PENENTUAN UMUR TEKNIS SISA MATERIAL ASTM A297 HP MOD (Nb/MA) DENGAN METODE RESPON ATENUASI GELOMBANG ULTRASONIK DAN REGANGAN CREEP

REMAINING LIFE ESTIMATION ON MATERIAL ASTM A297 HP MOD (Nb/MA) BY ULTRASONIC ATTENUATION METHOD AND CREEP STRAIN MEASUREMENT

Master Theses from JBPTITBPP / 2017-10-09 10:20:25
Oleh : EKO SUGIHARTO (NIM : 23709004); Tim Pembimbing : Dr. Ir. H. Husaini Ardy; Dr. Ir. Arif Basuki, S2 - Material Science and Engineering
Dibuat : 2011, dengan 7 file

Keyword : catalyst tube, creep, ultrasonik, atenuasi, regangan, umur teknis sisa.

Catalyst tube merupakan tabung tempat terjadinya reaksi pembentukan gas hidrogen (H2) dan karbon monoksida (CO) dari gas metana (CH4) dan air (H2O) dengan katalis nikel. Reaksi tersebut berlangsung pada kondisi endotermis dengan tekanan 35-40 kg/cm2 (gage) dan temperatur 650-900oC. Catalyst tube dibuat dari material dengan spesifikasi ASTM A297 dan didesain dengan standar API 530 agar tahan terhadap creep. Creep pada catalyst tube dimulai dengan tebentuknya micro voids, kemudian berkembang menjadi retak mikro (fissures). Creep pada catalyst tube dapat dideteksi dengan pengukuran dimensi dan pemeriksaan atenuasi ultrasonik, tetapi metode atenuasi ultrasonik ini tidak dapat diterapkan pada sambungan las. Penggantian catalyst tube dilakukan jika regangan creep yang terjadi lebih dari 6%, tetapi ternyata ada kegagalan catalyst tube dengan regangan creep kurang dari 6%. Jika atenuasi ultrasonik kurang dari 6 dB, regangan creep dengan atenuasi ultrasonik menunjukkan hubungan linier. Pada atenuasi ultrasonik lebih dari 6 dB, perubahan atenuasi tidak lagi sebanding dengan regangan creep. Metode pemeriksaan atenuasi ultrasonik dapat digunakan untuk mengetahui perubahan kondisi metalurgi dinding catalyst tube seperti terbentuknya fissures. Hasil penelitian ini menunjukkan bahwa Fissures kemungkinan besar ditemukan pada catalyst tube dengan atenuasi ultrasonik lebih besar dari 6 dB. Oleh karena itu catalyst tube dengan atenuasi ultrasonik lebih besar dari 6 dB harus mendapat perhatian khusus. Prediksi umur teknis sisa catalyst tube hanya dapat dilakukan pada atenuasi ultrasonik kurang dari 6 dB. Pemeriksaan atenuasi ultrasonik dan pengukuran regangan creep pada pengoperasian catalyst tube diperlukan karena dapat memberikan informasi terkait kondisi metalurgi, kualitas dan gambaran umur teknik sisa.

Deskripsi Alternatif :

Catalyst tubes are reactor where hydrogen (H2) and carbon monoxyde (CO) gases produced from methane (CH4) and water (H2O). The reaction promoted by nickel catalyst. It conducted in endothermis at 35-40 kg/cm2 (gage) pressure and 650-900oC temperature condition. Catalyst tube made from ASTM A297 material, and it designed according to API 530 to avoid creep. Creep in catalyst tube is initiated by micro voids formation. Micro voids linked up together to form micro cracks or fissures. Creep in catalyst tube could be detected by dimensional measurement and ultrasonic attenuation inspection method. However it could not be applied to welding joints. Based on dimensional measurement data said that catalyst tube with creep strain higher than 6% should be replaced. This research found according to the failure record, that catalyst tube could be failed even if the creep strain is less than 6%. When attenuation is less than 6 dB, creep strain and ultrasonic attenuation relationship is linear. But if ultrasonic attenuation is beyond 6 dB, threre are inconsistent corelation between ultrasonic attenuation and creep strain. Ultrasonic attenuation is non destructive inspection method, which is effective in monitoring micro structural change due to creep such as fissures formation. Another result on metallographic examination found that fissures formation occured in the catalyst tube wall if the ultrasonic attenuation higher than 6 dB. Ultrasonic attenuation method can estimate catalyst tube remaining life if the creep strain is less than 6% and attenuation is less than 6 dB. It should give warning mark on catalyst tube which have ultrasonic attenuation higher than 6 dB even if the creep strain less than 6%. Based on this research, ultrasonic attenuation inspection and dimensional measurement are importent role in catalyst tube maintenance, because of the information of metallurgical condition, quality and remaining life estimation.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Tim Pembimbing : Dr. Ir. H. Husaini Ardy; Dr. Ir. Arif Basuki, Editor: Alice Diniarti

File PDF...