PENGARUH PENAMBAHAN 2-MERKAPTOBENZOTIAZOL TERHADAP EFEKTIVITAS NATRIUM MOLIBDAT SEBAGAI INHIBITOR KOROSI BAJA KARBON DALAM LARUTAN NACL 1%

THE EFFECT OF THE ADDITION OF 2-MERCAPTOBENZOTHIAZOLE TOWARDS THE EFFECTIVITY OF SODIUM MOLYBDATE AS CORROSION INHIBITOR FOR CARBON STEEL IN 1% NACL SOLUTION

THE EFFECT OF THE ADDITION OF 2-MERCAPTOBENZOTHIAZOLE TOWARDS THE EFFECTIVITY OF SODIUM MOLYBDATE AS CORROSION INHIBITOR FOR CARBON STEEL IN 1% NACL SOLUTION
Undergraduate Theses from JBPTITBPP / 2017-09-27 11:42:30
Oleh : APRINI DWI BONITA PASARIBU ( NIM : 10508103); Pembimbing : Dr. Bunbun Bundjali, S1 - Department of Chemistry
Dibuat : 2012, dengan 7 file

Keyword : 2-Merkaptobenzotiazol, Baja Karbon, Efisiensi Inhibisi, Inhibitor Korosi, Natrium Molibdat

Baja karbon banyak digunakan dalam industri minyak dan gas sebagai material pipa pengalir minyak mentah dan gas alam basah. Pada lingkungan fluida tersebut, permukaan dalam pipa tersebut dapat terkorosi. Sebagai usaha untuk menghambat laju korosi tersebut, digunakan inhibitor korosi yang diinjeksikan secara periodik ke dalam aliran fluida Dalam penelitian ini, zat yang digunakan sebagai inhibitor korosi adalah natrium molibdat dan 2-merkaptobenzotiazol (MBT). Dibandingkan dengan kromat, inhibitor natrium molibdat lebih tidak beracun dan lebih ramah lingkungan. Pada penelitian ini, dilakukan pengujian daya inhibisi kedua inhibitor dalam larutan NaCl 1% pada temperatur 30, 45, dan 60oC dengan variasi konsentrasi natrium molibdat sebesar 5, 10, 15, 20, dan 25 ppm, serta 2-merkaptobenzotiazol dengan variasi konsentrasi 2, 4, 6, 8, dan 10 ppm. Pengukuran laju korosi dilakukan dengan menggunakan metode weight loss (pengurangan berat), Electrochemical Impedance Spectroscopy (EIS), dan metode ekstrapolasi Tafel. Pada temperatur 60oC, daya inhibisi natrium molibdat dengan konsentrasi 25 ppm adalah 35,7%. Dengan adanya penambahan 10 ppm MBT, efisiensi inhibisi meningkat hingga 79,4%. Natrium molibdat memiliki daya inhibisi yang rendah terhadap baja karbon dalam lingkungan yang bersuasana asam dan penambahan MBT dapat meningkatkan keefektifan natrium molibdat untuk menghambat laju korosi baja karbon, baik pada suhu rendah maupun pada suhu tinggi.

Deskripsi Alternatif :

Carbon steel is widely used in oil and gas industry as material for pipeline used to divert crude oil and natural wet gas. In this fluid environment, the inner part of pipeline may be corroded. To inhibit the corrosion rate, corrosion inhibitor is injected periodically into the fluids. In this study, sodium molybdate and 2-mercaptobenzothiazole (MBT) were used as corrosion inhibitor. Compared to chromate, sodium molybdate inhibitor is less toxic and more eco-friendly. Investigation of the effectivity of these inhibitors in 1% NaCl solution was tested at 30, 45, and 60oC with the variation of concentration of sodium molybdate was 5, 10, 15, 20, and 25 ppm, and 2-mercaptobenzothiazole with the variation of concentration of 2, 4, 6, 8, and 10 ppm. Weight loss method, Electrochemical Impedance Spectroscopy, and extrapolation Tafel method were used to measure the corrosion rate. At 60oC, the inhibition efficiency of 25 ppm sodium molybdate is 35.7%. The addition of 10 ppm MBT increased the inhibition efficiency to 79.4%. Sodium molybdate has low inhibition efficiency for carbon steel in acid media and the addition of MBT can increase the effectiveness of sodium molybdate in inhibiting corrosion rate of carbon steel not only at low temperature, but also at high temperature.

Beri Komentar ?#(0) | Bookmark

PropertiNilai Properti
ID PublisherJBPTITBPP
OrganisasiS
Nama KontakUPT Perpustakaan ITB
AlamatJl. Ganesha 10
KotaBandung
DaerahJawa Barat
NegaraIndonesia
Telepon62-22-2509118, 2500089
Fax62-22-2500089
E-mail Administratordigilib@lib.itb.ac.id
E-mail CKOinfo@lib.itb.ac.id