FITNESS FOR SERVICE KETAHANAN PIPA TERHADAP PATAH GETAS BERDASARKAN API 579 STUDI KASUS: PROPANE REFRIGERANT PIPING LNG TANGGUH

Undergraduate Theses from JBPTITBPP / 2014-04-24 13:54:37
Oleh : FIRMAN (NIM : 13105090); Pembimbing : Prof. Dr. Ir. IGN Wiratmaja Puja, S1 - Department of Mechanical Engineering
Dibuat : 2010, dengan 7 file

Keyword : Fitness For Service, Ketahanan Pipa, patah Getas, API 579

Operasi sistem perpipaan pada temperatur yang sangat rendah memerlukan pertimbangan khusus semenjak proses desain karena memungkinkan terjadinya kegagalan patah getas. Ciri utama kegagalan patah getas adalah kegagalan yang terjadi sangat cepat (biasanya tanpa peringatan) dan dapat menimbulkan bukaan besar atau kehancuran total padahal beban operasi masih di bawah beban desain. Untuk menentukan apakah komponen masih layak dioperasikan atau tidak, perlu

dilakukan suatu langkah evaluasi yang disebut fitness for service.

Dalam tugas sarjana ini, dilakukan studi dan analisis fitness for service pada piping yang cenderung dapat mengalami patah getas berdasarkan API 579 Part 3

(assessment of existing equipment for brittle fracture). Analisis FFS dilakukan pada pipa-pipa refrigerant propana di unit 051, train 1, Tangguh LNG, Papua. Untuk mempermudah dan mempercepat analisis, dikembangkan program bantu perhitungan pada piping berdasarkan kriteria assessment level 1 dan level 2.

Hasil analisis menunjukkan bahwa berdasarkan asessment level 1, tidak ada pipa yang memenuhi kriteria. Pipa dengan spesifikasi material A671-CC60-22 EFW Impact tested, sebagian besar tidak memenuhi kriteria assessment level 2

metode A - opsi A (tekanan operasi dan temperatur di dalam wilayah aman - impact test exemption curve) namun kriteria assessment level 2 metode A - opsi B (hasil uji impak) terpenuhi. Pipa dengan spesifikasi material A333-6 Seamless sebagian besar memenuhi kriteria assessment level 2 metode A opsi A kecuali pada pipa dengan line class 3CA1J NPS 14 – 26 dan 1CA1J pada segmen 1051 dan 1151. Prosedur level 2 metode B (hasil hidrotes) tidak dapat diterapkan. Sedangkan

berdasarkan analisis level 2 metode C (material, kondisi operasi dan lingkungan, pengalaman) semua pipa aman dan terbebas dari kemungkinan patah getas.

Deskripsi Alternatif :

Piping systems operating at very low temperature requires special consideration since the component will has the propensity of brittle fracture failure. Main characteristic of brittle fracture failure is occurs very quick (usually without warning) and can cause total destructions even the operating load below the design load. To determine whether the component is suitable for further operation or not, it

is necessary to conduct some evaluations which called fitness for service.

This final project contains study and analysis of fitness for service in piping which has a tendency to brittle fractures failure. FFS analysis performed on propane

refrigerant pipes at unit 051, train 1, Tangguh LNG, Papua. To simplify and expedite the analysis, piping calculations program based on level 1 and level 2 assessment criteria has been developed.

Based on the assessment level 1, no pipes meet the criteria. Most of pipe with material specifications A671-CC60-22 EFW Impact tested, do not meet level 2 method A - option A (operating pressure/temperature is within a safe envelope - impact test exemption curve) criteria, but it is met the level 2 method A-option B (impact test results) criteria. Most of pipe with material specification A333-6

Seamless ASME PE B36.10M/B36.19M, fulfills the level 2 method A-option A criteria, except pipes with line class 3CA1J, NPS 14-26 and 1CA1J at segment 1051 and 1151. Level 2 method B (hydrotest result) procedure cannot be applied.

While, all pipes safe and free from the possibility of brittle fracture, based on Level 2 method C (materials of construction, operating conditions, service environment

and past operating experience) analysis.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Prof. Dr. Ir. IGN Wiratmaja Puja, Editor: Alice Diniarti

Download...