM MIX ASPHALT CONCRETE BINDER COURSE (AC - BC) USING ASPHALT PEN 60/70, SASOBIT® AND LEADCAP® ADDITIVE

Master Theses from JBPTITBPP / 2017-09-27 15:29:58
Oleh : HANAFI ( NIM : 269 14 006), S2 - Transportation
Dibuat : 2016, dengan 8 file

Keyword : Temperatur, HMA, WMA, aspal Pen 60/70, Sasobit®, Leadcap®

Kenaikan suhu udara dipicu oleh semakin tingginya kadar Gas Rumah Kaca (GRK) diantaranya oleh CO2 yang banyak dihasilkan dari pembangunan jalan, campuran aspal hangat atau Warm Mix Asphalt (WMA) adalah salah satu teknologi yang berbasis ramah lingkungan dimana campuran aspal hangat diproduksi dengan temperatur yang lebih rendah dengan tingkat penurunan suhu antara 20°-40° C dibawah campuran aspal panas (HMA). Persentase penggunaan Sasobit® sebesar 3% sedangkan Leadcap® sebesar 1% dari berat aspal. Kinerja campuran WMA diukur dan dibandingkan dengan campuran HMA dengan melihat sifat dasar dan sifat reologi aspal, sementara kinerja campuran diperoleh dari pengujian Marshall, modulus resilien UMATTA dan uji kelelahan. Hasil pengujian DSR menunjukan penambahan zat aditif Leadcap maupun Sasobit® dapat merubah sifat aspal menjadi lebih elastis. Temperatur pencampuran dan pemadatan WMA dengan zat aditif Sasobit® pada temperatur 134°C /124°C sedangkan Leadcap®124°C/114°C, dimana hasil marshall menunjukan campuran HMA lebih tinggi dibandingkan campuran WMA. Hasil pengujian UMATTA pada temperatur 25°C dan 45°C nilai tertinggi pada campuran WMA dengan Sasobit® (3150 Mpa). Hasil pengujian kelelahan menunjukan campuran WMA dengan zat aditif Sasobit® maupun Leadcap® membuat umur kelelahan meningkat. Secara umum zat aditif dapat meningkatkan kinerja campuran dengan temperatur.


pencampuran dan pemadatan yang lebih rendah dari HMA.

Deskripsi Alternatif :

emissions including the CO2 generated a lot of road construction, Warm Mix Asphalt (WMA) is a technology based on environmentally friendly. Percentage Sasobit® use by 3 % while Leadcap® of 1% of the weight of the


asphalt. The performance WMA mixtures were measured and compared with a mixture of HMA to see properties of bitumen and the advanced rheology, while the performance of the mixture obtained from testing Marshall, UMATTA to


compare resilient modulus and to see fatigue resistance.


The test results showed the addition of additives DSR Leadcap and Sasobit® can change the nature of the asphalt becomes more elastic. Mixing and compaction


temperatures WMA with additives Sasobit® at a temperature of 134°C/124°C while Leadcap® 124°C/114°C, where the results showed a mixture of HMA marshall higher than WMA mix. The test results UMATTA at a temperature of 25°C and 45°C the highest value on the WMA mixture with Sasobit® (3150 Mpa). The test results showed fatigue WMA mixtures with additives Leadcap® and


Sasobit® increased fatigue life. Generally the additives can improve the performance of the mixture by mixing


and compaction temperatures lower than HMA.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing Prof. Dr. Ir Bambang Sugeng S DEA; Dr. Ir. Harmein Rahman, M.T, Editor: Alice Diniarti

File PDF...