ANALISIS BEBAN TEKUK KRITIS KOLOM SANDWICH KOMPOSIT SERAT ALAM MENGGUNAKAN PENDEKATAN METODE ELEMEN HINGGA DUA DIMENSI (2-D)

Undergraduate Theses from JBPTITBPP / 2017-10-09 10:33:28
Oleh : DIAN FADILLAH SAFARI (NIM 13603008), Central Library Institute Technology Bandung
Dibuat : 2007, dengan 8 file

Keyword : Kolom sandwich alam, Beban tekuk kritis, Overall buckling, Wrinkling, Delaminasi

Struktur sandwich dari serat alam memiliki potensi untuk dikembangkan menjadi material alternatif pengganti logam dan kayu. Hal ini dikarenakan sifatnya yang dapat diperbaharui, ringan, dan sifat mekaniknya yang kompetitif dibandingkan dengan komposit serat gelas. Selain itu, Indonesia kaya akan sumber daya alamnya termasuk serat alam. Namun permasalahannya adalah struktur sandwich sangat rentan terhadap beban kompresi. Tugas akhir ini meneliti tentang perilaku yang terjadi pada kolom sandwich komposit alam ketika diberi beban tekan. Kolom sandwich terdiri dari core (Serbuk Kelapa/Latek) dan face (Rami/Epoxy atau Serat Kelapa/Epoxy). Kolom sandwich dimodelkan secara dua dimensi pada MSC.Nastran sebagai kolom sempurna dengan tumpuan sederhana dan beban uniaksial. Pada tugas akhir ini dibuat empat jenis model, yaitu model overall buckling, wrinkling, model dengan variasi ketebalan core, dan model overall buckling dengan delaminasi awal. Dari hasil analisis, beban kritis untuk model overall buckling kolom sandwich dengan face Rami/Epoxy sebesar 206,02 N/mm dan untuk model wrinkling sebesar 306,97 N/mm. Sedangkan untuk model overall buckling dengan face Serat Kelapa/Epoxy sebesar 73,65 N/mm dan untuk model wrinkling sebesar 149,60 N/mm. Dari model dengan variasi ketebalan core diperoleh bahwa beban kritis meningkat seiring peningkatan ketebalan core dan terjadi perubahan modus dari overall buckling ke wrinkling setelah mencapai ketebalan core tertentu. Terjadi penurunan beban tekuk kritis untuk model kolom sandwich dengan delaminasi awal. Pada eksperimen, kolom sandwich terjadi delaminasi dan harga beban tekuk kritisnya mendekati hasil numerik untuk model dengan delaminasi awal 40%.

Deskripsi Alternatif :

Sandwich structure from natural fiber is potential to be developed as alternative material of wood and metal. This is due to its potential properties i.e. renewable, ligwas modeled htweight, and its competitive mechanical property compared to fiberglass composite. In addition, Indonesia has an abundant amount of natural resources including natural fiber. Nevertheless, sandwich structure has problem with compressive loading. This final project is a research about behavior of natural sandwich column under compressive loading. The Sandwich column consists of core (Coconut powder/latek) and face (Hemp/Epoxy or Coir/Epoxy). The sandwich column was modeled as 2-D perfect column with simply supported and uniaxial loading in MSC.Nastran. This final project has four model, that is overall buckling model, wrinkling, model with thickness variation of core, and overall buckling model with initial delamination. From analyze result, critical load of sandwich with face Hemp/Epoxy is 206,02 N/mm for overall buckling model and 306,97 N/mm for wrinkling model. In other hand, critical load of sandwich with face Coir/Epoxy is 73.65 N/mm for overall buckling model and 149.60 N/mm for wrinkling model. The analyzed result of model with thickness variation of core is that critical load increase with core thickness increasing and occur mode change from overall buckling mode to wrinkling mode after gain certain thickness. On the sandwich column occur decrease of critical load due to delamination between face and core. At experiment, on sandwich column occur delamination and its critical load approach the result of numerical method for model with 40% initial delamination.

Copyrights : Copyright Â(c) 2001 by ITB Central Library. Verbatim copying and distribution of this entire article is permitted by author in any medium, provided this notice is preserved.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiC
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Dr. Ir. Bambang Kismono Hadi, Ir. Muhammad Kusni, M.T., dan Dr. Ir. Djarot Widagdo, Editor: Rizki Apriyanti

File PDF...