PENGARUH PERLAKUAN PANAS PADA Al 204.0 TERHADAP SIFAT MEKANIK DAN LAJU KOROSI DALAM LARUTAN 3,5 % NaCl

EFFECT OF HEAT TREATMENT OF Al 204.0 TO MECHANICAL AND CORROSION PROPERTIES

Undergraduate Theses from JBPTITBPP / 2017-09-27 10:40:49
Oleh : ARIF RAHMAN HAKIM (NIM : 13102121); Pembimbing : Prof. Dr. Ir. Rochim Suratman, S1 - Department of Mechanical Engineering
Dibuat : 2007, dengan 7 file

Keyword : Al 204.0, Perlakuan panas, korosi.

Al 204.0 merupakan casting aluminum dengan unsur paduan utama yaitu copper, aluminium ini akan digunakan pada 25 part dari panser APC 6x6 buatan PT. Pindad. Sebelum digunakan, aluminium tersebut terlebih dahulu dikenai


proses perlakuan panas agar sifat mekaniknya sesuai dengan spesifikasi yang dibutuhkan. Proses perlakuan panas yang diterapkan pada aluminium untuk meningkatkan sifat mekanik juga akan mempengaruhi energi bebas yang dimiliki oleh aluminium tersebut.


Pada penelitian ini akan dilihat pengaruh perlakuan panas pada Al 204.0 terhadap sifat mekanik dan laju korosinya dalam larutan 3,5 % NaCl. Proses pelakuan panas yang dilakukan berbeda-beda sehingga menghasilkan aluminium


dengan sifat mekanik yang berbeda pula. Pengamatan struktur mikro akan digunakan untuk melihat pengaruh perlakuan panas yang diterapkan terhadap struktur mikro aluminium. Pengujian korosi yang digunakan pada penelitian ini


yaitu metode polarisasi dengan menggunakan potensiostat.


Dari data yang diperoleh, didapatkan bahwa proses perlakuan panas yang dibutuhkan untuk mendapatkan aluminium dengan spesifikasi yang dibutuhkan, yaitu solution + natural aging. Laju korosi akan meningkat seiring dengan


meningkatnya kekerasan dan kekuatan aluminium.

Deskripsi Alternatif :

Al 204.0 is one of casting aluminum with its primary alloy is copper. This aluminum will be used in 6 x 6 APC tanks that are produced by PT. Pindad. Before it is used, this aluminum is heat treated so that its mechanical properties


are suitable with some specification needed. The heat treatment processes that are applied are to enhance its mechanical properties and it also affects its storage


energy.


This research is done to analyze aluminum mechanical properties and corrosion rates in 3,5 % NaCl solution. Heat treatment processes that are applied are varied, so that different mechanical properties will be obtained. Micro


structural observation would be applied to observe the impact of heat treatment in aluminum micro structure. Corrosion test that is used in this research is polarization method by using potentiostat. From some data that are obtained, heat treatment processes that are needed to get some specification that are required are solution treatment + natural aging. Corrosion rates will be increased as the increasing of aluminum’s hardness and


strength.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id

Print ...

Kontributor...

  • Pembimbing : Prof. Dr. Ir. Rochim Suratman, Editor: PKL-SMK

File PDF...