Path: TopS1-Final ProjectChemistry-FMIPA2008

PEMBUATAN MEMBRAN FOTOKATALIS TITANIUM DIOKSIDA BERPENDUKUNG POLISTIREN DENGAN PEMEKA CAHAYA Tris-asetilasetonatokromium(III)

Synthesis of the Photocatalytic Membrane of Titanium Dioxide Supported Polystyrene with Tris-acetylacetonatechromium(III) as Photosensitizer

Undergraduate Theses from JBPTITBPP / 2017-09-27 11:42:34
Oleh : EMIR J. RUSTAMI (NIM 10501019), S1 - Department of Chemistry
Dibuat : 2008, dengan 7 file

Keyword : membran fotokatalis, polistiren, Tris-asetilasetonatokromium(III)

Penggunaan membran fotokatalis diketahui dapat mensinergikan reaksi fotokatalisa dan proses pemisahan hasil reaksi dari pereaksinya. Dalam penelitian sebelumnya, dilakukan pembuatan membran fotokatalis dengan menggabungkan antara membran polimerik organik komersial dengan fotokatalis titanium dioksida. Membran fotokatalis tersebut mempunyai kinerja dekomposisi senyawa organik dan pemisahan yang tinggi. Pada penelitian ini, penggabungan dilakukan antara polistiren koanhidrida maleat dan titanium dioksida yang diisi dengan trisasetilasetonatokromium(III) sebagai pemeka cahaya. Berdasarkan hasil penelitian yang dilakukan, peningkatan aktivitas fotokatalis dalam reaksi degradasi senyawa metilen biru secara pada sinar tampak bergantung pada jumlah pemeka cahaya yang ditambahkan. Sedangkan, hasil pengujian permselektivitas menunjukkan pemisahan metilen biru mencapai nilai 75%. Selain itu, membran fotokatalis memiliki kemampuan penghilangan warna hingga 95%. Namun, berdasarkan analisis Chemical Oxygen Demand tidak terjadi degradasi total metilen biru oleh membran fotokatalis yang diperoleh. Membran fotokatalis yang dihasilkan memiliki aktivitas fotokatalis dan pemisahan yang cukup baik.

Deskripsi Alternatif :

The ability of coupling photocatalysis reaction with separation process is a benefit of photocatalytic membranes application. Previous research succeed in making photocatalytic membrane by coupling of various commercial organic polymers with commercial titanium dioxide. This membrane has high performance of decomposition organic molecule and separation. In this Research, is attempted to synthesize photocatalytic membrane by impregnate titanium dioxide with trisacetylacetonatechormium(III) as photosensitizer and immersed on polystyrene comaleic anhydride film. The results show that photocatalytic degradation methylene blue activity under visible light irradiation increase by amount of added photosensitizer on the photocatalyst system. Permselectivity membrane test show 75% methylene blue rejected. Moreover, decolorization methylene blue of synthesized photocatalytic membrane is 95%. However, based on Chemical Oxygen Demand analysis is known that its degradation is not totally. Synthesized photocatalytic membrane has high photocatalytic activity and separation.

Copyrights : Copyright Â(c) 2001 by ITB Central Library. Verbatim copying and distribution of this entire article is permitted by author in any medium, provided this notice is preserved.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing: Dr. I Nyoman Marsih dan Dr. M. Ali Zulfikar, Editor: Vika A. Kovariansi

File PDF...